Fluorosiloxane-POSS acrylate block copolymers, blood-compatible coating thereof and preparation method of the fluorosiloxane-POSS acrylate block copolymers

A technology of block copolymer and acrylate, which is applied in medical containers, transportation and packaging, anticoagulation treatment, etc., can solve the problems of reducing platelet aggregation and activation, and achieves easy industrialization, large-scale production, and high practical value , good hydrophobic effect

Active Publication Date: 2014-07-30
UNIV OF JINAN
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polyfluoroalkylmethylsiloxane (PFMS) macromolecules, PFPMS and PDMS are similar in structure and performance, but the introduction of fluorine-containing groups makes it have better biocompatibility and biostability, which can reduce platelet Aggregation and activation (Su T., Wang G. Y., European Polymer Journal. 2010, 46: 472-483), about fluorosilicone block copolymers with PFPMS as soft segment and acrylate functional monomer and POSS copolymer as hard segment and surface blood compatibility studies have not been reported in the literature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluorosiloxane-POSS acrylate block copolymers, blood-compatible coating thereof and preparation method of the fluorosiloxane-POSS acrylate block copolymers
  • Fluorosiloxane-POSS acrylate block copolymers, blood-compatible coating thereof and preparation method of the fluorosiloxane-POSS acrylate block copolymers
  • Fluorosiloxane-POSS acrylate block copolymers, blood-compatible coating thereof and preparation method of the fluorosiloxane-POSS acrylate block copolymers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) Preparation of hydroxyl-terminated POSS acrylate copolymer

[0032] Add 10 g methyl methacrylate, 5 g butyl acrylate, 0.9 g 4-acryloyloxybutyl-heptaisobutyl POSS, 0.075 g mercaptoethanol, 0.08 azobisisobutyronitrile and 16 g acetic acid to the reaction flask Butyl ester, after stirring and mixing evenly, raise the temperature to 60~110°C to react for 5 hours, cool down to room temperature, discharge, and dry to obtain the hydroxyl-terminated POSS acrylate copolymer with a number average molecular weight of 10,000.

[0033] (2) Preparation and properties of fluorosilicone-POSS acrylate block copolymer and its blood-compatible coating:

[0034] At room temperature 25°C, add 10g of hydroxyl-terminated POSS-acrylate copolymer prepared above, 10g of single-ended hydrogen polymethyltrifluoropropylsiloxane and 0.005g of Karstedt platinum catalyst into 180g of butyl acetate, and mix well , to generate a polymer solution with a mass concentration of 10%. The prepared polym...

Embodiment 2

[0036] (1) Preparation of hydroxyl-terminated POSS acrylate copolymer

[0037]Add 10g methyl methacrylate, 13g butyl acrylate, 3g 4-methacryloxybutyl-heptaisobutyl POSS, 0.75g mercaptoethanol, 0.12g azobisisobutyronitrile in the reaction flask and 40g of butyl acetate, stir and mix evenly, raise the temperature to 60-110°C for 5 hours, cool down to room temperature, discharge, and dry to obtain a hydroxyl-terminated POSS acrylate copolymer with a number average molecular weight of 1000.

[0038] (2) Preparation and performance of fluorosilicone-POSS acrylate block copolymer hemocompatible coating:

[0039] At room temperature at 25°C, add 20g of hydroxyl-terminated POSS-acrylate copolymer prepared above, 10g of double-terminated hydrogen polymethyltrifluoropropylsiloxane and 0.01g of Karstedt platinum catalyst to 135g of ethyl acetate and mix well , to generate a polymer solution with a mass concentration of 20%. The prepared polymer solution is coated on a dry and clean pol...

Embodiment 3

[0041] (1) Preparation of hydroxyl-terminated POSS acrylate copolymer

[0042] Add 10 g methyl methacrylate, 5 g butyl acrylate, 0.9 g 4-acryloxybutyl-heptaisobutyl POSS, 0.038 g mercaptoethanol, 0.07 azobisisobutyronitrile and 16 g acetic acid to the reaction flask Butyl ester, after stirring and mixing evenly, raised the temperature to 60°C to react for 8 hours, cooled to room temperature, discharged, and dried to obtain a hydroxyl-terminated POSS acrylate copolymer with a number average molecular weight of 20,000.

[0043] (2) Preparation and performance of fluorosilicone-POSS acrylate block copolymer hemocompatible coating:

[0044] At room temperature at 25°C, add 10g of hydroxyl-terminated POSS-acrylate copolymer prepared above, 20g of double-terminated hydrogen polymethyltrifluoropropylsiloxane and 0.01g of Karstedt platinum catalyst into 150g of ethyl acetate, and mix well , to generate a polymer solution with a mass concentration of 20%. The prepared polymer solutio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
contact angleaaaaaaaaaa
contact angleaaaaaaaaaa
Login to View More

Abstract

The invention relates to a fluorosiloxane-POSS acrylate block copolymer, a hemocompatible coating and a preparation method thereof, belonging to the field of fluorosilicone copolymer preparation and biomedical polymers. The hemocompatible coating made of the fluorosiloxane-POSS acrylate block copolymer has good hydrophobicity, and the water static contact angle is greater than 107°. Compared with the polyvinyl chloride surface, the anticoagulant time was significantly increased; the adhesion and aggregation state of adhered platelets were observed under a scanning electron microscope. Compared with the blank PVC surface, after spraying the surface, the adherent platelets on the surface are significantly reduced by more than 85%, and the adherent platelets are basically not deformed, and the blood compatibility is good. The preparation process of the coating is simple, the raw materials are easy to obtain, easy for industrialization and large-scale production, and has high practical value. Fluorosiloxane-POSS acrylate block copolymer, as shown in formula 1 and formula 2, formula 1 and formula 2.

Description

technical field [0001] The invention relates to a fluorosiloxane-POSS acrylate block copolymer, a hemocompatible coating and a preparation method thereof, and belongs to the field of fluorosilicone copolymer preparation and biomedical polymers. Background technique [0002] Human beings have always been attacked by cardiovascular diseases, and the necessary blood-compatible biomaterials have always been a major issue in medicine that needs to be solved urgently. At present, there are many types and large quantities of artificial blood vessels or medical device materials that are in contact with human tissues and blood for a long time in clinical practice, but they still cannot meet the requirements, and the problem of blood compatibility still exists, which has become a limit for biological materials in contact with blood. One of the key problems in the application in the environment, there is an urgent need to develop a biomaterial with excellent comprehensive properties. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G81/02C08F220/14C08F220/18C08F230/08A61L33/06
Inventor 李辉袁晓燕张书香褚国红赵蕴慧张炉青
Owner UNIV OF JINAN