High-strength sealing glue for paper packaging box

A packaging box, high-strength technology, applied in the direction of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc. Low cost, no burning hazard, high initial viscosity

Inactive Publication Date: 2013-01-30
蚌埠市比优特包装印务有限责任公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the sealing glue is not handled well, it is very easy to have false sticking, which leads to the opening of the packaging box

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Prepare the following materials:

[0029] The adhesive is 30 kg of butyl acrylate and 30 kg of EVA emulsion.

[0030] The plasticizer selects 65 kilograms of isooctyl acrylate for use,

[0031] The tackifier is 15 kg of ethylene-vinyl chloride copolymer emulsion,

[0032] The wetting agent is 9 kg of methyl methacrylate,

[0033] 2 kg of acrylic acid and 3.5 kg of methylol acrylamide are selected as the linked monomers,

[0034] emulsifier 800 g,

[0035] Initiator selects 400 grams of ammonium persulfate for use,

[0036] Preservative is selected 150 grams of organosilicon quaternary ammonium salts,

[0037] 500 grams of deionized water, a 300-liter batching tank, agitator, thermometer, and dropping funnel.

[0038] In a batching tank with a capacity of 300 liters, add 15 kg of butyl acrylate, 15 kg of EVA emulsion, 30 kg of isooctyl acrylate, 800 g of emulsifier, and 500 g of deionized water, stir and emulsify and heat up to 50 ° C, add 100 grams of ammonium pe...

Embodiment 2

[0040] Prepare the following materials:

[0041] The adhesive is 40 kg of butyl acrylate and 14 kg of EVA emulsion.

[0042] Plasticizer selects 40 kilograms of isooctyl acrylates, 20 kilograms of epoxidized triglycerides and 10 kilograms of vinyl acetate-acrylic acid esters combination,

[0043] Tackifier selects 18 kilograms of terpene phenolic resins for use,

[0044] The wetting agent is 8 kg of methyl methacrylate,

[0045] 2 kg of acrylic acid and 3 kg of methylol acrylamide are selected as the linked monomers,

[0046] emulsifier 800 g,

[0047] Initiator selects 400 grams of ammonium persulfate for use,

[0048] Preservative is selected 150 grams of organosilicon quaternary ammonium salts,

[0049] 500 grams of deionized water, a 300-liter batching tank, a mixer, a thermometer, and a dropping funnel.

[0050] Add 40kg of butyl acrylate, 10kg of EVA emulsion, 40kg of isooctyl acrylate, 800g of emulsifier, and 500g of deionized water into a 300-liter batching tank,...

Embodiment 3

[0052] Prepare the following materials:

[0053] The adhesive is 45 kg of butyl acrylate and 25 kg of EVA emulsion.

[0054] Plasticizer selects 70 kilograms of isooctyl acrylate and 10 kilograms of vinyl acetate-maleate for use,

[0055] Tackifier selects 35 kilograms of modified rosin,

[0056] The wetting agent is 12 kg of methyl methacrylate,

[0057] 2 kg of acrylic acid and 4 kg of methylol acrylamide are selected as the linked monomers,

[0058] emulsifier 800 g,

[0059] Initiator selects 400 grams of ammonium persulfate for use,

[0060] Preservative is selected 150 grams of organosilicon quaternary ammonium salts,

[0061] 500 grams of deionized water, a 300-liter batching tank, a mixer, a thermometer, and a dropping funnel.

[0062] Add 36 kilograms of butyl acrylate, 20 kilograms of EVA emulsion, 40 kilograms of isooctyl acrylate, 10 kilograms of vinyl acetate-maleate, 800 grams of emulsifier, and 500 grams of deionized water into a 300-liter batching tank, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength sealing glue for a paper packaging box, which comprises the following components in parts by mass: 30-40 parts of binder, 40-50 parts of plasticizer, 10-20 parts of tackifier, 6-9 parts of wetting agent, 4-5 parts of associated monomer, an appropriate amount of emulsifier, an appropriate amount of preservative, an appropriate amount of initiator and an appropriate amount of deionized water. The binder is formed by compounding butyl acrylate and an EVA (Ethylene-vinyl acetate) emulsion, and two monomers of ethylene and vinyl acetate are subjected to an emulsion polymerization reaction to form a calibration emulsion with the solid content of 50%, i.e., the EVA emulation; and the binder comprises the following components by mass ratio: 50-80 parts of butyl acrylate and 50-20 parts of EVA emulsion. The high-strength sealing glue provided by the invention has the advantages of large early adhesive force, high bonding strength, strong permeability, environmental friendliness, non-volatilization, non-toxicity, tastelessness and the like for a non-polar hard sticky material, at the same time, the production process is simple, the production cost is low, raw materials are easily purchased, no three wastes are generated, no burning danger is generated, the development direction of a high molecular polymer is closely linked, and the urgent needs of the market are met.

Description

technical field [0001] The invention relates to the field of organic adhesives, in particular to a high-strength sealing glue used for bonding multiple media in paper packaging boxes. Background technique [0002] With the rapid development of social economy and the rapid development of individualization and diversification of packaging and decoration materials, people's requirements for product packaging are also getting higher and higher. Exquisite and exquisite cartons emerge in endlessly, such as glazing, UV, and complex film. , Dumb film, etc. These decorative materials increase the beauty and applicability of the packaging box, and at the same time, the requirements for the sealing glue are also getting higher and higher. If the sealing glue is not handled well, it is very easy to have false sticking, which leads to the opening of the packaging box. Therefore, there is an urgent need for a sealing glue that can adapt to various packaging and decoration media to comple...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J151/00C09J11/06C09J11/08
Inventor 柴剑南袁洪良
Owner 蚌埠市比优特包装印务有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More