Fluororesin heat dissipation coating and preparation method thereof

A technology of heat-dissipating coatings and fluororesins, applied in the direction of coatings, etc., can solve the problems of not meeting the development status and requirements of LED lamps, the decline of LED service life, and the aging of lamp housings, and achieve high adhesion, good heat dissipation, and excellent The effect of high and low temperature resistance

Inactive Publication Date: 2013-10-16
TIANCHANG CHICHENG ELECTRIC TECH
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the general LED lamp does not adopt special heat dissipation measures, and uses the natural heat dissipation of the lamp housing. This method causes the lamp housing to age after the LED lamp has been used for a period of time. Due to the long-term high temperature of the lamp housing, the service life of the LED is reduced; it cannot meet Development Status and Requirements of LED Lamps

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A fluororesin heat-dissipating coating is made of the following raw materials in parts by weight (kg):

[0015] Polytetrafluoroethylene 30, polyvinylidene fluoride 12, nonylphenol polyoxyethylene ether 3, xylene 120, ethyl acetate 30, zinc cyanurate 2, zinc oxide 4, alum powder 5, nano calcium carbonate powder 14, silicon Algal earth powder 8, antioxidant OD 2, silane coupling agent KH550 2, urotropine 1, aluminum nitride powder 12, film-forming agent 4,

[0016] Described film-forming agent is made from the raw material of following parts by weight (kg):

[0017] Composition of raw materials Vanadium boride 4, Crosslinker TAC2 , ditetradecyl alcohol ester 5, cyclohexanone peroxide 1, styrene 4, acrylonitrile 2, xylene 10, propylene glycol 13; the preparation method is: crosslinking agent TAC , ditetradecyl alcohol ester mixed, added to xylene, stirred for 10-20 minutes, added cyclohexanone peroxide, stirred and reacted for 30-40 minutes, added styrene, stirred and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a fluororesin heat dissipation coating and a preparation method thereof. The coating is characterized by comprising the following raw materials by weight parts: 30-35 parts of polytetrafluoroethylene, 12-15 parts of polyvinylidene fluoride, 2-3 parts of nonylphenol polyoxyethylene ether, 120-125 parts of xylene, 30-35 parts of ethyl acetate, 2-3 parts of cyanuric acid zinc, 3-4 parts of zinc oxide, 5-8 parts of alum powder, 12-14 parts of nano calcium carbonate powder, 8-10 parts of diatomite powder, 1-2 parts of an antioxidant OD, 2-3 parts of a silane coupling agent KH 550, 1-2 parts of urotropine, 10-12 parts of aluminium nitride powder and 4-5 parts of a film forming agent. According to the invention, the fluororesin is used as a base material; the coating is excellent in high and low temperature resistance, dielectric property, chemical stability, weatherability, incombustibility and inviscosity.

Description

technical field [0001] The invention belongs to the technical field of paints, and relates to a heat-dissipating paint, more specifically, a fluororesin heat-dissipating paint and a preparation method thereof. Background technique [0002] With the rapid expansion of the use of LED lamps, prolonging the service life of LED lamps has become an urgent problem to be solved. At present, the general LED lamp does not adopt special heat dissipation measures, and uses the natural heat dissipation of the lamp housing. This method causes the lamp housing to age after the LED lamp has been used for a period of time. Due to the long-term high temperature of the lamp housing, the service life of the LED is reduced; it cannot meet The development status and requirements of LED lamps. Contents of the invention [0003] The object of the present invention is to provide a fluororesin heat-dissipating coating and its preparation method. The coating of the present invention has the advanta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/18C09D127/16C09D125/12C09D7/12C08F212/08C08F220/44
Inventor 钱程
Owner TIANCHANG CHICHENG ELECTRIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap