Glass PVB film with sound insulation and ultraviolet insulation functions and preparation method thereof

A glass and functional technology, applied in film/sheet release coatings, film/sheet adhesives, adhesives, etc., can solve the problem of glass PVB film sound insulation, poor UV blocking function, affecting the use efficiency of glass PVB film, etc. problem, to achieve the effect of enhancing sound insulation and anti-ultraviolet performance, enhancing sound insulation and anti-ultraviolet performance, and strong anti-pull performance

Pending Publication Date: 2021-12-28
浙江多力塑胶有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing glass PVB film has poor sound insulation and UV insulation functions, which affects the use efficiency of glass PVB film. Based on this, further improvement is needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] S1: Mix and stir styrene-acrylic emulsion, polyurethane emulsion, and graphene according to the weight ratio of 3:2:1 to obtain a polymer emulsion;

[0021] S2: Send the shell powder into the maleic anhydride solution with a mass fraction of 30% according to the weight ratio of 1:3, then add the silane coupling agent KH550 with 10% shell powder, react at a temperature of 70°C for 20 minutes, and the reaction speed is 100r / min, the reaction is finished, and the grafted shell powder is obtained;

[0022] S3: Send lanthanum chloride into the phosphoric acid-hydrochloric acid buffer solution with a weight ratio of 3:1 for stirring treatment. The stirring temperature is 60°C, the stirring speed is 150r / min, and the stirring time is 20min. After the stirring is completed, then 100W laser Irradiation for 20min is processed to obtain modified lanthanum chloride for subsequent use;

[0023] Mix silicon dioxide and titanium dioxide at a weight ratio of 1:3, then add the modified...

Embodiment 2

[0029] S1: Mix and stir styrene-acrylic emulsion, polyurethane emulsion, and graphene according to the weight ratio of 3:2:1 to obtain a polymer emulsion;

[0030] S2: Send the shell powder into the maleic anhydride solution with a mass fraction of 40% according to the weight ratio of 1:3, then add the silane coupling agent KH550 with 10% shell powder, and react at a temperature of 90°C for 30 minutes, and the reaction speed is 500r / min, the reaction is finished, and the grafted shell powder is obtained;

[0031] S3: Lanthanum chloride is sent into the phosphoric acid-hydrochloric acid buffer solution obtained by the weight ratio of 3:1 for stirring treatment, the stirring temperature is 80°C, the stirring speed is 250r / min, the stirring time is 30min, the stirring is completed, and then the 500W laser Irradiated for 30 minutes to obtain modified lanthanum chloride;

[0032] Mix silicon dioxide and titanium dioxide according to a weight ratio of 1:3, then add the above-mentio...

Embodiment 3

[0040] S1: Mix and stir styrene-acrylic emulsion, polyurethane emulsion, and graphene according to the weight ratio of 3:2:1 to obtain a polymer emulsion;

[0041] S2: Send the shell powder into the maleic anhydride solution with a mass fraction of 35% according to the weight ratio of 1:3, then add the silane coupling agent KH550 with 10% shell powder, and react at a temperature of 80°C for 25 minutes, and the reaction speed is 300r / min, the reaction is finished, and the grafted shell powder is obtained;

[0042] S3: Send lanthanum chloride into the phosphoric acid-hydrochloric acid buffer solution with a weight ratio of 3:1 for stirring treatment. The stirring temperature is 70°C, the stirring speed is 200r / min, and the stirring time is 25min. After the stirring is completed, 300W laser radiation Treat according to 25min to obtain modified lanthanum chloride;

[0043] Mix silicon dioxide and titanium dioxide according to a weight ratio of 1:3, then add the above-mentioned mo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glass PVB film with sound insulation and ultraviolet insulation functions and a preparation method thereof, and belongs to the field of PVB films. The glass PVB film with the sound insulation and ultraviolet insulation functions comprises a middle layer and PVB layers arranged on the two sides of the middle layer respectively, wherein the middle layer and the PVB layers are subjected to hot press molding at 130-140 DEG C to form the glass PVB film, and the middle layer is obtained by adding grafted shell powder into a polymer emulsion, then adding a melt blend of modified bentonite and PA6, finally adding EVA resin, and after stirring is finished, co-extruding or roll-forming. According to the glass PVB film, the two PVB layers are subjected to hot press molding on the two sides of the middle layer to obtain the glass PVB film, the middle layer is made of the polymer emulsion, the grafted shell powder and the melt blend of the modified bentonite and the PA6, the lamellar spacing of the modified bentonite is increased so as to prevent external media from entering the glass PVB film, the toughness of the PVB film is stabilized through the PA6 by matching with the PA6, and the grafted shell powder is also matched, so that the sound insulation and ultraviolet insulation performance of the product is enhanced.

Description

technical field [0001] The invention relates to the field of PVB films, and more specifically relates to a glass PVB film with sound-insulating and ultraviolet-proof functions and a preparation method thereof. Background technique [0002] PVB interlayer film is a translucent film. PVB interlayer film is mainly used for laminated glass. It is a special glass made by inserting a layer of PVB film between two pieces of glass, compounding and heating under high pressure. PVB laminated glass is widely used in construction, automobile, photovoltaic and other industries due to its multiple functions such as safety, heat preservation, noise control and ultraviolet isolation. The PVB intermediate film produced with special formula is also widely used in aerospace, military and high-tech industries, such as aircraft, aerospace products, military instruments, solar cells and solar receivers. [0003] The existing glass PVB film has poor sound insulation and UV insulation functions, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/24C09J7/25C09J7/50C08L23/08C08L25/14C08L75/04C08L77/02C08K3/04C08K9/06C08K9/04C08K3/26C08K9/00C08K9/02C08K3/16C08K3/34C08K3/36C08K3/22
CPCC09J7/24C09J7/25C09J7/50C08L23/0853C09J2301/124C09J2301/41C08K2003/2241C08K2003/265C09J2475/003C09J2423/046C09J2477/006C08L25/14C08L75/04C08L77/02C08K3/042C08K9/06C08K9/04C08K3/26C08K9/00C08K9/02C08K3/16C08K3/346C08K3/36C08K3/22
Inventor 黄沈莞
Owner 浙江多力塑胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com