Preparation method of giant-dielectric-constant barium titanate ceramic

A technology of giant dielectric constant and barium titanate, applied in ceramics, inorganic insulators, etc., can solve the problems of low dielectric constant, complex preparation process, large dielectric loss, etc., and achieve short sintering time, simple process, dielectric The effect of low electrical loss

Inactive Publication Date: 2014-08-13
WUHAN UNIV OF TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The dielectric constant of the product obtained by this method is not high, and the dielectric loss is very large, the preparation process is relatively complicated, and the energy consumption is large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of giant-dielectric-constant barium titanate ceramic
  • Preparation method of giant-dielectric-constant barium titanate ceramic
  • Preparation method of giant-dielectric-constant barium titanate ceramic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The present embodiment provides a kind of preparation method of giant dielectric constant barium titanate ceramics, it comprises the following steps:

[0033] 1) Preparation of self-propagating system powder

[0034] ①Based on weight percentage, the system needs 109.55g of chromium trioxide powder, 38.92g of aluminum powder, 11.53g of carbon powder, and 40.00g of aluminum oxide powder to weigh the system. Powder, alumina powder and alumina grinding balls were put into the roller tank of the horizontal roller ball mill, the ratio of ball to material was 2:1, and the composite powder was obtained in the roller for 24 hours.

[0035] ②Place the composite powder in a vacuum oven at 60°C for 24 hours, pass through a 50-mesh sieve and granulate to obtain granular composite powder.

[0036] 2) Preparation of barium titanate blank

[0037] ①Under the pressure of 200MPa, barium titanate powder (particle size 2 microns, purity 99.7%) was pressed into a disc with a diameter of 1...

Embodiment 2

[0048] The present embodiment provides a kind of preparation method of giant dielectric constant barium titanate ceramics, it comprises the following steps:

[0049] 1) Preparation of self-propagating system powder

[0050] ①Based on percentage by weight, the system needs 110.35g of chromium trioxide powder, 40.15g of aluminum powder, 12.50g of carbon powder, and 37.00g of aluminum oxide powder to weigh the system. Powder, alumina powder and alumina grinding balls were put into the roller tank of the horizontal roller ball mill, the ratio of ball to material was 2:1, and the composite powder was obtained in the roller for 24 hours.

[0051] ②Place the composite powder in a vacuum oven at 60°C for 24 hours, pass through a 50-mesh sieve and granulate to obtain granular composite powder.

[0052] 2) Preparation of barium titanate blank

[0053] ①Under the pressure of 200MPa, barium titanate powder (particle size 2 microns, purity 99.7%) was pressed into a disc with a diameter o...

Embodiment 3

[0058] The present embodiment provides a kind of preparation method of giant dielectric constant barium titanate ceramics, it comprises the following steps:

[0059] 1) Preparation of self-propagating system powder

[0060] ① Calculated by weight percentage, the system needs 123.24g of chromium trioxide powder, 43.78g of aluminum powder, 12.94g of carbon powder, and 20.00g of aluminum oxide powder to weigh the system. Powder, alumina powder and alumina grinding balls were put into the roller tank of the horizontal roller ball mill, the ratio of ball to material was 2:1, and the composite powder was obtained in the roller for 24 hours.

[0061] ②Place the composite powder in a vacuum oven at 60°C for 24 hours, pass through a 50-mesh sieve and granulate to obtain granular composite powder.

[0062] 2) Preparation of barium titanate blank

[0063] ①Under the pressure of 200MPa, barium titanate powder (particle size 2 microns, purity 99.7%) was pressed into a disc with a diamete...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heightaaaaaaaaaa
diameteraaaaaaaaaa
purityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing barium titanate ceramics with a giant dielectric constant, and belongs to the technical field of ceramic materials. The giant dielectric constant barium titanate ceramic is sintered by self-propagating high-temperature rapid pressure technology, and the self-propagating high-temperature system adopts thermite system. The barium titanate powder is compacted with a pressure of 200 MPa and placed in a self-propagating system. After the self-propagating reaction is completed, an axial pressure of 100-200 MPa is applied to make the barium titanate ceramics dense. The barium titanate ceramic prepared by the invention has the advantages of high dielectric constant, low dielectric loss and high thermal stability. At the same time, the self-propagating high-temperature rapid pressurization technology consumes less energy, the process is simple, the required materials are cheap, and the sintering time is extremely short, so it has great value in industrial applications.

Description

technical field [0001] The invention relates to a dielectric ceramic material and a preparation method thereof, in particular to a preparation method of a giant dielectric constant barium titanate ceramic, which belongs to the technical field of ceramic materials. Background technique [0002] The molecular formula of barium titanate is BaTiO 3 , which is a tetragonal phase at room temperature, is a commonly used ferroelectric material with excellent dielectric, piezoelectric, and ferroelectric properties, and is widely used in electronic devices, such as for the preparation of multiple capacitors, PTC thermistors , Piezoelectric transducers, pyroelectric detectors, etc. With the advancement of science and technology, the miniaturization and miniaturization of various equipment has put forward higher requirements for material performance, and various high dielectric and giant dielectric constant materials have been developed one after another. The dielectric constant of ba...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information