White carbon black high-activity dispersing agent composition and preparation method thereof

A high-activity, dispersant technology, applied in the field of silica high-activity dispersant composition and its preparation, can solve the problem of small dispersing function of silica, and achieve the effect of easy operation and simple process

Active Publication Date: 2014-01-22
朝阳好优达橡塑助剂有限公司
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, white smoke dispersant-450 is a mixture of high-boiling alcohol and amine, which has a certain inhibitory effect on the adsorption of amine accelerators and anti-aging agents by whi...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • White carbon black high-activity dispersing agent composition and preparation method thereof
  • White carbon black high-activity dispersing agent composition and preparation method thereof
  • White carbon black high-activity dispersing agent composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] Weigh raw materials by weight:

[0061] Acetyl phenylhydrazine 76 kg;

[0062] Lauric acid 60 kg;

[0063] Cetyltrimethylammonium chloride 18 kg;

[0064] Stearyl alcohol 8 kg;

[0065] Monoglyceride 16 kg;

[0066] Diethylene glycol 6 kg;

[0067] C9 petroleum resin 16 kg.

[0068] First put 60 kg of lauric acid, 18 kg of cetyltrimethylammonium chloride, 8 kg of stearyl alcohol, 16 kg of monoglyceride, 6 kg of diethylene glycol, and 16 kg of C9 petroleum resin into the pressure of -0.09Mpa In the negative pressure reaction kettle, the reaction kettle is heated up. When the temperature rises to 160 ° C, 76 kg of acetylphenylhydrazine is added to the reaction kettle through the feeder. After the reaction is completed, the white carbon black high-activity dispersant combination can be obtained. For the product, discharge the white carbon black high-activity dispersant composition in the reaction kettle into the storage tank of the condensation granulator, and make i...

Embodiment 2

[0070] Weigh raw materials by weight:

[0071] Benzohydrazide 62 kg;

[0072] Benzenesulfonyl hydrazide 16 kg;

[0073] 54 kg of oleic acid;

[0074] Palmitic acid 40 kg;

[0075] Cetyltrimethylammonium chloride 10 kg;

[0076] Diethylene glycol 6 kg;

[0077] Monoglyceride 12 kg;

[0078] Stearyl alcohol 6 kg;

[0079] C9 petroleum resin 14 kg.

[0080] First put 54 kg of oleic acid, 40 kg of palmitic acid, 10 kg of cetyltrimethylammonium chloride, 6 kg of diethylene glycol, 12 kg of monoglyceride, 6 kg of stearyl alcohol, and 14 kg of C9 petroleum resin into the In a negative pressure reactor with a pressure of -0.09Mpa, the temperature of the reactor is raised. When the temperature rises to 180°C, 62 kg of benzohydrazide and 16 kg of benzenesulfonylhydrazide are added to the reactor through a feeder. After the reaction is completed, , the white carbon black high-activity dispersant composition can be obtained, and the white carbon black high-activity dispersant comp...

Embodiment 3

[0082] Weigh raw materials by weight:

[0083] Acetyl phenylhydrazine 38 kg;

[0084] Lauric acid 30 kg;

[0085] Monoglyceride 8 kg;

[0086] Cetyltrimethylammonium chloride 9 kg;

[0087] Stearyl alcohol 4 kg;

[0088] C9 petroleum resin 8 kg;

[0089] Diethylene glycol 3 kg.

[0090] First put 30 kg of lauric acid, 8 kg of monoglyceride, 9 kg of cetyltrimethylammonium chloride, 4 kg of stearyl alcohol, 8 kg of C9 resin, and 3 kg of diethylene glycol into the pressure of -0.09Mpa In the negative pressure reaction kettle, the temperature of the reaction kettle is raised. When the temperature rises to 170°C, 38 kg of acetylphenylhydrazine is added to the reaction kettle through the feeder. After the reaction is completed, the white carbon black high-activity dispersant composition can be obtained. , discharge the white carbon black high activity dispersant composition in the reaction kettle into the storage tank of the condensation granulator, and make it into granules o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a white carbon black high-activity dispersing agent composition. The preparation method comprises the following steps: weighing the following materials in percentages by weight: 20%-60% of at least one of hydrazide and sulfohydrazide, 25%-50% of long-chain fatty acid, 1%-15% of octadecanol, 1%-15% of diethylene glycol, 1%-15% of monoglyceride, 1%-20% of hexadecyl trimethyl ammonium chloride and 1%-20% of C9 resin; putting the long-chain fatty acid, octadecanol, diethylene glycol, monoglyceride, hexadecyl trimethyl ammonium chloride and the C9 resin into a negative-pressure reaction kettle; increasing the temperature; adding at least one of hydrazide and sulfohydrazide into the reaction kettle, thus obtaining the white carbon black high-activity dispersing agent composition after the reaction is finished. The preparation method is simple in technology and easy to operate; in a formula of rubber filled with white carbon black, the added composition is capable of increasing the activity of the white carbon back and improving the dispersing effect of the white carbon back in the rubber, and then enhancing the physical mechanical property of vulcanized rubber.

Description

technical field [0001] The invention relates to a white carbon black high-activity dispersant composition and a preparation method thereof. Background technique [0002] Silica is an inorganic powder material. Due to its fine particles and large specific surface area, its application in rubber tires can improve the physical and mechanical properties of tires such as puncture resistance, and can also greatly reduce tire heat generation and rolling resistance. Tire manufacturers Green tires with 10% fuel saving have been manufactured with white carbon black. The range of raw materials for white carbon black production is very wide, mainly inorganic silicate ore, straw, and coal gangue, and the raw materials for carbon black production are mainly non-renewable resource petroleum. Therefore, the production of tires produced by carbon black replaced by white carbon black will be The trend of the times not only saves oil resources and reduces costs, but also purifies the urban ai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08K13/02C08K5/25C08K5/43C08K5/09C08K5/19C08K3/36C08L7/00C08L9/06
Inventor 戴近禹
Owner 朝阳好优达橡塑助剂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap