O-shaped seal ring rubber sizing material of gate valve end surface and preparation method thereof

A technology of O-ring and rubber compound, which is applied in the production of rubber compound for parallel gate valve end face O-ring and its preparation field, which can solve the problems of high cost, expensive raw materials, high sealing performance and corrosion resistance, etc. problems, to achieve good comprehensive performance, low material cost, and good air tightness

Inactive Publication Date: 2012-04-18
TONGLING XINTE VALVE
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the fluid pipeline system, the valve is the control element, its main function is to isolate the equipment and the pipeline system, adjust the flow, prevent backflow, adjust and discharge the pressure, so the requirements for the sealing and corrosion resistance of the valve are relatively high. The existing casting The high temperature resistance and corrosion resistance of the gate valve are not very good. The high temperature resistance and corrosion resistance of the rubber compound of the existing parallel gate valve end face O-ring seal are not very ideal. Although some have good corrosion resistance, the raw materials Expensive, high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • O-shaped seal ring rubber sizing material of gate valve end surface and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] 1. Raw material preparation:

[0032] Preparation of raw materials for rubber compound:

[0033] Weigh nitrile rubber 3304 90, sulfur 0.4, zinc oxide 5, stearic acid 1.5, antioxidant BHT 1.5, antioxidant RD 1.5, antioxidant 4010Na1.5, microcrystalline wax 3.5, quick press carbon black N660 24, High wear-resistant carbon black N330 63, dioctyl sebacate 20, diatomaceous earth 12, accelerator M 3.5, accelerator DM 1.5, accelerator TMTD 1.5,

[0034] Preparation of raw materials for B rubber compound:

[0035] Weigh polyacrylate rubber 85, ethylene propylene rubber 15, sodium stearate 1.5, anti-aging agent RD 2, gelatin T-78 0.5, rhine wax 1.5, quick extruded carbon black 50, graphite powder 12, sebacic acid Dioctyl ester 6, curing agent DCP 1, co-curing agent TAIC 0.6, accelerator Na-22 1.5.

[0036] 2. A method for preparing a gate valve end face O-ring rubber compound, comprising the following steps:

[0037] The first step: Prepare A rubber material and B rubber mat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an O-shaped seal ring rubber sizing material of a gate valve end surface, which is formed by mixing a rubber sizing material A and a rubber sizing material B, wherein the rubber sizing material A comprises the following raw materials in part by weight: 85-95 parts of nitrile rubber 3304, 0.3-0.5 parts of sulphur, 4-6 parts of zinc oxide, 1-1.5 parts of stearic acid, 1-2 parts of 2,6-Di-tert-butyl-p-methyl phenol (BHT), 1-2 parts of anti-aging agent RD, 1-2 parts of anti-aging agent 4010Na, 3-4 parts of microcrystalline wax, 22-25 parts of fast extruding carbon black N660, 62-65 parts of high wear-resistant carbon block N330, 18-22 parts of sebacic acid dioctyl phthalate, 10-15 parts of kieselguhr, 3-4 parts of accelerator M, 1-2 parts of 2,2'-dibenzothiazoledisulfde (DM) and 1-2 parts of tetramethylthiuram disulfide (TMTD); and the rubber sizing material B comprises the following raw materials in part by weight: 82-87 parts of polyacrylate rubber, 13-18 parts of ethylene propylene rubber, 1-2 parts of sodium stearate, 1-3 parts of anti-aging agent RD, 0.4-0.6 parts of gum easyT-78, 1-2 parts of Rhine wax, 45-55 parts of fast extruding carbon black, 10-14 parts of graphite powder, 5-8 parts of sebacic acid dioctyl phthalate, 0.5-1.5 parts of dicumyl peroxide (DCP), 0.2-0.8 part of Triallyl Iso cyanurate (TAIC) and 1-2 parts of accelerator Na-2. The seal ring rubber lining sizing material disclosed by the invention has good comprehensive performance. The produced O-shaped seal ring of the gate valve end surface has the characteristics of good gas tightness, weather resistance, low temperature resistance, oil resistance and the like, and also has low material cost.

Description

technical field [0001] The invention relates to the field of rubber composite material processing, in particular to a rubber compound used for producing an O-shaped sealing ring on the end face of a parallel gate valve and a preparation method thereof. Background technique [0002] In the fluid pipeline system, the valve is the control element, its main function is to isolate the equipment and the pipeline system, adjust the flow, prevent backflow, adjust and discharge the pressure, so the requirements for the sealing and corrosion resistance of the valve are relatively high. The existing casting The high temperature resistance and corrosion resistance of the gate valve are not very good. The high temperature resistance and corrosion resistance of the rubber compound of the existing parallel gate valve end face O-ring seal are not very ideal. Although some have good corrosion resistance, the raw materials Expensive and costly. Contents of the invention [0003] The invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/02C08L33/04C08L23/16C08K13/02C08K3/06C08K3/22C08K5/09C08K3/04C08K5/11C08K3/34C08K5/098B29B7/28B29B7/72
Inventor 吴寿涛
Owner TONGLING XINTE VALVE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products