Preparation method of active collagen with triple-helix structure

A triple-helix and active technology, applied in the field of protein engineering, can solve the problems of destroying the triple-helix structure, unable to realize the active collagen triple-helix structure, and low extraction efficiency, and achieve the effects of improving extraction efficiency, low immunogenicity and improving purity.

Active Publication Date: 2012-03-28
无锡贝迪生物工程股份有限公司
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The methods disclosed in the prior art often destroy the triple helix structure of collagen during the extraction and preparation of collagen, or the extraction efficiency is low, and it is impossible to preserve the triple helix structure of active collagen while improving the extraction efficiency and purity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Take fresh cowhide, cut and remove the grease layer and fur layer, remove impurities, wash, break the cowhide into small particles, add 0.03mol / L sodium hydroxide aqueous solution according to the ratio of solid to liquid ratio of 1:30, and Soak at 6-8°C for 2 hours, filter, and set aside;

[0027] (2) Add anhydrous ether or acetone with a quality 8 times that of the cowhide to the cowhide after the above pretreatment, reflux at 35°C for 8 hours, then rinse with distilled water until there is no peculiar smell, and set aside;

[0028] (3) immerse the above-mentioned cowhide in the mixed solution of 0.6mol / L glacial acetic acid and 700mg / L pepsin, and keep stirring for about 25 hours;

[0029] (4) Adopt progressive ultrasonic treatment to the above mixture, first use 100W ultrasonic treatment for 30 minutes, then use 300W ultrasonic treatment for 30 minutes, and finally use 400W ultrasonic treatment for 1 hour;

[0030] (5) Add 2% H 2 o 2 Solution, mix and stand f...

Embodiment 2

[0035] (1) Take fresh beef Achilles tendon, cut and remove the grease layer and fur layer, remove impurities, wash, break the beef Achilles tendon into small particles, and add 0.01mol / L of hydrogen peroxide according to the solid-liquid ratio of 1:40 Sodium aqueous solution, soak at 6-8°C for 1 hour, filter, and set aside;

[0036] (2) Add anhydrous ether or acetone with a mass 6 times the mass of the Achilles tendon to the Achilles tendon after the above pretreatment, reflux at 40°C for 5 hours, then rinse with distilled water until there is no peculiar smell, and set aside;

[0037] (3) immerse the above-mentioned bovine Achilles tendon in the mixed solution of 0.7mol / L glacial acetic acid and 600mg / L pepsin, and keep stirring for about 30 hours;

[0038] (4) Adopt progressive ultrasonic treatment to the above mixture, first use 100W ultrasonic treatment for 30 minutes, then use 200W ultrasonic treatment for 30 minutes, and finally use 300W ultrasonic treatment for 1 hour;

...

Embodiment 3

[0044] (1) Take fresh pigskin, cut and remove the grease layer and fur layer, remove impurities, wash, break the pigskin into small particles, and add 0.02mol / L sodium hydroxide aqueous solution according to the ratio of solid to liquid 1:35 , soaked at 6-8°C for 1.5 hours, filtered, and set aside;

[0045] (2) Add anhydrous ether or acetone whose mass is 7 times that of the pigskin to the pigskin after the above pretreatment, reflux at 37° C. for 6 hours, then rinse with distilled water until there is no peculiar smell, and set aside;

[0046] (3) immerse the above-mentioned pigskin in the mixed solution of 0.65mol / L glacial acetic acid and 650mg / L pepsin, and keep stirring for about 28 hours;

[0047] (4) Adopt progressive ultrasonic treatment to the above mixture, first use 150W ultrasonic treatment for 30 minutes, then use 250W ultrasonic treatment for 30 minutes, and finally use 350W ultrasonic treatment for 1 hour;

[0048] (5) Add 2.5% H 2 o 2 solution, mix and stand...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of collagen; fresh pigskin is used as a raw material; the raw material is treated by pretreatment, fat removal, and acid-enzyme treatment; ultrasonic treatment is employed to further improve extraction efficiency; and finally purification is performed to prepare a collagen product with high purity. The preparation method of collagen has high extraction efficiency, and the product purity is up to above 98%. The product is active collagen with a maintained triple-helix structure, has low immunogenicity and high biocompatibility, is biodegradable, and is applicable to medical purposes.

Description

technical field [0001] The invention relates to a preparation method of active collagen with a triple helix structure, which belongs to the field of protein engineering. The product is active collagen maintaining a triple helix structure, has low immunogenicity, high biocompatibility, is biodegradable, and is suitable for use in medical use. Background technique [0002] Collagen is a group of hard proteins with the most abundant content and widest distribution in vertebrates. 25%-33% of the total protein content of the animal body. Several types of collagen are often contained in the same tissue, and a certain type is often the main one. Type I collagen is distributed in all parts of the body, mainly in the skin, tendons and ligaments, and has strong tensile strength. Type II collagen mainly exists in hyaline cartilage and vitreous body, and has a strong ability to resist pressure. Type III collagen is widely distributed in tissues with high extensibility, such as loose...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C07K14/78
Inventor 任伟业
Owner 无锡贝迪生物工程股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap