A kind of high temperature resistant transparent glass fiber insulation board and preparation method thereof

A technology of glass fiber and glass fiber cloth, applied in the field of transparent glass fiber insulation board and its preparation, can solve the problems of poor mechanical properties, poor flame retardant performance, general high temperature resistance, etc., and achieve excellent water resistance, high practicability, and high technology Well-designed effects

Active Publication Date: 2022-07-08
广东纵胜新材料股份有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing glass fiber insulation laminates on the market have general high temperature resistance, poor mechanical properties and flame retardancy, which brings us great inconvenience in practical application. Therefore, in order to further improve the application range of insulation boards, how to Improving the high temperature resistance and flame retardancy of insulating boards is one of the technical problems that we need to solve urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A preparation method of a high temperature resistant transparent glass fiber insulating board, comprising the following steps:

[0034] (1) get hexachlorocyclotriphosphazene and tetrahydrofuran, and after mixing, obtain hexachlorocyclotriphosphazene solution; get p-hydroxybenzaldehyde, tetrahydrofuran, add triethylamine under nitrogen atmosphere after mixing, and heat up to 60 ℃ , dropwise addition of hexachlorocyclotriphosphazene solution, constant temperature reaction for 8h, rotary evaporation to remove solvent, ethanol washing and filtration, ethyl acetate recrystallization, filtration and drying to obtain material A; wherein the hexachlorocyclotriphosphazene, p-hydroxybenzene The molar ratio of formaldehyde is 1:6;

[0035] Take material A, tetrahydrofuran and methanol, mix and stir for 10 min, stir evenly, add sodium borohydride under nitrogen atmosphere, react at 25 ° C for 10 h, remove the solvent by rotary evaporation, wash and filter with ethanol, recrystalliz...

Embodiment 2

[0042] A preparation method of a high temperature resistant transparent glass fiber insulating board, comprising the following steps:

[0043] (1) get hexachlorocyclotriphosphazene and tetrahydrofuran, and make hexachlorocyclotriphosphazene solution after mixing; Get p-hydroxybenzaldehyde, tetrahydrofuran, add triethylamine under nitrogen atmosphere after mixing, and heat up to 63 ℃ , dropwise added hexachlorocyclotriphosphazene solution, reacted at constant temperature for 7.5h, rotary evaporated to remove the solvent, washed with ethanol, filtered, recrystallized from ethyl acetate, filtered and dried to obtain material A; wherein the hexachlorocyclotriphosphazene, p-hydroxyl The molar ratio of benzaldehyde is 1:6;

[0044] Take material A, tetrahydrofuran and methanol, mix and stir for 12 min, stir evenly, add sodium borohydride under nitrogen atmosphere, react at 25°C for 12 h, remove the solvent by rotary evaporation, wash and filter with ethanol, recrystallize with ethyl...

Embodiment 3

[0051] A preparation method of a high temperature resistant transparent glass fiber insulating board, comprising the following steps:

[0052] (1) get hexachlorocyclotriphosphazene and tetrahydrofuran, and make hexachlorocyclotriphosphazene solution after mixing; Get p-hydroxybenzaldehyde and tetrahydrofuran, add triethylamine under nitrogen atmosphere after mixing, and heat up to 65 ℃ , dropwise add hexachlorocyclotriphosphazene solution, react at constant temperature for 7h, remove the solvent by rotary evaporation, wash and filter with ethanol, recrystallize with ethyl acetate, filter and dry to obtain material A; wherein the hexachlorocyclotriphosphazene, p-hydroxybenzene The molar ratio of formaldehyde is 1:6;

[0053] Take material A, tetrahydrofuran and methanol, mix and stir for 15 min, stir evenly, add sodium borohydride under nitrogen atmosphere, react at 25 ° C for 14 h, remove the solvent by rotary evaporation, wash and filter with ethanol, recrystallize with ethyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high temperature-resistant transparent glass fiber insulating board and a preparation method thereof. The scheme uses epoxy resin as the main material, benzoxazine resin and flame retardant prepolymer as auxiliary materials to prepare glue solution for the insulating board. The prepreg is obtained after dipping on the surface of the glass fiber cloth, and the prepreg is hot-pressed and compounded. The obtained insulating board not only has excellent high temperature resistance, but also has excellent flame retardant performance, and the surface is hydrophobic, which can effectively prevent the entry of water media. At the same time, due to the limited parameters of the flame retardant prepolymer, the crosslinking density of the glue is excellent, the water absorption rate is also greatly reduced, and the water resistance is more excellent. The invention discloses a high-temperature-resistant transparent glass fiber insulating board and a preparation method thereof. The process design is reasonable and the component distribution ratio is suitable. It can be widely used in various fields and has high practicability.

Description

technical field [0001] The invention relates to the technical field of insulating boards, in particular to a high temperature resistant transparent glass fiber insulating board and a preparation method thereof. Background technique [0002] Laminate is a kind of laminated product. Laminate is a whole made of two or more layers of resin-impregnated fibers or fabrics that are laminated and thermocompressed. Laminates can be processed into various insulation and structural parts. , With the development of the electrical industry, laminates have begun to be used in motors, transformers, high and low voltage electrical appliances, electrical instruments and electronic equipment, and glass cloth is one of the more widely used ones. [0003] The existing glass fiber insulation laminates on the market have average high temperature resistance, and poor mechanical properties and flame retardant properties, which bring great inconvenience to us in practical application. Therefore, in o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J5/24C08L63/00C08L61/34C08L25/18C08K5/544C08K7/14C08K9/06B32B17/04B32B17/06B32B37/06B32B37/10B32B38/08B32B38/16
CPCC08J5/24B32B5/02B32B5/26B32B37/06B32B37/10B32B38/08B32B38/164C08J2363/00C08J2461/34C08J2425/18C08K5/544C08K7/14C08K9/06B32B2260/023B32B2260/046B32B2262/101B32B2307/206B32B2307/306B32B2307/3065B32B2307/412B32B2307/73Y02B80/10
Inventor 张宗权何辉春
Owner 广东纵胜新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products