Low-temperature dyeing method for aramid/fire-retardant viscose blended fabric

A technology for flame-retardant viscose and blended fabrics, which is applied in the field of textile printing and dyeing, can solve the problems of not bright color of fabrics, poor fabric homochromaticity, limited color types, etc. Effect

Inactive Publication Date: 2009-12-16
XI'AN POLYTECHNIC UNIVERSITY
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to provide a low-temperature dyeing method for aramid fiber/flame retardant viscose blended fabrics, which can dye aramid fiber/flame retardant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature dyeing method for aramid/fire-retardant viscose blended fabric
  • Low-temperature dyeing method for aramid/fire-retardant viscose blended fabric
  • Low-temperature dyeing method for aramid/fire-retardant viscose blended fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] Get sodium hydroxide, oil remover DO and water respectively, mix and prepare pretreatment liquid, the concentration of sodium hydroxide and oil remover DO in this pretreatment liquid is respectively 10g / L and 2g / L; Press bath ratio 50: 1. Put the aramid fiber / flame retardant viscose blended fabric to be dyed into the prepared pretreatment solution, and boil it at 80°C for 30 minutes to remove the oil and stains produced during the weaving process, and then , washed with water and dried; respectively taking pyrrolidone and sulfolane at a volume ratio of 6:4 to prepare a dyeing aid. According to the weight of the aramid fiber / flame-retardant viscose blended fabric after pretreatment, according to the weight percentage (owf) of the dye and the fabric, respectively take 3% of Enix Red, 3% of Cibacron Red, and 3% of Cibacron Yellow B3% and remazol blue B3%, and then take the dispersant NNO, NaCl, the prepared dyeing aid and OP-10 respectively, make the mixed solution of the ...

Embodiment 2

[0079] Get sodium hydroxide, degreasing agent DO water respectively, mix and prepare pretreatment liquid, the concentration of sodium hydroxide and degreasing agent DO in this pretreatment liquid is respectively 15g / L and 2.5g / L; Press bath ratio 50: 1. Put the aramid fiber / flame retardant viscose blended fabric to be dyed into the prepared pretreatment solution, and boil it at 90°C for 40 minutes to remove the oil and stains produced by the fabric during the weaving process. After that, Washing and drying; take acetophenone and sulfolane respectively according to the volume ratio of 6:4, and compound them to obtain dyeing aids; Percentage (owf), respectively take Big Enix Red 5%, Cibacron Red B5%, Cibacron Yellow B5% and Remazol Element Blue B5%, respectively take dispersant NNO, sodium sulfate, prepared dyeing aids and fatty alcohol polyoxyethylene ether, the raw materials taken are made into a mixed solution, and acetic acid is added dropwise in the mixed solution to make a...

Embodiment 3

[0081] Take sodium hydroxide, degreasing agent DO and water respectively, mix and prepare pretreatment liquid, the concentrations of sodium hydroxide and degreasing agent DO in this pretreatment liquid are respectively 12.5g / L and 2.25g / L; 50:1, put the aramid / flame retardant viscose blended fabric to be dyed into the prepared pretreatment solution, boil at 85°C for 35 minutes, and remove the oil and stains generated during the weaving process of the fabric, After that, wash with water and dry; according to the volume ratio of 6:4, take pyrrolidone and sulfolane respectively, and compound them to obtain dyeing aids; Percentage (owf), respectively get Big Enix red 4%, Cibacron red B4%, Cibacron yellow B4% and Remazol blue B4%, respectively get dispersant NNO, NaCl, the dyeing aid that makes and OP-10 nonylphenol polyoxyethylene ether, the raw materials taken are made into a mixed solution, and acetic acid is added dropwise to the mixed solution to obtain a dye solution with a p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low-temperature dyeing method for an aramid/fire-retardant viscose blended fabric, which comprises the steps of: preparing pre-treatment solution; placing an aramid/fire-retardant viscose blended fabric which needs to be dyed into the prepared pre-treatment solution for pre-treatment; compounding to obtain a dyeing assistant; taking a dye which accounts for certain weight percentage of the pre-treated aramid/fire-retardant viscose blended fabric, then taking a dispersant NNO, an electrolyte, anhydrous sodium carbonate, a wetting agent and the prepared dyeing assistant respectively, and preparing the raw materials into dye solution with the pH value of between 4.0 and 5.5; and placing the pre-treated aramid/fire-retardant viscose blended fabric into the prepared dye solution for dyeing, and then finishing the dyeing of the aramid/fire-retardant viscose blended fabric through the afterfinish. The dyeing method can perform integral one-bath dyeing on the aramid/fire-retardant viscose blended fabric, and ensure that the fabric has bright color, lower cost and unlimited color varieties and the fabric has better homochromatism.

Description

technical field [0001] The invention belongs to the technical field of textile printing and dyeing, and relates to a low-temperature dyeing method, in particular to a low-temperature dyeing method of an aramid / flame-retardant viscose blended fabric. Background technique [0002] Aramid / flame-retardant viscose blended fabric is a new type of high-performance heat-resistant and flame-retardant blended fabric, which has the properties of fire prevention, heat resistance and flame retardancy. [0003] The aramid fiber in the aramid / flame-retardant viscose blended fabric is composed of amide groups and benzene rings. The stable skeleton structure endows the fiber with excellent chemical stability, thermal stability, high strength, and high modulus. . Its macromolecular structure is compact, its crystallinity is relatively high, its glass transition temperature is about 270°C, and it has no affinity group. The dye is basically not dyed by conventional dyeing methods. At present,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06P3/852D06P3/84D06P1/16D06P1/38D06P1/44D06P1/651D06P1/642D06M11/38D06M101/06D06M101/36
Inventor 谭艳君刘昌南张方娟
Owner XI'AN POLYTECHNIC UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap