Wall flow type honeycomb formaldehyde-removing air conditioner filter element
A honeycomb and wall-flow technology, which is applied in the direction of dispersed particle filtration, gas treatment, membrane technology, etc., can solve the problems that the coating adsorption and durability are difficult to guarantee, so as to improve the utilization rate of materials, increase the adsorption rate, reduce the The effect of production costs
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0031] Example 1:
[0032] (1) Ceramic fibers having a 200 g diameter of about 3 μm, length 200 μm, 500 g ratio surface area 510 m 2 The ZSM-5 molecular sieve of / g, the content of 30% alkaline silica sol 280 g, polystyrene emulsion 30g, Tianjing powder 20 g, 90 mL water mixed, then stirred with a mixer for 30 minutes, vacuum training in the mud machine The mud is 10 minutes to get a uniform mud material.
[0033] (2) The sludge is extruded into a honeycomb moisture billet with a hydraulic machine and a honeycomb mold, and the wet cutter is cut by a wet blade cutting machine to cut a 100 mm × 100 mm × 100 mm square honeycomb moist billet, honeycomb moist bum. The honeycomb hole is 2.5 mm × 2.5mm square, the hole wall thickness is 1.5 mm.
[0034] (3) Place the honeycomb moisture bille in the indoor natural air dry 36 h, 120 ° C, 12 h, 12 h, 550 ° C, 550 ° C, 550 ° C, to form an activated honeycomb filtration material (honeycomb).
[0035] (4) The aluminum plate of the hit hole is...
Example Embodiment
[0036] Example 2:
[0037] (1) Ceramic fibers of 220 g of 2 μm, length 500 μm, 500 g ratio surface area 1240 m 2 The activated carbon powder of / g, a neutral silica sol 260 g, a polystyrene emulsion 40g, a field of Tanjing powder, added to 110 ml of water, then stirred with a mixer for 20 minutes, vacuum training in mud machine 20 minutes, get a uniform muddy mud.
[0038] (2) The smear is squeezed into a honeycomb moisture billet with a hydraulic machine and a honeycomb mold, and the wet cutter is cut by a wet blade cutting machine to cut a 100 mm × 100 mm × 80 mm rectangular honeycomb moist billet, honeycomb wet billet. The honeycomb hole is 1.5 mm × 1.5 mm square, the hole wall thickness is 1 mm.
[0039] (3) The honeycomb moistrid is then placed in the indoor natural air drying 26h, and the honeycomb filtration material (honeycomb body) is formed after 220 ° C for 6 h in the muffle furnace, 550 ° C.
[0040] (4) The stainless steel sheet of the hinged hole is adducted to the ...
Example Embodiment
[0041] Example 3:
[0042] (1) Ceramic fibers having a diameter of about 5 μm, length 400mm, 580g specific surface area 60m 2 / g of manganese oxide, aluminum sol 88g, acrylic emulsion 20g, Tianjing powder 20g, added to 190 ml of water, then stirred for 20 minutes using a mixer, vacuum training in mud for 20 minutes, resulting in a uniform gas-free muddy .
[0043](2) The sludge is squeezed into a honeycomb somer having a sludge of 150 mm × 150 mm in a honeycomb body of 150 mm × 150 mm, and the wet cutting machine is cut, and the moisture cutter is cut into a honeycomb moist bar, and a honeycomb wet bar. The honeycomb hole is 2.5 mm × 2.5mm square, the hole wall thickness is 1.5 mm.
[0044] (3) The honeycomb moistrid blender is then placed in the indoor natural air dry 12h after 120 ° C for 6 h, 550 ° C, and the activated honeycomb filter material (honeycomb body) is formed after 550 ° C.
[0045] (4) Adhesion of the hooded plastic sheet with acrylic emulsion is attached to both ...
PUM
Property | Measurement | Unit |
---|---|---|
Hole wall thickness | aaaaa | aaaaa |
Cross-sectional area | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.