Semi-conductive ethylene vinyl acetate (EVA) plastic for shielding and production method thereof

Abstract

The invention relates to semi-conductive ethylene vinyl acetate (EVA) plastic for shielding and a production method thereof. A formula comprises EVA resin, carbon black, a dispersant, a cross-linking agent, a coupling agent and other aids. The carbon black is highly dispersed under the actions of the dispersant and relevant aids and the interlocking structures of carbon black particles are used, so that an EVA plastic product has high conductivity. The EVA plastic has the advantages of further enhancing the technology content of a cable, improving the flame resistance and the high temperatureresistance of the cable, lowering product cost and enhancing economic benefit. A large amount of graphite is added as a flame-resistant and high temperature-resistant filler and enhances the flame resistance of the cable together with an appropriate amount of chlorinated paraffin and zinc stannate. The filler has high compatibility with other materials and high dispersibility and is matched with other stabilizers, so that a product has high heat resistance stability and flame resistance. Moreover, the lubricating performance of the product is improved to a large extent, a polyvinyl chloride (PVC) mixture has high uniform plasticizing capacity and high-speed melt fluidity, and the product has smooth surface, soft handfeel and high performance.

Description

technical field [0001] The invention relates to a wire and cable plastic and a production method thereof, in particular to a formula of semi-conductive EVA plastic for shielding and a production method thereof. Background technique [0002] With the development of information transmission integration, broadband, intelligence, and digitization, various lines in the integrated wiring system engineering of buildings and buildings are more and more concentratedly arranged together, and high-speed data streams are interfered by the same frequency electromagnetic interference. , Electromagnetic Interference (EMI) and Electromagnetic Compatibility (EMC) issues are becoming more and more obvious. [0003] Early electromagnetic shielding technologies mainly used metals and their composite materials. These materials have good shielding properties, but they have low elasticity, high density, are easy to corrode, are expensive, and the shielding effectiveness is difficult to adjust. ...

AI Technical Summary

Problems solved by technology

The peroxide cross-linking method is widely used, but it requires high temperature and high pressure; the silane boiling cross-linking method requires less investment, and can obtain better peelability than the peroxide cross-linking method, but the production process is complicated and must be processed after extrusion. Cross-linking in moisture can easily cause water-containing micropores on the insulating layer; radiation cross-linking is room temperature cross-linking, and the resulting shielding layer has good performance and high production efficiency, but requires expensive equipment, such as electron ray accelerators, etc.