Latex special for dry method dustless paper and its preparing method

A clean paper and dry process technology, applied in the direction of adding water repellents, can solve the problems of latex easily sticking to machinery and equipment, unsuitable for clean paper production, yellowing on the surface of latex, etc. Easy to understand operation, stable product quality effect

Inactive Publication Date: 2004-12-15
李泽潜 +3
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Comprehensive comparison of three types of copolymers, diene latex, because ethylene is a gas at room temperature, there are many inconveniences in transportation, use, and production processes; raw materials must be pre-emulsified in production, which increases the production steps, and the degree of monomer pre-emulsification Strict requirements, poor production operability
Styrene-butadiene copolymer can be cured quickly when the curing temperature and time are limited during the production process, but the surface of the latex is generally yellowish, which is not suitable for the production of dust-free paper
The third type of acrylic copolymer has low odor, but the cost of raw materials is relatively high. At the same time, this kind of latex is easy to stick to machinery and equipment, which is difficult to clean, which is not conducive to spraying and sizing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The present invention is described in detail below in conjunction with embodiment.

[0018] The special latex for dry-process dust-free paper of the present invention is a kind of styrene and acrylic acid ester copolymer, which belongs to the water-based polymer emulsion type adhesive, and the production process is as follows:

[0019] 1. Formula (according to 100 parts by mass):

[0020] Butyl acrylate 19, methyl acrylate 3, hydroxyethyl acrylate 4, styrene 12, acrylic acid 2, butyl methacrylate 1, NaHCO 3 , deionized water 55, initiator 0.4, emulsifier 3, stabilizer 0.6.

[0021] The above-mentioned initiator adopts ammonium persulfate, and the emulsifier adopts MS-1 and OP-10.

[0022] 2. Method:

[0023] Take butyl acrylate, methyl acrylate, hydroxyethyl acrylate, styrene, acrylic acid and butyl methacrylate according to the ratio of the formula, mix them thoroughly to form monomers, and put them into the monomer high tank of the polymerization kettle for standby...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to latex specially for dry process dustless paper and its preparation process, and belongs to the field of special chemical. butyl acrylate, methyl acrylate, ethoxyl acrylate, styrene, acrylic acid and butyl methacrylate as monomers, are added with deionized water, emulsifier, NaHCO3 and initiator to produce branch chain connection to form copolymer. The present invention can meet the requirement of producing dustless paper and is favorable to spraying. The present invention has high fiber combining strength of paper, high dry and wet strength, simple production operation and stable product quality.

Description

technical field [0001] The invention belongs to special chemicals for papermaking, in particular to a special latex for the production of dry dust-free paper. The invention also relates to a method for preparing the latex. Background technique [0002] Special latex for dry-laid dust-free paper is a water-soluble emulsion polymer polymerized adhesive. In the dry-laid forming paper web, it plays the role of bonding fluff pulp fibers, and its quality directly affects the product. price and quality. Latex is a kind of polymer, which is composed of multiple chemical chains called monomers. The chemical characteristics of monomers will affect the strength, hardness, viscosity, absorption rate, solvent resistance and flame retardancy of latex. The common types of latex polymerization are: A ethylene and vinyl acetate copolymer (commonly known as diene latex), B styrene-butadiene copolymer, and C acrylate copolymer. Comprehensive comparison of three types of copolymers, diene la...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H21/16
Inventor 李泽潜王东升吴存军杨西军
Owner 李泽潜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products