Nano inorganic germicide and its preparation method

A nano-inorganic, antibacterial agent technology, applied in the field of nanomaterials, can solve the problems of large amount of antibacterial agent, few antibacterial active ingredients, no antibacterial properties, etc., to achieve the effect of improving bactericidal ability and efficiency, enhancing affinity and reducing dosage

Inactive Publication Date: 2005-03-09
骆天荣
View PDF1 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many reports on nano-inorganic antibacterial agents, most of which are loaded on inorganic carrier materials (such as molecular sieves, montmorillonite, calcium carbonate, etc.) with nano-scale silver, zinc, copper, rare earth elements, etc. The disadvantage is that the carrier materials have no antibacterial properties and are effective in antibacterial Less ingredients, large amount of antibacterial agent; in the patent CH1341358A, a kind of antibacterial agent composed of water-based amino acid silver, amino acid zinc and its decomposition generated nano-metal silver and nano-zinc oxide as the main material is disclosed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano inorganic germicide and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment one nanometer inorganic antibacterial agent and preparation method thereof:

[0016] 1, the nano inorganic antibacterial agent of this example, its each component ratio is: zinc oxide: copper carbonate: silver chloride: cerium sulfate: calcium phosphate: titanium sulfate: lanthanum nitrate=85%: 0.1%: 1%: 1% : 9%: 1.9%: 2%, (percentage by weight), the sum of the proportions of each component is 100%.

[0017] 2. The preparation method of the nano-inorganic antibacterial agent of this example: prepare zinc-ammonia complex solution with 85% zinc oxide according to the requirements of patent ZL98 1 16820.5, and add 0.1% copper carbonate, 1% silver chloride, and 1% cerium sulfate respectively in order , 9% calcium phosphate, 1.9% titanium sulfate, 2% lanthanum nitrate, heat the solution to 40°C, chemical coprecipitation at PH=8.5, filter, wash, dry, and calcinate to obtain the finished product, add it to plastic products, Antibacterial effect is very good. 100% ...

Embodiment 2

[0018] Embodiment two nano inorganic antibacterial agent and preparation method thereof:

[0019] 1, the nano inorganic antibacterial agent of this example, its each component ratio is: zinc oxide: copper acetate: silver nitrate: thorium sulfate: lanthanum nitrate: iron phosphate: magnesium sulfate=55%: 15%: 12%: 10%: 2%: 3%: 3%, (percentage by weight), the sum of the proportions of each component is 100%.

[0020] 2. The preparation method of the nano-inorganic antibacterial agent of this example: 55% zinc oxide is prepared according to the requirements of the patent ZL981 16820.5 to prepare a zinc-ammonia complex solution, and 15% copper acetate, 12% silver nitrate, 10% thorium sulfate, and 2% silver nitrate are added in order. Lanthanum nitrate, 3% iron phosphate, 3% magnesium sulfate, heat the solution to 98°C, chemical co-precipitation at PH=4, filter, wash, dry, and calcinate to obtain the finished product, add it to paint products, the antibacterial effect is very good ...

Embodiment 3

[0021] Embodiment three nanometer inorganic antibacterial agent and preparation method thereof:

[0022] 1, the nano inorganic antibacterial agent of this example, its each component ratio is: zinc oxide: copper sulfate: silver nitrate: cerium sulfate: rubidium chloride: lanthanum chloride=55%: 15%: 15%: 10%: 2 %: 3%, (percentage by weight), the sum of the proportions of each component is 100%.

[0023] 2, the preparation method of the nano-inorganic antibacterial agent of this example: 55% zinc oxide is prepared zinc-ammonia complex liquid according to the requirement of patent ZL98 1 16820.5, add 15% copper sulfate in order, 15% silver nitrate, 10% cerium sulfate, 2 % rubidium chloride, 3% lanthanum chloride, heat the solution to 75°C, chemical co-precipitation at PH=7, filter, wash, dry, and calcinate to obtain the finished product, add it to textile products for trial use, the antibacterial effect is very good . The killing rate of Staphylococcus aureus is 100% within 3 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

An inorganic nano-bacterial agent is prepared from nano-zinc oxide and water-soluble metal salt through chemical coposition, washing, drying and calcining.

Description

1. Technical field: [0001] The invention discloses a nano inorganic antibacterial agent and a preparation method thereof, belonging to the technical field of nano materials, and in particular relates to a nano inorganic antibacterial agent mainly composed of nano zinc oxide and a preparation method thereof. 2. Background technology [0002] As we all know, harmful bacteria are an important factor that causes human diseases and affects health. Therefore, how to eliminate and suppress harmful bacteria has been one of the focuses of scientists from all over the world since the discovery of bacteria. With the continuous development of science and technology, various antibacterial materials emerge in endlessly, which can be roughly divided into inorganic antibacterial agents and organic antibacterial agents. Most of the traditional inorganic antibacterial agents are toxic or corrosive, and their stability is poor, which limits the use of inorganic antibacterial agents. use. Org...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A01N59/16
Inventor 骆天荣任真赵永红乔爱萍
Owner 骆天荣
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap