A technology of gold ore and gold concentrate, which is applied in the field of extracting gold from platinum, palladium, refractory gold ore and gold concentrate, can solve the problems of increased maintenance costs, low product yield, and environmental pollution, and achieve production The effect of cost reduction, equipment investment reduction and high output

Inactive Publication Date: 2005-07-06
邹贵田
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In the existing technology, the production pretreatment of arsenic and sulfur-containing refractory gold ores is mainly roasted, and the obtained products are directly cyanided and stirred and leached. Waste gas, waste residue and waste liquid will be generated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for extracting gold, platinum and palladium from goldmine

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Example 1: 10,000 grams of Beishan gold mine (which contains 1.2% of C, 25% of S, and 8% of As) is crushed and finely ground to -200 mesh (85% passes), and the resulting gold ore powder is heated to 800°C , feed oxygen for 2.5 hours, decarburization, arsenic fixation, and sulfur fixation. The ore powder obtained after pretreatment is added to the agitator for leaching. The leachate is a 30% (NaCl) solution, and 3% of the oxidizing agent is added to the solution. Among the added oxidizing agents, NaClO 4 、H 2 o 2 , NaClO 3 Each takes one-third. Adjust the solid-liquid ratio to 1:5, stir at a temperature of 70°C, and react for 2.5 hours. After the reaction is completed, the solution is filtered and separated, and the filtrate is separated from gold with resin or activated carbon. The resin or activated carbon that adsorbs gold is desorbed. The desorption solution is electrolyzed as the electrolyte, and gold is precipitated at the anode of the electrolysis, and the gold...

Embodiment 2

[0042]Example 2: 15,000 grams of a certain gold ore (which contains S14%, As 3.5%) is pulverized and finely ground to -200 mesh (85% passes through), and the resulting gold ore powder is heated to 750°C, and oxygen is fed into it. For 3.0 hours, arsenic and sulfur were fixed, and the ore powder obtained through roasting pretreatment was added to the agitator for leaching. The leaching solution was a 28% (NaCl) solution, and 3% of the oxidizing agent was added to the solution. In the added oxidizing agent, NaClO 4 、H 2 o 2 , NaClO 3 Each takes one-third. Adjust the solid-liquid ratio to 1:4, stir at a temperature of 75°C, and pass the reaction time for 2.5 hours. After the reaction is completed, filter and separate, and separate the gold with resin or activated carbon. The resin or activated carbon that adsorbs gold is desorbed and the solution is used as electrolysis solution, electrolysis, gold is precipitated on the anode of electrolysis, and the gold is removed and cast ...

Embodiment 3

[0043] Embodiment 3: 50,000 grams of gold ore (wherein containing C 1.0%, S 15%, As 3.5%) of a certain scene ore is through crushing, finely ground to-200 order (by 85%), and the gold ore powder of gained is heated To 800°C, feed oxygen for 2.5 hours, fix arsenic, decarburize, and fix sulfur. The ore powder obtained after pretreatment is added to the mixer. The leachate is a 25% (NaCl) solution, and 2% of the oxidant is added to the solution. NaClO in oxidizing agent 4 、H 2 o 2 , NaClO 3 Each takes one-third. Adjust the solid-liquid ratio to 1:5, stir at a temperature of 80°C, and pass the reaction time for 2.5 hours. After the reaction is completed, filter and separate, and use resin or activated carbon to adsorb gold. The gold-adsorbed resin or activated carbon is desorbed and desorbed. As electrolyte electrolysis, gold is precipitated on the anode of electrolysis, the gold is removed, and cast into gold ingots, the yield of gold is 97%; the remaining mother liquor after...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for extracting gold, platinum and palladium from infusible gold ore, comprising: disintegrating infusible gold ore, pre-processing them by roasting, leaching out the roasted product by salt water, filtrating and separating, adsorbing filter liquor by active carbon and extracting gold, separating platinum and palladium from the remain filter liquor by extraction. The invention is a cyanogens-less leaching method with advantages of high extraction ratio of gold, platinum and palladium, less environmental pollution and good economic returns.

Description

technical field [0001] The invention belongs to a method for extracting gold, platinum and palladium from gold ore, in particular to a method for extracting gold, platinum and palladium from insoluble gold ore and gold concentrate. Background technique [0002] Gold, platinum, and palladium are rare and precious metals. Because of their small reserves in nature, stable chemical properties, high temperature resistance, corrosion resistance, and not easy to be oxidized, they are called rare and precious metals. Gold has played a very important role in the history of mankind. It has been used as currency or equivalent to currency for a long period of time. In recent decades, with the rapid development of science and technology, these rare and precious metals are used in aerospace, electricity, In the fields of chemistry and military science, there are some uses that other metals cannot replace, so the demand for these rare and precious metals has increas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B1/02C22B3/04C22B3/24C22B3/26
CPCY02P10/20
Inventor 邹贵田
Owner 邹贵田
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap