A kind of reuse method of phenol tar waste residue

A technology of tar waste residue and phenol tar, which is applied in the field of phenol tar waste residue as an unsaturated compound monomer polymerization inhibitor, can solve the problems of energy waste, unsuitable tar waste residue, toxic gas pollution, etc., and achieve good polymerization inhibition effect and low cost Low cost and low equipment investment

Active Publication Date: 2011-12-21
SHANGHAI HUAYI NEW MATERIAL
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to incomplete statistics, the annual by-production of such tar waste residues in Jiangsu, Zhejiang, Shandong and other places reaches about 5,000 tons. Now this type of residues are all processed by incineration. waste, and the combustion process will produce a large amount of toxic gas and pollute the environment
However, this method needs to consume a large amount of reagents such as acid and alkali, and will generate a large amount of waste water, and this method is not suitable for the tar waste residue produced by the phenol hydroxylation process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of reuse method of phenol tar waste residue

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-4

[0015] Under the conditions of no air and a temperature of 120°C, acrylic acid with a purity of 99.8% after rectification is used as a raw material. The tar waste residue powder was used as a polymerization inhibitor alone, and the polymerization inhibition experiment was carried out in a 50ml pear-shaped bottle by heating with silicone oil. The results are shown in Table 1.

[0016] Table 1 tar powder alone is the experimental result of polymerization inhibitor

[0017] Example

Amount added / ppm

temperature / ℃

Induction period / h

1

100

120

84

2

200

120

230

3

300

120

378

4

400

120

646

[0018] The hydroquinone of the same addition amount of table 2 is used as polymerization inhibitor experimental result

[0019] comparative example

Embodiment 5-9

[0023] Experimental condition is the same as embodiment 1. The tar waste residue powder was compounded with one of the copper salt compounds, nitrogen oxide free radical compounds, phenols and amine compounds, and the polymerization inhibition experiment was carried out in a 50ml pear-shaped bottle heated with silicone oil. The experimental results are shown in Table 3.

[0024] Table 3 Binary composite polymerization inhibitor experimental results

[0025] Example

Embodiment 10-13

[0033] Experimental condition is the same as embodiment 1. The tar waste residue powder was compounded with two kinds of copper salt compounds, nitrogen oxide free radical compounds, phenols and amine compounds, and the polymerization inhibition experiment was carried out in a 50ml pear-shaped bottle heated with silicone oil. The experimental results are shown in Table 5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for utilizing phenol tar waste residue produced in the process of phenol hydroxylation to produce ortho / hydroquinone as a polymerization inhibitor for unsaturated compound monomers. The tar waste residue is used alone or compounded with one or more selected from copper salt compounds, nitrogen-oxyl radical compounds, phenols and amine compounds as a polymerization inhibitor for unsaturated compound monomers that are prone to self-polymerization, The addition amount of the polymerization inhibitor is 50-5000 ppm of the mass of the unsaturated compound monomer. Through the reuse of tar oil residue, not only the waste residue in the production of hydroquinone is processed, energy is saved, and environmental pollution is reduced. In addition, compared with the polymerization inhibition system used in various unsaturated compound monomers in industry, this The inventive method has better inhibition effect and lower cost.

Description

technical field [0001] The present invention relates to the utilization method of the tar waste residue produced in the process of preparing ortho / hydroquinone by hydroxylation of phenol, specifically the by-product phenol tar waste residue in the process of preparing ortho / hydroquinone by hydroxylation of phenol and hydrogen peroxide As a method of unsaturated compound monomer polymerization inhibitor. Background technique [0002] Catechol and hydroquinone are two important chemical products with a wide range of applications. Catechol, also known as catechol, is a basic organic raw material or intermediate in industries such as pesticides, medicines, spices, rubber, dyes, and photosensitive materials. Hydroquinone, also known as hydroquinone, is mainly used in the synthesis of photosensitive materials, fertilizer additives, anthraquinone dyes and azo dyes, as well as polymerization inhibitors, antioxidants, and rubber additives for synthetic material processing. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07B63/04
Inventor 崔曜许宁唐勇张春雷马建学