Preparation method for organic silicon-modified printing adhesive

A silicone and adhesive technology, which is applied in dyeing, textiles and papermaking, can solve the problems of poor wet rubbing fastness and hard hand feeling, and achieve the effects of excellent softness, environmental friendliness and good storage stability

Active Publication Date: 2012-06-20
上海康美特科技发展有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But the existing technology has two disadvantages: first, when the amount of acrylate is large, the hand feels hard; degree difference

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A) Preparation of silicone pre-emulsion:

[0018] First, 140 parts by weight of deionized water, 4 parts by weight of fatty acid polyoxyethylene ether (AEO9) as a composite emulsifier, 3 parts by weight of dodecasulfobenzenesulfonic acid, and 7 parts by weight of organosilicon monomer octamethylcyclotetrasiloxane , 5 parts by weight of polymethylhydrogensiloxane and 0.2 parts by weight of silane coupling agent а-methacryloxypropyltrimethoxysilane were added to the reaction kettle, stirred at room temperature for 40min, and the temperature was raised to 85 °C, react at this temperature for 120min to prepare silicone pre-emulsion

[0019] B) Preparation of printing adhesive:

[0020] Control the temperature of the above-mentioned silicone pre-emulsion to 80°C, and add 8 parts by weight of acrylate monomer methyl acrylate, 32 parts by weight of butyl acrylate, and 0.4 parts by weight of potassium persulfate as an initiator in sequence under rapid stirring at 1000 r / min, w...

Embodiment 2

[0022] A) Preparation of silicone pre-emulsion:

[0023] First, 120 parts by weight of deionized water, 3 parts by weight of fatty acid polyoxyethylene ether (AEO9) as a composite emulsifier, 2 parts by weight of sodium dodecylsulfobenzenesulfonate, and 8 parts by weight of organosilicon monomer octamethylcyclotetrasiloxane parts, 2 parts by weight of polydimethylsiloxane and 0.2 parts by weight of silane coupling agent vinyltrimethoxysilane were added to the reaction kettle, stirred at room temperature for 70min, and the temperature was raised to 80°C to react at this temperature 110 min to prepare a silicone pre-emulsion;

[0024] B) Preparation of printing adhesive:

[0025] The above-mentioned silicone pre-emulsion was controlled at a temperature of 80°C, and 15 parts by weight of the acrylate monomer ethyl methacrylate, 23 parts by weight of butyl acrylate, and 0.4 parts by weight of the initiator potassium persulfate were added dropwise under rapid stirring at 1000 r / mi...

Embodiment 3

[0027] A) Preparation of silicone pre-emulsion:

[0028] First 80 parts by weight of deionized water, 1 part by weight of composite emulsifier Span 80, 2 parts by weight of Tween 80, 1 part by weight of dodecasulfobenzenesulfonic acid, 6 parts by weight of organosilicon monomer decamethylcyclopentasiloxane Parts by weight, 2 parts by weight of polydimethylsiloxane and 0.1 part by weight of silane coupling agent vinyltriethoxysilane were added to the reaction kettle, stirred at room temperature for 60 min, and the temperature was raised to 75°C. React at high temperature for 130 min to prepare silicone pre-emulsion;

[0029] B) Preparation of printing adhesive:

[0030] Control the temperature of the above silicone pre-emulsion to 80°C, add 14 parts by weight of acrylate monomer methyl acrylate, 16 parts by weight of ethyl methacrylate, and 0.2 parts by weight of initiator ammonium persulfate successively under rapid stirring at 1000 r / min. The dropwise addition was completed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method for an organic silicon-modified printing adhesive. The preparation method comprises the following steps of: preparing an organic silicon pre-emulsion: adding 80-140 parts by weight of deionized water, 3-7 parts by weight of a compounding emulsifier, 8-12 parts by weight of an organic silicon monomer and 0.1-0.2 part by weight of a silane coupling agentinto a reaction kettle, stirring at the room temperature for 40-70 minutes, heating to 75-90 DEG C, and reacting at the temperature for 110-130 minutes to obtain the organic silicon pre-emulsion; andpreparing a printing adhesive: controlling the temperature of the organic silicon pre-emulsion at 75-85 DEG C, dropwise adding an acrylate monomer and an initiator in sequence while stirring at the high speed of 1,000 revolutions per minute within 2 hours, heating to 4-6 DEG C, preserving heat for reacting for 25-35 minutes, cooling, and adjusting the pH to 6-7 with sodium hydroxide to obtain theorganic silicon-modified printing adhesive. The preparation method has the advantages of simple process steps, high storage stability, washability, superior softness and contribution to environmentalfriendliness.

Description

technical field [0001] The invention belongs to the technical field of preparation of textile printing and dyeing auxiliaries, and in particular relates to a preparation method of an organic silicon modified printing adhesive. Background technique [0002] Pigment printing achieves the purpose of coloring by means of adhesives to adhere pigment particles to the fabric, so it is not picky about various fibers. Moreover, pigment printing has a simple process, a wide range of colors, easy color matching, and no need for washing after color fixing, so it has the characteristics of water saving and energy saving. In the global printed fabrics or fabrics, the share of pigment printing is increasing year by year. Adhesive is the main component of pigment printing paste, and its quality directly affects the quality of the final product. At present, the adhesives for pigment printing are mainly acrylic esters such as Chinese patents (CN101948555A, CN102190989A, CN101942772A), which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/12D06P1/613D06P1/52
Inventor 方云祥
Owner 上海康美特科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap