Anti-corrosion galvanized steel sheet and preparation method thereof

A galvanized steel plate, anti-corrosion technology, applied in coating, metal material coating technology, etc., can solve the problems of steel plate losing anti-corrosion effect, short anti-corrosion time, etc., to achieve increased anti-corrosion performance, not easy to remove, and good economic benefits Effect

Inactive Publication Date: 2022-01-28
安徽荣起安防科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing galvanized steel plate is coated with an anti-corrosion zinc layer on the surface of the steel plate after the steel plate is processed. The simple anti-corrosion zinc layer has a short anti-corrosion time in daily use. Due to the thin zinc layer, when the steel plate is damaged by manual friction, etc. The antiseptic effect will be lost here

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] A method for preparing an anti-corrosion galvanized steel sheet, comprising the following steps:

[0039] Step 1: Prepare the steel plate,

[0040] Specifically, 1.1: The steel plate ingredients are heated and smelted according to the proportion, and then cooled and cast to obtain the casting blank; that is, according to (15-30)% carbon, (18-70)% silicon, (10-25)% manganese, (5- 20)% aluminum, (5-30)% chromium, (10-20)% molybdenum, (15-30)% titanium, (5-10)% aluminum sulfide, (0.1-0.5)% sulfur, (0.8-1 )% boron, (0.1-0.5)% phosphorus, and the balance is iron. The ingredients are stirred evenly and added to the melting furnace, and melted at a temperature of about 2000 ° C. After each ingredient is melted, it is cooled to obtain a casting embryo;

[0041] 1.2: Hot-roll the cast billet at 1300-1350°C for 1-1.5 hours, then at 1150-1200°C for 1-1.5 hours, then at 1250-1300°C for 1-1.5 hours; The resulting steel billet is more stable;

[0042] 1.3. Cool the hot-rolled bill...

Embodiment

[0062] Prepare the galvanized steel sheet of the present invention, specifically:

[0063] Weigh 15kg carbon, 29kg silicon, 10kg manganese, 5%kg, 5kg chromium, 10kg molybdenum, 15%kg, 5kg aluminum sulfide, 1kg sulfur, 8kg boron, 1kg phosphorus, 1kg iron;

[0064] First: prepare the steel plate,

[0065] 1.1: The steel plate ingredients are heated and smelted according to the ratio, and then cooled and cast to obtain the casting embryo; that is, according to 15kg carbon, 29kg silicon, 10kg manganese, 5%kg, 5kg chromium, 10kg molybdenum, 15%kg, 5kg aluminum sulfide, 1kg sulfur, 8kg of boron, 1kg of phosphorus, 1kg of iron, stir the ingredients evenly, put them into the melting furnace, and melt them at a temperature of about 2000°C, or stir them after melting, and wait until the ingredients are melted and cooled to obtain cast iron. Embryo;

[0066] 1.2: Hot rolling the cast billet at 1350°C for 1.5 hours, then at 1200°C for 1.5 hours, then at 1300°C for 1.5 hours;

[0067] 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

An anti-corrosion galvanized steel sheet comprises a steel sheet and a plating layer. The plating layer comprises a plating layer formed by a zinc plating solution and a passivation plating solution. The zinc plating solution comprises the following components in percentage by weight: (15-20)% of sodium hydroxide, (35-50)% of zinc oxide, (25-40)% of nanoscale zinc powder, (5-20)% of barium sulfate, (1-10)% of talcum powder, (1-10)% of a flatting agent and (1-10)% of calcium borate. The passivation plating solution comprises the following components in percentage by weight: (25-30)% of epoxy resin, (20-40)% of sodium benzoate, (15-30)% of cinnamic acid, (15-30)% of phosphoric acid, (5-30)% of vanadate, (15-20)% of triethanolamine and (5-10)% of a dispersing agent. According to the galvanized steel sheet, two plating layers are formed on the outer surface, so that the corrosion resistance of the steel sheet can be increased in a limited mode; and meanwhile, the preparation is easy, the corrosion-resistant coatings are stable and not prone to being removed, and good economic benefits are achieved.

Description

technical field [0001] The invention belongs to the technical field of preparation of galvanized steel sheets, in particular to an anti-corrosion galvanized steel sheet and a preparation method thereof. Background technique [0002] Galvanized steel sheet is a welded steel sheet with a hot-dip galvanized or electro-galvanized layer on the surface; the characteristic of galvanized steel sheet is that galvanizing can effectively prevent steel corrosion and prolong the service life; the thickness of galvanized thin steel sheet is 0.4-1.2mm, also known as galvanized iron sheet , commonly known as white iron sheet; galvanized steel sheet is widely used in construction, vehicles, home appliances, daily necessities and other industries. [0003] The existing galvanized steel plate is coated with an anti-corrosion zinc layer on the surface of the steel plate after the steel plate is processed. The simple anti-corrosion zinc layer has a short anti-corrosion time in daily use. Due to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C26/02C21D1/18C21D6/00C21D8/02C22C33/04C22C38/02C22C38/04C22C38/06C22C38/22C22C38/28C22C38/32C22C38/34C22C38/38C22C38/60C23C22/40
CPCC23C26/02C23C22/40C22C38/02C22C38/04C22C38/06C22C38/22C22C38/28C22C38/32C22C38/60C22C38/34C22C38/38C22C33/04C21D1/18C21D6/002C21D6/005C21D6/008C21D8/0205C21D8/0221C21D8/0247
Inventor 朱诚
Owner 安徽荣起安防科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com