Iron phosphate-wrapped photocatalytic nano titanium dioxide powder and application thereof
A nano-titanium dioxide, titanium dioxide technology, applied in physical/chemical process catalysts, chemical instruments and methods, chemical/physical processes and other directions, can solve problems such as large limitations, and achieve the effects of easy mixing, wide application and convenient use
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0039] Example 1: Pour 100g of titanium dioxide (P25-a highly dispersed titanium dioxide produced by the AEROSIL200 process with an average particle size of 21nm) into 200mL of water and add Na 2 CO 3 Control the pH to 8.0, and add 2g of polyvinylpyrrolidone (PVP-from China National Pharmaceutical), and fully shake and disperse.
[0040] Dissolve 200 g of ferric nitrate tetrahydrate and 400 g of ammonium dihydrogen phosphate in 500 mL of distilled water, stir well, add 5 g of polyvinylpyrrolidone (PVP), and shake ultrasonically; then add the resulting titanium dioxide solution to mix, and adjust the pH to 8.0 with lye. Stir and heat to obtain gel; after drying and grinding, the gel is pyrolyzed at 400°C for 2h and then calcined at 500°C under the protection of nitrogen atmosphere.
[0041] The liquid acetaldehyde method was used as the degradation marker to determine the photocatalytic degradation of small-molecule pollutants by the photocatalytic nano-titanium dioxide powder coated...
Example Embodiment
[0045] Example 2: By implementing the same procedure as in Example 1, except that sodium hexametaphosphate (China National Medicines) was used as an anionic surfactant, all other conditions were kept the same to obtain a light yellow powder for photocatalysis. The resulting photocatalytic powder can completely degrade acetaldehyde in 2 hours, and the methyl orange becomes colorless at the same time.
[0046] It is mixed and extruded with the plastic component polyethylene terephthalate resin to obtain a strip containing 30% of the photocatalytic powder, which is irradiated with an ultraviolet lamp, and the resin will not change color or age for a day. It is used in the coating system water-soluble aldol resin solution (produced by Dow Company) to make a coating system containing 30% photocatalytic powder. It is irradiated with a 246nm ultraviolet lamp, and the resin will not change color or age after a day.
Example Embodiment
[0047] Example 3: By implementing the same procedure as in Example 1, except that 15nm titanium dioxide (provided by Fuzhou University) particles were used, and all other conditions were kept the same, the photocatalytic powder was obtained. The obtained photocatalytic powder is used to degrade acetaldehyde or methyl orange. The measurement results show that the synthesized photocatalytic powder can completely degrade acetaldehyde in 2 hours, and the methyl orange becomes colorless at the same time.
[0048] It is mixed and extruded with the plastic component polyethylene terephthalate resin to obtain a strip containing 30% of photocatalytic powder, which is irradiated with a 246nm ultraviolet lamp, and the resin changes color and ages within a day. It is used in the coating system water-soluble aldol resin solution (produced by Dow Company) to make a coating system containing 30% photocatalytic powder. It is irradiated with a 246nm UV lamp, and the resin will not change color or ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap