Phosphogypsum fireproof door core filler and preparation method thereof

A fire door core, phosphogypsum technology, applied in fire doors, clay preparation devices, chemical instruments and methods, etc., can solve the problems of cumbersome installation, poor mechanical properties of fire door core boards, etc., to speed up construction speed, high humidity film Strength and coverage effects, performance-enhancing effects

Pending Publication Date: 2022-04-29
GUIZHOU ZHENGHE AERATED CONCRETE CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a phosphogypsum fireproof door core filler and its preparation method to solve the problems of poor mechanical properties and cumbersome installation of the existing fireproof door core boards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phosphogypsum fireproof door core filler and preparation method thereof
  • Phosphogypsum fireproof door core filler and preparation method thereof
  • Phosphogypsum fireproof door core filler and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A phosphogypsum fire door core filler, comprising the following components in parts by weight: 850 parts of alpha-type phosphogypsum, 60 parts of polyester fibers, 39 parts of redispersible latex powder, 370 parts of expanded foam microbeads, powder 128 parts of coal ash microbeads, 3 parts of waterproofing agent, 15 parts of aluminum powder, 15 parts of lime;

[0030] The preparation method includes the following steps:

[0031] 1) Weigh the α-type phosphogypsum, polyester fiber, redispersible latex powder, expanded foamed microbeads, fly ash microbeads and waterproofing agent and mix them uniformly to obtain composite phosphogypsum powder;

[0032]2) Water is firstly added to the mixer, and then the compound phosphogypsum powder after step 1) is evenly mixed into the mixer for uniform mixing. The mass ratio of the compound phosphogypsum powder and water is 1:2. component A;

[0033] 3) Weigh the aluminum powder and lime and mix them evenly, and obtain component B af...

Embodiment 2

[0037] A phosphogypsum fire door core filler, comprising the following components in parts by weight: 800 parts of alpha-type phosphogypsum, 55 parts of polyester fibers, 35 parts of redispersible latex powder, 350 parts of expanded foamed microbeads, powder 120 parts of coal ash microbeads, 2.8 parts of waterproofing agent, 12 parts of aluminum powder, 12 parts of lime;

[0038] The preparation method includes the following steps:

[0039] 1) Weigh the α-type phosphogypsum, polyester fiber, redispersible latex powder, expanded foamed microbeads, fly ash microbeads and waterproofing agent and mix them uniformly to obtain composite phosphogypsum powder;

[0040] 2) Water is firstly added to the mixer, and then the compound phosphogypsum powder after step 1) is evenly mixed into the mixer for uniform mixing. The mass ratio of the compound phosphogypsum powder and water is 1:2. component A;

[0041] 3) Weigh the aluminum powder and lime and mix them evenly, and obtain component...

Embodiment 3

[0045] A phosphogypsum fire door core filler, comprising the following components in parts by weight: 900 parts of alpha-type phosphogypsum, 65 parts of polyester fibers, 42 parts of redispersible latex powder, 390 parts of expanded foamed microbeads, powder 140 parts of coal ash microbeads, 3.2 parts of waterproofing agent, 18 parts of aluminum powder, 18 parts of lime;

[0046] The preparation method includes the following steps:

[0047] 1) Weigh the α-type phosphogypsum, polyester fiber, redispersible latex powder, expanded foamed microbeads, fly ash microbeads and waterproofing agent and mix them uniformly to obtain composite phosphogypsum powder;

[0048] 2) Water is firstly added to the mixer, and then the compound phosphogypsum powder after step 1) is evenly mixed into the mixer for uniform mixing. The mass ratio of the compound phosphogypsum powder and water is 1:2. component A;

[0049] 3) Weigh the aluminum powder and lime and mix them evenly, and obtain component...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses ardealite fireproof door core filler and a preparation method thereof, belongs to the technical field of door core filler processing, and aims at solving the problems that an existing fireproof door core plate is poor in mechanical property and tedious in door core plate installation. The preparation method comprises the following steps: weighing alpha type phosphogypsum, polyester fiber, redispersible latex powder, expanded foaming microbeads, fly ash microbeads, a waterproof agent, aluminum powder and lime according to component amounts, mixing to obtain composite phosphogypsum powder, mixing the composite phosphogypsum powder with water according to a mass ratio of 1: 2 to obtain a component A, mixing the aluminum powder with the lime to obtain a component B, mixing the component A with the component B according to a mass ratio of 1: 1 to obtain a liquid slurry filler, and mixing the liquid slurry filler with water according to a mass ratio of 1: 1 to obtain the waterproof material. And the liquid slurry filler is poured into the door plate cavity, the liquid slurry filler is naturally foamed for 1.5-2 h, and the liquid slurry filler is in a solid state after being foamed. The problems that a fireproof door core plate is poor in mechanical property and tedious in door core plate installation are solved, and the fireproof door core plate has the advantages of sound insulation, heat insulation, heat preservation, fire prevention, light volume weight and the like.

Description

technical field [0001] The invention belongs to the technical field of door core processing, and in particular relates to a phosphogypsum fireproof door core filler and a preparation method thereof. Background technique [0002] The door panel is composed of skeleton, door core filling material and fireproof hardware. The filling material of the door core panel is the core material to improve the performance of the door core panel. Existing door core board Most of the filling materials of the existing door core board are rock wool, aluminum silicate wool, mineral wool, perlite board, foamed magnesium oxychloride cement board, foamed cement board and other materials. Aluminum silicate wool board, rock wool, slag wool or glass wool fireproof door board, although these materials are light in weight and good in heat insulation, but high energy consumption in the production process, using organic adhesive to form, the production process and use process produce Pollution, it is d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/08C04B38/02C04B28/14C04B16/06C04B24/42B28C5/40E06B3/70E06B5/16C04B111/28
CPCC04B38/085C04B38/02C04B28/143C04B16/0683C04B24/42B28C5/402B28C5/388E06B3/70E06B5/16C04B2111/28C04B38/0006C04B2103/0057C04B20/0036C04B18/082C04B22/04C04B22/064
Inventor 李玮贺靖陈英
Owner GUIZHOU ZHENGHE AERATED CONCRETE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com