Reinforced concrete resin slurry casting pipe and method for manufacturing the same

A technology of reinforced concrete resin and production method, which is applied in the directions of mixed operation control, chemical instrument and method, mixed operation control device, etc. Inconvenient construction and other problems, to achieve the effect of light weight, tight interface, simple and ingenious structure

Inactive Publication Date: 2009-05-06
泊谊文化传播(北京)有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, in the technical field of pipeline building materials, there are various pipe fittings such as steel pipes, cast iron pipes, plastic pipes, glass steel pipes, cement pipes, etc.; in these existing known technologies: steel pipes and cast iron pipes are not corrosion-resistant, have short lifespan and are expensive , need to do internal and external anti-corrosion construction, complex and poor working conditions and pollute the environment; plastic pipes and glass steel pipes have low strength, poor load bearing capacity, easy deformation, easy aging, not tight joints during construction, easy to leak, and limited scope of use; The heavy weight of the cement pipe makes it extremely inconvenient to carry and construct, and it is not corrosion-resistant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reinforced concrete resin slurry casting pipe and method for manufacturing the same
  • Reinforced concrete resin slurry casting pipe and method for manufacturing the same
  • Reinforced concrete resin slurry casting pipe and method for manufacturing the same

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 2

[0118] It is carried out according to specific implementation mode 1, except that the operation step ① is to prepare the following raw materials required for the pipe wall by weight according to the following ratio:

[0119] The resin is methacrylic resin: 60%

[0120] Toughening agent is washing oil: 10%

[0121] The plasticizer is polymethyl methacrylate: 3.75%

[0122] Quartz sand: 5%

[0123] Leveling agent is amyl alcohol: 2.75%

[0124] The curing agent is ethylene diamine: 14%

[0125] The accelerator is N,N-dimethylaniline: 2.75%

[0126] The defoamer is vegetable oil: 1.75%

[0127] The total proportion of all raw materials constituting the pipe wall is 100%.

specific Embodiment approach 3

[0128] Carry out the implementation according to specific implementation mode 1, except that the operation step ① is to prepare the following raw materials required for the pipe wall by weight according to the following ratio:

[0129] The resin is unsaturated polyester resin: 10%

[0130] The toughening agent is benzyl alcohol: 15%

[0131] The plasticizer is dibutyl benzoate: 6%

[0132] Quartz sand: 42.5%

[0133] Leveling agent is n-butanol: 5%

[0134] The curing agent is dicumyl peroxide: 11.5%

[0135] The accelerator is N,N-dimethyl-p-methylaniline: 5%

[0136] The defoamer is vegetable oil: 5%

[0137] The total proportion of all raw materials constituting the pipe wall is 100%.

specific Embodiment approach 4

[0138] It is carried out according to specific implementation mode 1, except that the operation step ① is to prepare the following raw materials required for the pipe wall by weight according to the following ratio:

[0139] The resin is epoxy resin: 35%

[0140] The toughening agent is anthracene oil: 8%

[0141] The plasticizer is polymethyl methacrylate: 2%

[0142] Quartz sand: 12.995%

[0143] The leveling agent is tung oil: 1%

[0144] The curing agent is dibenzoyl peroxide: 40%

[0145] The accelerator is a cobalt salt accelerator: 1%

[0146]The defoamer is methyl silicone oil: 0.005%

[0147] The total proportion of all raw materials constituting the pipe wall is 100%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses the reinforcement coagulate resin mortar casting tube and preparing method. The method comprises the following steps: 1 10-60% resin, 3.497-15% toughening agent, 1.5-6% plasticizing agent, 5- 80% quartz sand, 0.5-5% levelling agent, 40-3% curing agent, 0.5-5% accelerating agent, 0.003-5% defoaming agent; 2 mixing resin, plasticizing agent, quartz sand, levelling agent, curing agent and accelerating agent; 3 adding defoaming agent; 4 adding them into die with web tendon; 5 curing, stewing and mould unloading; 6 checking; 7 getting the reinforcement coagulate resin mortar casting tube. The tube is used as tube building material. The invention has the advantages of high strength, light weight, good sealing, corrosion prevention, long lifetime and low cost.

Description

Technical field [0001] The invention relates to a reinforced concrete resin mortar casting pipe and a manufacturing method thereof, which relate to the technical field of building materials; in particular, to the technical field of pipeline building materials; in particular, it relates to the technical field of a reinforced concrete resin mortar casting pipe and a manufacturing method thereof. Background technique [0002] At present, in the field of pipeline building materials technology, there are various pipe fittings such as steel pipes, cast iron pipes, plastic pipes, glass steel pipes, cement pipes, etc. Among these existing known technologies: steel pipes and cast iron pipes are not corrosion resistant and have short life and are expensive. , Need to do internal and external anti-corrosion construction, complex and poor working conditions and pollute the environment; plastic pipes and glass steel pipes have low strength, poor load-bearing capacity, easy to deform, easy to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B28C7/04B28C5/00B28B21/04B28B21/66
Inventor 张炼
Owner 泊谊文化传播(北京)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com