Process for preparing submicron grade barium strontium phthalate powder by packing method

A barium strontium titanate, submicron technology, applied in the field of ceramic powder preparation, can solve problems such as difficulty in obtaining stoichiometric ratio, difficulty in removing impurity ions, and limiting practical application, and achieves fine particle size, low dielectric loss, The effect of easy control of the process

Inactive Publication Date: 2006-06-28
JIANGSU SOUTH PORCELAIN INSULATOR CO LTD
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current various liquid-phase methods have greatly limited their practical application due to some insurmountable shortcomings.
For example, the agglomeration of powder prepared by co-precipitation method is relatively serious (Y.B.Khollam, S.B.Deshpande, H.S.Potdar, Mater Charact 2005; 54:6

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for preparing submicron grade barium strontium phthalate powder by packing method
  • Process for preparing submicron grade barium strontium phthalate powder by packing method
  • Process for preparing submicron grade barium strontium phthalate powder by packing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Example 1: Preparation of ultrafine BST powder under the condition of pH=7

[0021] according to figure 1 As shown in the process, first configure a certain concentration (1mol / l) of strontium nitrate solution, then mix barium carbonate, titanium dioxide and strontium nitrate solution according to the stoichiometric ratio (Ba:Sr:Ti=0.70:0.30:1.00), and add 0.5%-1% polyacrylic acid with a concentration of 50% relative to the total weight of the barium carbonate and titanium dioxide solids is used as a dispersant and a surfactant, and wet ball milled for 24 hours. Take out the mixed slurry, add the pre-prepared, excess ammonium bicarbonate solution (concentration: 1mol / l) under stirring, adjust the pH value to about 7 with ammonia water, so that the strontium ions are evenly wrapped in the form of strontium carbonate precipitation A stable slurry is formed on the surface of barium carbonate and titanium dioxide particles. The precipitate is filtered, washed, dried and c...

Embodiment 2

[0022] Example 2: Preparation of ultrafine BST powder under the condition of pH=10

[0023] according to figure 1As shown in the flow chart, a strontium nitrate solution with a certain concentration (2mol / l) is first configured, then barium carbonate, titanium dioxide and strontium nitrate solution are mixed according to the stoichiometric ratio (Ba:Sr:Ti=0.90:0.10:1.00), and Add 0.5%-1% polyacrylic acid with a concentration of 50% relative to the total weight of barium carbonate and titanium dioxide solids as a dispersant and surfactant, and wet ball mill for 24 hours. Take out the mixed slurry, add the pre-prepared and excess ammonium bicarbonate solution (concentration is 1mol / l) under stirring, and adjust the pH value to about 10 with ammonia water, so that the strontium ions are evenly distributed in the form of strontium carbonate precipitation Wrapped on the surface of barium carbonate and titanium dioxide particles to form a stable slurry. The precipitate is filtered...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A process for preparing submicron-class barium strontium titanate (BST) powder by wrapping method includes such steps as mixing barium carbonate powder, TiO2 powder and strontium nitrate solution, adding polyacrylic acid, wet ball grinding, adding excessive ammonium bicarbonate solution while stirring, using ammonia water to regulate pH=7-10 for depositing the strontium carbonate on the surface of barium carbonate and TiO2 particles, filtering, washing, drying and calcining.

Description

technical field [0001] The invention relates to a preparation method of barium strontium titanate (BST) submicron powder, belonging to the category of ceramic powder preparation. This method is different from the traditional solid-phase and liquid-phase preparation methods of BST powder, but uses polyacrylic acid as a dispersant and surfactant, and makes strontium carbonate evenly coated on the surface of solid particles by the encapsulation method to prepare submicron BST powder body. technical background [0002] Ferroelectric BST ceramic materials are widely used in various electronic ceramic devices due to their excellent properties such as high dielectric constant and adjustable Curie temperature. Such as various piezoelectric sensors (Li, X.; Qiu, F.; Guo, K.; Zou, B.; Gu, J.; Wang, J.; Xu, B. Mater. Chem. Phys. 1997, 50 , 227.), Dynamic Random Access Memory (DRAM) (Tahan, D.; Safari, A.; Klein, L.C. in Proc. IEEE. Int. Symp. Appl. Ferroelectr. ed. Pandey, R.K.; Liu,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01G23/00C01F11/00C04B35/47C04B35/626
Inventor 董显林毛朝梁
Owner JIANGSU SOUTH PORCELAIN INSULATOR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap