Calcination-free board prepared from diatomite and preparation method of calcination-free board

A diatomite and calcination-free technology, applied in the field of sheet metal processing, can solve the problems of inability to utilize secondary and tertiary diatomite and high production costs, and achieve the effects of waste utilization, low cost and compact process flow

Pending Publication Date: 2021-07-06
白山和一硅藻科技股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a non-calcined plate prepared by using diatomite and its preparation method. The main purpose of the present invention is to solve the problem that the existing diatomite plate cannot use secondary and tertiary diatomite, and the production cost is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: a calcination-free board prepared by utilizing diatomite, comprising the following raw materials by weight: 40 parts of diatomite, 5 parts of silica fume, 5 parts of quicklime, 5 parts of bamboo and wood fibers, and 2 parts of aluminum powder And 5 parts of water glass.

[0023] Diatomite adopts secondary and tertiary diatomite.

[0024] A preparation method of a calcined-free plate prepared by utilizing diatomite, comprising the following steps:

[0025] S1, pulverization: take each raw material according to the proportion by weight and obtain mixed powder after pulverizing and ball milling;

[0026] S2, mixing: add the powder obtained in S1 into the mixer, add water and stir to obtain a slurry, and the mixing time is 20min;

[0027] S3, granulation: the slurry prepared in S2 is fed into the extruder for fusion and extrusion to obtain pellets, the fusion temperature of the extruder is 60°C, and the fusion time is 15min;

[0028] S4, pressing: the granu...

Embodiment 2

[0031] Embodiment 2: A calcination-free board prepared by utilizing diatomite, comprising the following raw materials by weight: 50 parts of diatomite, 8 parts of silica fume, 10 parts of quicklime, 10 parts of bamboo and wood fibers, and 4 parts of aluminum powder And 8 parts of water glass.

[0032] Diatomite adopts secondary and tertiary diatomite.

[0033] A preparation method of a calcined-free plate prepared by utilizing diatomite, comprising the following steps:

[0034] S1, pulverization: take each raw material according to the proportion by weight and obtain mixed powder after pulverizing and ball milling;

[0035] S2, mixing: add the powder obtained in S1 into the mixer, add water and stir to obtain a slurry, and the mixing time is 23min;

[0036] S3, granulation: the slurry prepared in S2 is fed into the extruder for fusion and extrusion to obtain pellets, the fusion temperature of the extruder is 65°C, and the fusion time is 20min;

[0037] S4, pressing: the pel...

Embodiment 3

[0040] Embodiment 3: A calcination-free board prepared by utilizing diatomite, comprising the following raw materials by weight: 60 parts of diatomite, 10 parts of silica fume, 15 parts of quicklime, 15 parts of bamboo and wood fibers, and 6 parts of aluminum powder And 10 parts of water glass.

[0041] Diatomite adopts secondary and tertiary diatomite.

[0042] A preparation method of a calcined-free plate prepared by utilizing diatomite, comprising the following steps:

[0043] S1, pulverization: take each raw material according to the proportion by weight and obtain mixed powder after pulverizing and ball milling;

[0044] S2, mixing: add the powder obtained in S1 into the mixer, add water and stir to obtain a slurry, and the mixing time is 25min;

[0045] S3, granulation: the slurry prepared in S2 is fed into the extruder for fusion and extrusion to obtain pellets, the fusion temperature of the extruder is 70°C, and the fusion time is 25min;

[0046] S4, pressing: the p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of building boards, and discloses a calcination-free board prepared from diatomite. The calcination-free board is prepared from the following raw materials in parts by weight: 40-60 parts of diatomite, 5-10 parts of silica fume, 5-15 parts of quick lime, 5-15 parts of bamboo and wood fiber, 2-6 parts of aluminum powder and 5-10 parts of water glass. The main steps comprise crushing, mixing, granulation, pressing, maintenance and polishing. The production process is compact in flow. Waste second-level and third-level diatomite is adopted as diatomite, the cost is low, waste utilization is achieved, aluminum powder serves as a foaming agent, water glass serves as an adhesive, the overall structure of the board is uniform, the second-level and third-level diatomite has many pores, the process does not have a calcination link, the pores cannot be damaged, and therefore the board body has certain adsorption capacity, the indoor humidity can be adjusted, indoor harmful gas can be removed, and the method is suitable for industrial production.

Description

technical field [0001] The invention relates to the technical field of sheet metal processing, in particular to a calcination-free sheet prepared by using diatomite and a preparation method thereof. Background technique [0002] Plate is a flat rectangular building material plate made of standard size, used in the construction industry, used as a component of walls, ceilings or floors, and also refers to forged, rolled or cast metal plates; [0003] Plate is an essential component in the field of building decoration. With the development and progress of society, ordinary building plates can no longer meet people's needs. Ordinary plates have many disadvantages such as easy mold and poor corrosion resistance. Chinese patent CN107963880A discloses a A method for preparing a large-size multifunctional sintered diatom plate, the steps of which include: mixing of raw materials, granulation, molding, drying of the green body, and sintering of the plate, wherein the raw materials a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/26C04B18/04C04B16/02C04B22/04
CPCC04B28/26C04B18/04C04B22/04C04B16/02C04B2111/00017C04B18/146C04B22/064Y02W30/91
Inventor 于波
Owner 白山和一硅藻科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka