Biological gradable composite material, its preparing method and use

A technology of biodegradable and composite materials, applied in the fields of biodegradable composite materials and their production methods and applications, to achieve the effects of reduced EVA consumption, high degradation degree, and good physical properties

Inactive Publication Date: 2008-05-28
丁少忠
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is no mention in these patent documents that composite materials containing biodegradable masterbatches can be used to make shoe materials or shock-resistant sheets for packaging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] According to the weight ratio of each component, 100 parts of biodegradable masterbatch, 40 parts of EVA, 40 parts of LDPE, filler CaCO 3 80 parts, 0.3 part of crosslinking agent (DCP) dicumyl peroxide, 3 parts of foaming agent (Ac) butane, 0.7 part of stabilizer calcium stearate, 0.5 part of lubricant stearic acid, nucleating agent powder 0.05 parts of silicon dioxide and 0.4 parts of colorant titanium dioxide were put into a low-speed mixer and stirred for 5 minutes to prepare a blend. Add the blend to the masticator for mastication. The roller temperature of the plasticizer is 160°C±2°C, and the sheet is plasticized for 15 minutes, and the sheet is placed in a hot press for 10 minutes and the pressure is 12-15Mpa. Take out the pressed tablet and trim the corners to make a sheet of a specified size, cut the sheet of a specified size into a small-sized sheet with a slicer, put the small-sized sheet into a molding machine, and press the mold with a steam pressure of 0...

Embodiment 2

[0045] According to the weight ratio of each component, 100 parts of biodegradable masterbatch, 40 parts of EVA, 40 parts of LDPE, filler CaCO 3 80 parts, 0.3 part of crosslinking agent (DCP) dicumyl peroxide, 3 parts of foaming agent (Ac) butane, 0.7 part of stabilizer calcium stearate, 0.5 part of lubricant stearic acid, nucleating agent powder 0.05 parts of silicon dioxide and 0.4 parts of colorant titanium dioxide were put into a low-speed mixer and stirred for 5 minutes to prepare a blend. Add the blended material to the plastic mixer for plastication. The roller temperature of the plastic mixer is 160°C±2°C. Plasticize for 12 minutes to pull the sheet. Put the sheet in a hot press for 10 minutes and press it at a pressure of 12-15Mpa. , take out the pressing sheet and trim the corners to make a sheet of standard size. Use a granulator to make pellets from the sheets with specifications and sizes, put the pellets into the extruder, extrude and foam at the same time, the m...

Embodiment 3

[0048] According to the weight ratio of each component, 100 parts of biodegradable masterbatch, 40 parts of EVA, 40 parts of LDPE, filler CaCO 3 80 parts, 0.3 part of crosslinking agent (DCP) dicumyl peroxide, 3 parts of foaming agent (Ac) butane, 0.7 part of stabilizer calcium stearate, 0.5 part of lubricant stearic acid, nucleating agent powder 0.05 parts of silicon dioxide and 0.4 parts of colorant titanium dioxide were put into a low-speed mixer and stirred for 5 minutes to prepare a blend. Add the blended material to the plastic mixer for plastication. The roller temperature of the plastic mixer is 160°C±2°C. Plasticize for 12 minutes to pull the sheet. Put the sheet in a hot press for 10 minutes and press it at a pressure of 12-15Mpa. , take out the pressing sheet and trim the corners to make a sheet of standard size. Use a granulator to make pellets from the sheets of specifications and sizes, put the pellets into the injection machine, inject and foam at the same tim...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention refers to a biodegradable complex material, the making method and the use. It uses biodegradable mother material as main material, mixes together with EVA, PE, filler, cross-linking agent, vesicant, stabilizing agent, lubricant, colorant and nucleating agent, and get the material through plastication, calendering, flaking, slicing, moulding pressing, foaming and so on. The material can be made into degradable shoe material and aseismatic piece material for packing.

Description

technical field [0001] The invention relates to a biodegradable composite material and its manufacturing method and application, in particular to a composite material used for degradable shoe materials and shock-resistant sheets for degradable packaging. The composite material is made of biodegradable masterbatch The main material is made. Background technique [0002] At present, the main components of shoe materials and shock-resistant sheets for packaging on the market are PVC (polyvinyl chloride), PE (polyethylene), PP (polypropylene), EVA (ethylene-vinyl acetate copolymer), rubber, etc. Petrochemical products, they are all high polymers, because of the high degree of polymerization and strong intermolecular force, the polymer chains are difficult to break and decompose, which leads to the non-degradability of existing shoe materials and shock-resistant packaging sheets, which will pollute environment. At the same time, petroleum is a non-renewable resource on the eart...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L3/04C08L31/04C08L23/06B29C70/00
Inventor 丁少忠
Owner 丁少忠
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com