Filter medium used for removing artificially synthesized musk in drinking water and manufacturing method thereof

A filter medium, artificial synthesis technology, applied in the direction of filtration separation, separation method, alkali metal compounds, etc., can solve the problems of poor handling of concentrated liquid, affecting human health, and high cost of reverse osmosis, achieving low cost and strong surface adsorption capacity. , good removal effect

Inactive Publication Date: 2012-02-15
QIDI ELECTRIC GROUP
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Studies have shown that 77% of synthetic musk enters domestic sewage after use, enters sewage treatment plants through the sewage system, and re-enters the environment with the reuse of sewage sludge, affecting human health
[0005] Conventional water treatment processes are difficult to remove artificial musk from drinking water; air flotation, oxidation and other equipment are complex and inconvenient to use; reverse osmosis is costly and wastes water, and the concentrated solution produced is more difficult to handle and easy to produce secondary pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Filter medium used for removing artificially synthesized musk in drinking water and manufacturing method thereof
  • Filter medium used for removing artificially synthesized musk in drinking water and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) Weigh 100 g of activated carbon fiber powder, with a particle size of 20 μm to 30 μm;

[0030] (2) Take ultra-high molecular weight polyethylene powder 250g, described ultra-high molecular weight polyethylene is the M-II type product of Beijing Dongfang Petrochemical Co., Ltd. Auxiliary No. 2 Factory, and its molecular weight is 2.5 million;

[0031] (3) Immerse the nano silicon oxide in the dodecyltrimethylammonium chloride cationic surfactant solution, the mass percent concentration of the surfactant solution is 10%, and the mass ratio of the nano silicon oxide to the surfactant solution is 1: 30 Stir the mixture at 60°C for 20h, filter, and wash; dry the filtered solid, activate it at 105°C for 1h, then grind it to 50nm-80nm, and weigh 120g of the prepared modified nano-silica powder;

[0032](4) Weigh 150 g of activated alumina powder, with a particle size of 74 m to 89 μm;

[0033] (5) Take food-grade ammonium bicarbonate 100g, and the purity reaches more than...

Embodiment 2

[0039] (1) Weigh 250 g of activated carbon fiber powder, with a particle size of 20 μm to 30 μm;

[0040] (2) Take ultra-high molecular weight polyethylene powder 350g, described ultra-high molecular weight polyethylene is the M-III type product of Beijing Dongfang Petrochemical Co., Ltd. Auxiliary No. 2 Factory, and its molecular weight is 3.5 million;

[0041] (3) Nano silicon oxide is immersed in cetyltrimethylammonium bromide (CTMAB) cationic surfactant solution, the mass percent concentration of surfactant solution is 8%, and the mass ratio of nano silicon oxide and surfactant solution is 1:20; Stir the mixture at 80°C for 8h, filter and wash; dry the filtered solid, activate it at 105°C for 2h, then grind to 50nm-80nm, weigh 150g of the prepared modified nano-silica powder ;

[0042] (4) Weigh 120 g of activated alumina powder, with a particle size of 74 μm to 89 μm;

[0043] (5) Take food-grade ammonium bicarbonate 120g, and the purity reaches more than 99.99%;

[00...

Embodiment 3

[0049] (1) Weigh 150 g of activated carbon fiber powder, with a particle size of 20 μm to 30 μm;

[0050] (2) Take ultra-high molecular weight polyethylene powder 300g, said ultra-high molecular weight polyethylene is the M-II type product of Beijing Dongfang Petrochemical Co., Ltd. Auxiliary No. 2 Factory, and its molecular weight is 2.5 million;

[0051] (3) Nano silicon oxide is immersed in cetylpyridinium bromide cationic surfactant solution, the mass percent concentration of surfactant solution is 5%, and the mass ratio of nano silicon oxide and surfactant solution is 1: 60; Mixture Stir at 40°C for 15h, filter, and wash; dry the filtered solid, activate at 105°C for 3h, then grind to 50nm-80nm, and weigh 180g of the prepared modified nano-silica powder;

[0052] (4) Weigh 100 g of activated alumina powder, with a particle size of 74 μm to 89 μm;

[0053] (5) Weigh 150 g of azodicarbonamide, with a purity of more than 99.99%;

[0054] (6) Put the above five kinds of pow...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a filter medium used for removing artificially synthesized musk in drinking water, which comprises the following steps of: a) mixing the raw materials containing activated carbon fiber powder, ultrahigh molecular weight polyethylene powder, nanometer silicon oxide powder, active alumina powder and a gas generation agent, wherein, the weight ratio ofthe activated carbon fiber powder, the ultrahigh molecular weight polyethylene powder, the nanometer silicon oxide powder, the active alumina powder and the gas generation agent is (100-300): (200-450): (80-200): (80-200): (50-150); and b) suppressing, sintering and cooling the obtained mixture in a mould. The prepared filter medium has high removal rate on the artificially synthesized musk in the drinking water, is suitable for being used in the drinking water polluted by the artificially synthesized musk, and can be used for avoiding the damage of the artificially synthesized musk on human bodies, and is simple in use and low in cost; and in addition, a filter element instead of a powder body is used, thus post-treatment is not needed; and the preparation method is suitable for treatinghome terminal drinking water; and through the detection, the removal rate of the filter medium on the artificially synthesized musk in the drinking water is over 95%.

Description

technical field [0001] The invention relates to a filter medium for removing artificially synthesized musk in drinking water and a preparation method thereof, a filter element, a water purification device and a water dispenser composed of the filter medium. Background technique [0002] With the improvement of people's living standards, the demand for musk is increasing year by year. In addition, the random hunting and killing of animal musk deer has led to the depletion of natural musk resources, which is far from meeting the needs of the society. In order to promote the protection of animal musk deer, People have obtained a class of compounds with a musky smell through artificial synthesis methods, i.e. a substitute for natural musk - artificial musk. [0003] As an alternative fragrance, synthetic musk is widely used in the daily chemical industry. Due to its continuous input into the environment, the concentration of some typical compounds such as Gala musk and Tuna musk...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/26B01J20/30B01J20/28B01D39/14C02F1/28C02F1/58
Inventor 周奇迪栾云堂
Owner QIDI ELECTRIC GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap