Metal anti-rust phosphating solution

A technology of metal anti-rust and phosphating solution, which is applied in the direction of metal material coating process, etc., can solve the problems of toxic and irritating odor, difficulty in getting rid of chemical rust removal hazards, etc., achieve good corrosion resistance, wide range of process parameters, increase The effect of corrosion resistance

Inactive Publication Date: 2013-11-20
石欣
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the phosphating treatment agents currently used are generally highly corrosive, and it is difficult to get rid of the harm caused by chemical rust removal during use and storage, such as the production of toxic and pungent odors, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Take hydroxyethyl cellulose and gelatin, add warm water at 50°C to dissolve completely, and set aside; take octylphenol polyoxyethylene ether, sodium lauryl polyoxyethylene ether sulfate and 1.3-diethylthiourea, add 50°C Dissolve in warm water, then add phosphoric acid and citric acid, after dissolving, add nickel sulfate, ferric sulfate, zinc dihydrogen phosphate, ferrocene, sodium perborate, stir for 1 hour, set aside; take aluminum hydroxide and graphite, add water to dissolve Finally, set aside; Combine the above solutions, add an appropriate amount of water, and stir evenly to make the raw material content meet the requirements of octylphenol polyoxyethylene ether 2g / L; sodium lauryl polyoxyethylene ether sulfate 2g / L; 1.3-diethyl Thiourea 2g / L; phosphoric acid 10g / L; citric acid 5g / L; nickel sulfate (NiSO 4 ·6H 2 O) 15 g / L; iron sulfate 10 g / L; zinc dihydrogen phosphate 10 g / L; ferrocene 5 g / L; sodium perborate 5.0 g / L; hydroxyethyl cellulose 2 g / L; gelatin 5 g / ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a metal anti-rust phosphating solution, comprising the following raw materials by concentration: 2 g / L of octylphenol polyoxyethylene ether, 2 g / L of sodium polyoxyethylenelauryl ether sulfate, 2 g / L of diethyl thiourea, 10 g / L of phosphoric acid, 5 g / L of citric acid, 15 g / L of nickel sulfate (NiSO4.6H2O), 10 g / L of ferric sulfate, 10 g / L of zinc dihydrogen phosphate, 5 g / L of ferrocene, 5.0 g / L of sodium perborate, 2 g / L of hydroxyethyl cellulose, 5 g / L of gelatin, 40 g / L of aluminium hydroxide and 5 g / L of graphite. Harmful substances such as nitrate, nitrite, chromate and the like are not adopted, so that the metal anti-rust phosphating solution is environment-friendly. Meanwhile, an anti-rust object of the metal surface can be achieved; and a phosphating film formed by the phosphating solution has good corrosion resistance, thereby completely reaching relevant standards.

Description

technical field [0001] The invention relates to a metal antirust phosphating solution, which belongs to the technical field of metal surface treatment agents. Background technique [0002] Metal anti-rust phosphating solution is a phosphating treatment agent for anti-rust purpose. After smearing and drying on the metal surface, a phosphating film can be formed to prevent the metal from rusting. At the same time, the adhesion of the metal coating film can be improved after phosphating treatment . However, the phosphating treatment agents currently used are generally highly corrosive, and it is difficult to get rid of the harm caused by chemical rust removal during use and storage, such as the production of toxic and pungent odors. Along with the raising of people's environmental protection requirement, invent a kind of non-polluting, non-hazardous metal antirust agent and become an urgent problem to be solved. Contents of the invention [0003] In order to solve the abov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/05C23F11/16
Inventor 石欣
Owner 石欣
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com