Fe monatomic catalyst Fe-PANI and preparation method thereof

A catalyst and atom technology, which is applied in the field of Fe single-atom catalyst Fe-PANI and its preparation, can solve the problems of the narrow pH range of homogeneous Fenton and the inability to recycle Fe of the catalyst, and achieve high heterogeneous Fenton catalytic activity. and stability, less environmental hazard, and the effect of improving transmission efficiency

Pending Publication Date: 2022-05-31
XI AN JIAOTONG UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the deficiencies in the prior art, the object of the present invention is to provide a Fe single-atom catalyst Fe-PANI and a preparat

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fe monatomic catalyst Fe-PANI and preparation method thereof
  • Fe monatomic catalyst Fe-PANI and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

1

2) dipping polyaniline carrier in the mixed solution of iron salt solution or ferrous salt solution or iron salt and ferrous salt

Fig. 1 and Fig. 2 are respectively the high-resolution transmission electron microscope of the Fe single-atom catalyst Fe-PANI that this embodiment prepares

For verifying the Fe-PANI catalyst prepared by the method of the present invention to the treatment effect of refractory organic waste water, with

Example Embodiment

2+

2) dipping polyaniline carrier in the mixed solution of iron salt solution or ferrous salt solution or iron salt and ferrous salt

Example Embodiment

3+

2) dipping polyaniline carrier in the mixed solution of iron salt solution or ferrous salt solution or iron salt and ferrous salt

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a Fe monatomic catalyst Fe-PANI. The preparation method comprises the following steps: 1) pretreating a polyaniline carrier; polyaniline in a complete oxidation state or an intermediate oxidation state is directly used as a carrier; the polyaniline in the acid-doped state is used as a carrier after being subjected to alkali washing; (2) dipping the polyaniline carrier in a ferric salt solution or a ferrous salt solution or a mixed solution of ferric salt and ferrous salt, so that Fe atoms are coordinated with imine nitrogen atoms in polyaniline to be loaded on the surface of polyaniline; and 3) separating out the polyaniline carrier loaded with Fe atoms, washing the polyaniline carrier with deionized water, and drying to obtain the Fe monatomic catalyst Fe-PANI. The invention further relates to the Fe monatomic catalyst Fe-PANI prepared through the method, polyaniline serves as a carrier of the Fe monatomic catalyst Fe-PANI, and Fe monatomic atoms are stably loaded on the surface of the polyaniline carrier in a highly dispersed mode through coordination.

Description

technical field [0001] The invention relates to a catalyst and water treatment technology, in particular to an Fe single-atom catalyst Fe-PANI and a preparation method thereof. Background technique [0002] Homogeneous Fenton oxidation technology is often used in the treatment of organic wastewater that is refractory to biodegradation or difficult to treat with general chemical oxidation technology. The mechanism is that ferrous ions (Fe 2+ ) catalyzes the decomposition of hydrogen peroxide to produce strong oxidizing hydroxyl radicals (oxidation potential, as high as 2.80V, second only to fluorine). Hydroxyl radicals have high electronegativity or electrophilicity, and their electron affinity is as high as 569.3kJ, so they have strong addition reaction characteristics and can effectively degrade organic pollutants in water bodies. However, the homogeneous Fenton reaction has disadvantages such as narrow pH range (about 3), difficulty in catalyst recovery, and generation of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J31/06B01J31/18C02F1/72C02F101/30
CPCB01J31/069B01J31/1805B01J35/004C02F1/722C02F1/725B01J2531/842C02F2101/30C02F2101/40C02F2305/10C02F2305/023C02F2209/06Y02P20/584
Inventor 杨鸿辉石博方李航
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap