Environment-friendly snow melting agent and preparation method thereof

A snow-melting agent and an environmentally friendly technology, applied in the field of environmentally friendly snow-melting agent and its preparation, can solve the problems of small amount of application, high price, and long snow-melting reaction time, and achieve simple production process, low destructiveness, and good snow-melting and ice-melting performance Effect

Active Publication Date: 2013-10-09
SHENYANG POLYTECHNIC UNIV
View PDF10 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Non-chlorine salt deicing agents include organic deicing agents such as acetates and urea. The main characteristics of this type of deicing agents are that they are expensive, rely on natural factors such as temperature and sunlight for snow melting, and have a long reaction time for snow melting.
At present, the environmentally friendly deicing agents recognized internationally are limited to acetate products, which have fewer types of raw materials, simple production technology, and environmental protection characteristics that are in line with my country's economic development policies. only a small amount of application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly snow melting agent and preparation method thereof
  • Environment-friendly snow melting agent and preparation method thereof
  • Environment-friendly snow melting agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] An environment-friendly deicing agent prepared by weight from the following raw materials: 30% calcium magnesium acetate, 15% potassium acetate, 20% calcium chloride, 25% magnesium chloride, 6.5% calcium oxide, and 3.5% corrosion inhibitor.

[0060] The corrosion inhibitor components are as follows by weight: 50% sodium hexametaphosphate, 25% sodium silicate, 10% zinc dihydrogen phosphate, 10% thiourea and 5% urea.

[0061] The preparation method of above-mentioned environment-friendly type deicing agent, the steps are as follows:

[0062] (1) Take the raw materials according to the above ratio, 30% calcium magnesium acetate, 15% potassium acetate, 20% calcium chloride, 25% magnesium chloride, 6.5% calcium oxide, 3.5% corrosion inhibitor, and grind them into powder with a ball mill ;

[0063] (2) Mix calcium magnesium acetate, potassium acetate, calcium chloride, magnesium chloride, and calcium oxide powder and then fully stir;

[0064] (3) After adding 3.5% slow-rele...

Embodiment 2

[0066] An environment-friendly deicing agent prepared by weight from the following raw materials: 35% calcium magnesium acetate, 15% potassium acetate, 20% calcium chloride, 20% magnesium chloride, 7.5% calcium oxide, and 2.5% corrosion inhibitor.

[0067] The corrosion inhibitor components are as follows by weight: 50% sodium hexametaphosphate, 25% sodium silicate, 10% zinc dihydrogen phosphate, 10% thiourea and 5% urea.

[0068] The preparation method of above-mentioned environment-friendly type deicing agent, the steps are as follows:

[0069] (1) Take the raw materials according to the above ratio, 35% of calcium magnesium acetate, 15% of potassium acetate, 20% of calcium chloride, 20% of magnesium chloride, 7.5% of calcium oxide, 2.5% of corrosion inhibitor, and grind them into powder with a ball mill ;

[0070] (2) Mix calcium magnesium acetate, potassium acetate, calcium chloride, magnesium chloride, and calcium oxide powder and then fully stir;

[0071] (3) After add...

Embodiment 3

[0073] An environment-friendly deicing agent prepared by weight from the following raw materials: 32% calcium magnesium acetate, 18% potassium acetate, 15% calcium chloride, 24% magnesium chloride, 8% calcium oxide and 3% corrosion inhibitor.

[0074] The corrosion inhibitor components are as follows by weight: 50% sodium hexametaphosphate, 25% sodium silicate, 10% zinc dihydrogen phosphate, 10% thiourea and 5% urea.

[0075] The preparation method of above-mentioned environment-friendly type deicing agent, the steps are as follows:

[0076] (1) Take the raw materials according to the above proportions, 32% of calcium magnesium acetate, 18% of potassium acetate, 15% of calcium chloride, 24% of magnesium chloride, 8% of calcium oxide, 3% of corrosion inhibitor, and grind them into powder with a ball mill ;

[0077] (2) Mix calcium magnesium acetate, potassium acetate, calcium chloride, magnesium chloride, and calcium oxide powder and then fully stir;

[0078] (3) After adding...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melting pointaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to an environment-friendly snow melting agent and a preparation method of the snow melting agent, and belongs to the field of the snow melting agents. The snow melting agent is prepared from acetates and chlorine salts with low corrosivity as the main raw materials by mixing acetates including potassium acetate, magnesium acetate and calcium acetate with calcium chloride and magnesium chloride in a certain proportion, as well as a small quantity of corrosion inhibitor. The common fault that a common inorganic snow melting agent is high in corrosivity is effectively overcome, the cost is reduced, and therefore the snow melting agent is suitable for promotion and application.

Description

technical field [0001] The invention relates to an environment-friendly deicing agent and a preparation method thereof, in particular to a preparation formula and a preparation process of the environment-friendly deicing agent. Background technique [0002] Ice and snow in winter have always brought serious hidden dangers to traffic safety, and traffic accidents caused by ice and snow roads have caused huge economic losses and casualties. At present, snow removal methods are mainly divided into mechanical snow removal and chemical snow removal. Among them, mechanical snow removal is flexible, fast, and has a wide range of applications, but there are deficiencies such as poor removal rate and easy damage to the road surface; the snow removal method of chemical deicing agent can make up for the shortage of mechanical snow removal, and is an effective means of melting snow and ice. Its use is irreplaceable. The type and application amount of deicing agent are generally deter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/18
Inventor 金生吉于贺刘子心张健李忠良
Owner SHENYANG POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap