Carbon fiber cloth-aluminum alloy compound material and preparation method thereof

A technology of carbon fiber cloth and composite materials, which is applied in the direction of carbon fiber, fiber treatment, metal processing equipment, etc., can solve the problem of difficult composite bonding of carbon fiber cloth, and achieve the effect of good bonding, not easy to detach, and high specific modulus

Inactive Publication Date: 2012-08-22
BEIJING INSTITUTE OF TECHNOLOGYGY
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the disadvantages that carbon fiber cloth is difficult to compound into aluminum alloy and has poor bonding, and to provide a carbon fiber cloth-aluminum alloy with high specific strength, specific modulus, controllable carbon fiber cloth distribution, and controllable aluminum alloy composition. Alloy composite material and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 1. Cut the carbon fiber cloth into 10cm*10cm, make holes for fixing on the edge and use the air burning method to remove the glue, and then use the roughening solution consisting of nitric acid, potassium dichromate, hydrogen peroxide and ammonium persulfate to roughen, apply 10 %NaOH solution and use SnCl 2 Sensitized as a sensitizer, and then the component is PdCl 2 Activate with AgCl activation solution, and finally soak the carbon fiber cloth in 20g / L sodium hypophosphite solution for 1-3 minutes to complete the reduction process;

[0021] 2. The carbon fiber cloth is treated by electroless copper plating. The bath composition contains CuSO 4 , HCHO, NaKC 4 h 4 o 6 . The pH value of the plating solution is 12.7, the plating temperature is 60°C, and the plating time is 20 minutes. In order to maintain the smoothness of the carbon fiber distribution plating process, the electroless copper plating solution is uniformly dispersed by ultrasonic oscillation method....

Embodiment 2

[0025] 1. Cut the carbon fiber cloth into 10cm*10cm, make holes for fixing on the edge and use the air burning method to remove the glue, and then use the roughening solution consisting of nitric acid, potassium dichromate, hydrogen peroxide and ammonium persulfate to roughen, apply 10 %NaOH solution and use SnCl 2 Sensitized as a sensitizer, and then the component is PdCl 2 Activate with AgCl activation solution, and finally soak the carbon fiber cloth in 20g / L sodium hypophosphite solution for 1-3 minutes to complete the reduction process;

[0026] 2. The carbon fiber cloth is copper-plated by electroplating. The plating solution composition is that the plating solution composition used is potassium sodium tartrate 10g / L, potassium nitrate 12g / L, and emulsifier (OP-10) is 0.4g / L. After taking it out, wash it with deionized water for 15 minutes, and then dry it in hot air at 70-80°C for 20 minutes;

[0027] 3, with paraffin 50%, the proportioning of stearic acid 50% (weigh...

Embodiment 3

[0030] 1. Cut the carbon fiber cloth into 10cm*10cm, make holes for fixing on the edge and use the air burning method to remove the glue, and then use the roughening solution consisting of nitric acid, potassium dichromate, hydrogen peroxide and ammonium persulfate to roughen, apply 10 %NaOH solution and use SnCl 2 Sensitized as a sensitizer, and then the component is PdCl 2 Activate with AgCl activation solution, and finally soak the carbon fiber cloth in 20g / L sodium hypophosphite solution for 1-3 minutes to complete the reduction process;

[0031] 2. The carbon fiber cloth is treated by electroless copper plating. The bath composition contains CuSO 4 , HCHO, NaKC 4 h 4 o 6 . The pH value of the plating solution is 12.7, the plating temperature is 60°C, and the plating time is 20 minutes. In order to maintain the smoothness of the carbon fiber distribution plating process, the electroless copper plating solution is uniformly dispersed by ultrasonic oscillation method....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a carbon fiber cloth-aluminum alloy compound material and a preparation method thereof. The carbon fiber cloth-aluminum alloy compound material is obtained by cladding carbon fiber cloth with copper and then casting aluminum alloy. The preparation method comprises the following steps: 1) pre-treating the carbon fiber cloth; 2) cladding the carbon fiber cloth with copper: cladding the surface of the carbon fiber cloth with the copper according to a chemical plating or electroplating method; 3) preparing a casting mould,wherein the casting mould is prepared according to the demand on the arrangement of the carbon fiber cloth in the aluminum alloy; and 4) smelting the aluminum alloy and casting, thereby lastly obtaining the carbon fiber cloth-aluminum alloy compound material in required shape. The carbon fiber cloth-aluminum alloy compound material prepared according to the preparation method is excellently compounded; the components of the aluminum alloy are adjustable; the distribution of the carbon fiber cloth is controllable; and the compound material has higher specific modulus, low density and high specific strength, and is suitable for the building field and the protecting field.

Description

technical field [0001] The invention relates to a preparation process of carbon fiber cloth copper plating and metal composite material, belongs to the field of metallurgy technology, and in particular relates to a preparation method of carbon fiber cloth-aluminum alloy composite material. Background technique [0002] Carbon fiber cloth-aluminum alloy composite material is composed of aluminum alloy with high specific strength and carbon fiber cloth with high specific modulus and tensile resistance. It has the advantages of low density, high specific strength, tensile resistance and high specific modulus. Its mechanical properties can be adjusted within a certain range by adjusting the distribution of carbon fiber cloth in the aluminum alloy and controlling the composition of the aluminum alloy. It has a good application prospect in construction, military industry and other fields. [0003] When carbon fiber cloth is used in building materials at the present stage to be co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B22D19/00B22C9/04D06M11/83D06M101/40
Inventor 刘金旭骆雨萌李树奎王迎春王星
Owner BEIJING INSTITUTE OF TECHNOLOGYGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com