Boron absorptive material and its preparing method

A technology of adsorption material and porous material, which is applied in the field of composite material preparation and adsorption separation, can solve the problem of limiting the application of adsorption method, reducing the surface utilization rate of high polymer carrier, thermal stability, mechanical stability and solvent resistance of high polymer carrier Poor performance and other problems, to achieve the effect of high yield, high surface modification ratio and high selectivity

Inactive Publication Date: 2005-09-14
INST OF PROCESS ENG CHINESE ACAD OF SCI
View PDF1 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 2) After the polymer is functionalized, there are many functional groups in the highly crosslinked network of the polymer. Although the situation will be improved after the swelling of the solvent, it may still be difficult to be approached by the reactant molecules,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Boron absorptive material and its preparing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Using silica gel as the adsorbent carrier, the carrier has micropores, mesopores and macropores, with an average pore diameter of 8.5nm and a specific surface area of ​​512m 2 / g, the pore volume is 1.1ml / g. 10g of silica gel and 10g of γ-aminopropyltriethoxysilane were refluxed in 200ml of toluene solvent for 6 hours to obtain an intermediate product, and then 10g of the intermediate product was reacted with 20g of glucose in 200ml of methanol for 10 hours. The reaction process was performed with N 2 protection, the light yellow boron adsorption material was prepared, with an average pore size of 4.5nm and a specific surface area of ​​334m 2 / g, pore volume 0.67ml / g.

[0049] Take 0.1g of this adsorption material, add 10ml of Qinghai Chaerhan Salt Lake brine with a pH value of 5.05 and boron content of 267ppm, and after equilibrating for 24 hours, use the ICP-AES method to detect the concentration of boron in the brine before and after adsorption. The boron adsorption...

Embodiment 2

[0051] Using cetyltrimethylammonium bromide (CTAB) as template, tetraethyl orthosilicate (TEOS) as organosilicon source, ethanol (EtOH) and water as solvent, and ammonia water to adjust the pH value of the system, synthesized Ordered silicon-based mesoporous material MCM-41. Under mechanical stirring, the silicon source was added into the template agent aqueous solution, stirred at room temperature for 1 hour, and then statically crystallized at 80° C. for 24 hours. Filter and wash with deionized water until neutral. Calcined at 540° C. for 4 hours to obtain a mesoporous silica carrier. The carrier has a most probable pore diameter of 2.5nm and a specific surface area of ​​1260m 2 / g. 2g of the carrier was first reacted with 5g of γ-aminopropyltriethoxysilane in 50ml of dichloromethane solvent under reflux for 6 hours to obtain an intermediate product, and then 2g of the intermediate product was reacted with 7g of glucose in 80ml of ethanol for 10 hours, and the reaction pr...

Embodiment 3

[0054] Using Pluronic P123 as the template, cetyltrimethylammonium bromide (CTAB) as the co-template, tetraethyl orthosilicate (TEOS) as the organic silicon source, water as the solvent, and hydrochloric acid to adjust the pH value of the system , Synthesis of ordered silicon-based mesoporous material SBA-15. Under mechanical stirring, the silicon source was added into the aqueous template solution, stirred at room temperature for 20 hours, and then crystallized at rest for 24 hours. Filter, wash with deionized water until neutral, dry at room temperature, and bake at 550°C for 4 hours to obtain the SBA-15 carrier. The carrier has a most probable pore diameter of 6.5nm and a specific surface area of ​​1007m 2 / g. React 2g of the carrier with 10g of γ-chloropropyldimethylmethoxysilane in 100ml of n-hexane at room temperature for 48 hours to obtain a chloropropyl-containing intermediate, then mix 2g of the intermediate with 5g of N-methylglucamine in 50ml Reflux reaction in d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Apertureaaaaaaaaaa
Pore volumeaaaaaaaaaa
Average pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the boron absorbing material and its preparation method and belongs to the multiple materials preparation and absorbing separation fields. It is to load multi-hydroxyl functional genes on the surface of inorganic multi-hole carrier in non-medium water to prepare the boron absorbing material with special structure and surface chemical character. The invention is suitable for the absorbing separation and collection of various enhydrous agents with boron and provides an effective way for the utilization of the boron resources and the treatment of the boron waster water.

Description

technical field [0001] The invention belongs to the field of composite material preparation and adsorption separation, and in particular relates to an organic-inorganic composite boron adsorption functional material and a preparation method thereof, and is used for adsorption and separation of boron in a boron-containing solution. technical background [0002] Boron and its compounds are widely used in metallurgy, medicine, glass, ceramics, fertilizers, textiles, leather, paints, pigments, military, aerospace and other industrial sectors. Since the reserves of easily decomposable high-grade borate ore are decreasing with the massive consumption of boron ore resources, countries all over the world attach great importance to the development of boron-containing aqueous solutions. In addition, while using boron, the discharge of waste water and mother liquor from boron raw material processing also causes environmental pollution and greatly affects the e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/22B01J20/32
Inventor 王丽娜齐涛张懿
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap