Nanometer intelligent cleaning antibacterial pearl ceramic glaze

A ceramic glaze and nanotechnology, which is applied in the field of nano-zhijie antibacterial pearl ceramic glaze, can solve the problems of acid and alkali resistance, insufficient hydrophobicity and antifouling technology, insufficient density of ceramic glaze, insufficient brightness and smoothness, etc. Not easy to absorb dirt, high brightness and smoothness, beautiful appearance

Inactive Publication Date: 2011-06-29
陈干礼
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing ceramic glaze adopts the traditional production and sintering process, the density of the ceramic glaze surface is not enough, there are tiny pores, the brightness and smoothness are not enough, the acid and alkali resistance, hydrophobic and antifouling technology is not advanced enough, and the effect is not obvious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A nano-clean antibacterial pearl ceramic glaze, which contains the following components: 200 parts of ordinary ceramic glaze, 0-10 parts of zinc oxide, 0.7-1.0 parts of bismuth trioxide, 1.5-1.8 parts of antimony trioxide, 0.7-1.0 Parts of manganese dioxide, 1.5-1.8 parts of dicobalt trioxide, 0.7-1.0 parts of dichromium trioxide, 1.5-1.8 parts of nickel monoxide, 2.0-2.8 parts of silicon dioxide, 0.15-0.2 parts of diboron trioxide, 0- 0.2 parts of aluminum nitrate nonahydrate, inorganic nanomaterials.

[0015] Its production process is as follows:

[0016] 1. Raw materials enter the factory;

[0017] 2. Raw material appearance inspection, chemical testing and calcination test;

[0018] 3. Determine the ratio of raw materials;

[0019] 4. Grinding by ball mill;

[0020] 5. The finished glaze is sieved to remove impurities;

[0021] 6. Glaze storage pool (use a mixer to stir evenly);

[0022] 7. Spraying;

[0023] 8. Calcined finished products.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A nanometer intelligent cleaning antibacterial pearl ceramic glaze comprises the following components in parts by weight: 200 parts of common ceramic glaze, 0-10 parts of zinc oxide, 0.7-1.0 part of bismuth trioxide, 1.5-1.8 parts of diantimony trioxide, 0.7-1.0 part of manganese dioxide, 1.5-1.8 parts of cobalt oxide, 0.7-1.0 part of chromium oxide, 1.5-1.8 parts of nickel monoxide, 2.0-2.8 parts of silicon dioxide, 0.15-0.2 part of boron trioxide, 0-0.2 part of aluminium nitrate nonahydrate and the balance inorganic nanometer material. The production process of the ceramic glaze comprises the following steps: transferring the raw materials into a plant; inspecting the appearances of raw materials, performing chemical examinations, performing calcination tests; determining the raw material proportionings; milling with a ball mill; sieving the finished glaze to remove impurities; sending the sieved glaze to a glaze slurry storage pool to mix evenly with a mixer; spraying; and calcining to obtain the finished product. The preparation process of the invention is simple, water-saving, environmentally friendly and economical; the ceramic glaze has high glaze density, fewer tiny holes, high brightness and smoothness, large scope of heat resistance, good acid resistance and alkali resistance and self-cleaning and antibacterial effects.

Description

technical field [0001] The invention relates to the technical field of ceramic glaze production technology, in particular to a nano-clean antibacterial pearl ceramic glaze, which is suitable for self-cleaning ceramic products such as power porcelain rods, buildings and households. Background technique [0002] Ceramic glazing can not only make the surface smooth, prevent the absorption of liquid and gas, improve the mechanical strength and insulation performance, but also use various glaze colors as foils to make porcelain more ornamental in addition to practicality, and become a piece of exquisite art. Taste. Existing ceramic glaze adopts traditional production and sintering process. The density of the ceramic glaze surface is not enough, there are tiny pores, the brightness and smoothness are not enough, the acid and alkali resistance, hydrophobic and antifouling technology are not advanced enough, and the effect is not obvious. Contents of the invention [0003] The pu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/86
Inventor 陈干礼
Owner 陈干礼
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products