Flame-retardant environment-friendly PC-ABS composite plastic master batch and preparation method thereof
A technology of PC-ABS and composite plastics, which is applied in the field of polymer materials, can solve the problems of affecting the mechanical properties of PC-ABS composite plastics, the effect of flame retardant effect needs to be improved, and the effect of flame retardant is not good, so as to achieve good toughness and good resistance. Flammability, crystallinity reduction effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example 1
[0052] A kind of preparation of nano silicon dioxide, comprises the steps:
[0053] Step A: Weigh 1Kg of sodium persulfate and 2Kg of polyethylene glycol, stir and dissolve in deionized water to obtain mixture I, and set aside; weigh 80Kg of concentrated sulfuric acid with a mass fraction of 95% and 5Kg of hydrogen peroxide, and mix well to obtain mixture II , for subsequent use; 5Kg sodium carbonate was weighed and dissolved in 200Kg mass fraction of 10% sodium hydroxide solution to obtain mixture III;
[0054] Step B: Weigh 60Kg of sodium silicate and 3Kg of sodium sulfate, dissolve them in water, add dropwise the mixture II obtained in step A, and stir evenly to obtain mixture IV;
[0055] Step C: Add mixture I to the mixture IV obtained in step B, react for 80 minutes, filter with a vacuum filter, then add the filter residue to the mixture III obtained in step A, stir evenly, let stand for 3 minutes, and vacuum The filter is used for suction filtration. During the suction...
preparation example 2
[0057] A kind of preparation of nano silicon dioxide, comprises the steps:
[0058] Step A: Weigh 0.75Kg of sodium persulfate and 1.5Kg of polyethylene glycol, stir and dissolve in deionized water to obtain mixture I, and set aside; weigh 75Kg of concentrated sulfuric acid with a mass fraction of 93% and 4Kg of hydrogen peroxide, and mix well to obtain Mixture II, set aside; weigh 4Kg sodium carbonate and dissolve in 150Kg mass fraction of 7.5% sodium hydroxide solution to obtain mixture III; step B: weigh 55Kg sodium silicate and 2Kg sodium sulfate, dissolve in water, dropwise The mixture II obtained in A is stirred evenly to obtain the mixture IV;
[0059] Step C: Add mixture I to the mixture IV obtained in step B, react for 70 minutes, filter with a vacuum filter, then add the filter residue to the mixture III obtained in step A, stir evenly, stand for 2.5 minutes, vacuum The suction filter is used for suction filtration. During the suction filtration process, it is rinsed...
preparation example 3
[0061] A kind of preparation of nano silicon dioxide, comprises the steps:
[0062] Step A: Weigh 0.5Kg of sodium persulfate and 1Kg of polyethylene glycol, stir and dissolve in deionized water to obtain mixture I, and set aside; weigh 75Kg of concentrated sulfuric acid with a mass fraction of 90% and 4Kg of hydrogen peroxide, and mix evenly to obtain a mixture Ⅱ, standby; 3Kg of sodium carbonate was weighed and dissolved in 100Kg of 5% sodium hydroxide solution to obtain mixture Ⅲ;
[0063] Step B: Weigh 50Kg of sodium silicate and 1Kg of sodium sulfate, dissolve them in water, add dropwise the mixture II obtained in step A, and stir evenly to obtain mixture IV;
[0064] Step C: Add mixture I to the mixture IV obtained in step B, react for 65 minutes, filter with a vacuum filter, then add the filter residue to the mixture III obtained in step A, stir evenly, let stand for 2 minutes, and vacuum The filter is used for suction filtration. During the suction filtration process, ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com