Surface sizing agent and preparation method thereof
A surface sizing agent, guar collagen technology, applied in the direction of adding water repellent, can solve the problems of production and environmental impact, slow reaction speed, reduce cationic starch, etc., achieve easy dispersion and use, increase affinity, and improve air permeability Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0017] Example 1
[0018] (1) In the four-necked flask equipped with stirring, thermometer, dripping pipeline and ventilation pipeline, add 200 parts of ethanol, pass nitrogen, add 200 parts of guar collagen powder under stirring, and after 10 minutes of dispersion at room temperature, dropwise add 40 parts of 3-chloro-2-hydroxypropyltrimethylammonium chloride, a cationic etherifying agent, was added dropwise for 15 minutes. After the dropwise addition was completed, sodium hydroxide solution was added to adjust the pH value of the solution to 11.0, and the temperature was heated up. to 70°C, react at this temperature for two hours to obtain cationic guar gum, and cool the system to 30°C;
[0019] (2) adjust the pH value of solution with hydrochloric acid to 4.0, get 0.2 part of peracetic acid and join it in the reactor and mix with cationic guar gum, be warming up to 40 ℃ of reaction 2 hours;
[0020] (3) after above-mentioned solution temperature is reduced to 25 ℃, add 0.2...
Example Embodiment
[0021] Example 2
[0022] (1) In the four-necked flask equipped with stirring, thermometer, dripping pipeline and ventilation pipeline, add 400 parts of ethanol, pass nitrogen, add 200 parts of guar collagen powder under stirring, disperse at room temperature for 10 minutes, add dropwise 80 parts of 3-chloro-2-hydroxypropyltrimethylammonium chloride, a cationic etherification agent, was added dropwise for 10 minutes. After the dropwise addition, sodium hydroxide solution was added to adjust the pH value of the solution to 11.5, and the temperature was heated up. to 60°C, react at this temperature for three hours to obtain cationic guar gum, and cool the system to 25°C;
[0023] (2) adjust the pH value of solution with hydrochloric acid to 3.0, get 0.4 part of peroxysulfuric acid and join it in the reactor and mix with cationic guar gum, be warming up to 50 ℃ of reaction 1.5 hours;
[0024] (3) after above-mentioned solution temperature is lowered to 25 ℃, add 0.4 part of visc...
Example Embodiment
[0025] Example 3
[0026] (1) In the four-necked flask equipped with stirring, thermometer, dripping pipeline and ventilation pipeline, add 300 parts of ethanol, pass nitrogen, add 200 parts of guar collagen powder under stirring, and after 10 minutes of dispersion at room temperature, dropwise add 70 parts of 3-chloro-2-hydroxypropyltrimethylammonium chloride, a cationic etherifying agent, was added dropwise for 15 minutes. After the dropwise addition, a sodium hydroxide solution with a weight concentration of 30% was added to adjust the pH of the solution. The value is 10.5, heated to 55°C, reacted at this temperature for 3.5 hours to obtain cationic guar gum, and the system was cooled to 30°C;
[0027] (2) adjust the pH value of solution with hydrochloric acid to 4.0, get 2 parts of peracetic acid and join in the reactor and mix with cationic guar gum, be warming up to 70 ℃ of reaction 0.5 hour;
[0028] (3) after above-mentioned solution temperature is lowered to 25 ℃, ad...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap