Water-based cleaning agent for aluminum alloy part

A technology for aluminum alloy parts and cleaning agents, applied in the field of cleaning agents, can solve problems such as easy corrosion of aluminum alloy parts, difficulty in subsequent waste liquid treatment, poor surface quality, etc., achieve good surface quality, improve processing environment and sanitary conditions , The effect of low cleaning cost

Active Publication Date: 2014-02-19
苏州安美润滑科技有限公司
View PDF2 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These two methods have the disadvantages of residue after drying, easy corrosion of aluminum alloy parts, poor surface quality, unsafe and environmental protection, and difficulty in subsequent waste liquid treatment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The water-based cleaning agent for aluminum alloy parts of this embodiment includes the following components by weight percentage: 6% alcohol ether carboxylate, 6% polycarboxylate, 12% alcohol ether surfactant, 7.5% oleamide, 1.75% diethanolamine, 1.75% triethanolamine, 1.2% benzoate, 0.8% polyglycolic acid 1.2% carbonate, 1.5% borax, 0.5% sodium hydroxide, 6% alcohol, the rest is deionized water Add to 100%.

[0016] In this embodiment, the polycarboxylate is disodium edetate. In this embodiment, the disodium edetate is replaced by tetrasodium edetate, lemon One of sodium oxyacetate and sodium glycolate; or a mixture of disodium edetate, tetrasodium edetate, sodium citrate, and sodium hydroxyacetate in the same weight percentage, all of which are qualified cleaning agents , there was no significant difference in the properties of the obtained products.

[0017] In this embodiment, the alcohol ether surfactant is fatty alcohol polyoxyethylene ether; in this embodiment...

Embodiment 2

[0023] The water-based cleaning agent for aluminum alloy parts of the present embodiment comprises the following components by weight percentage: 2% alcohol ether carboxylate, 2% polycarboxylate, 5% alcohol ether surfactant, 5% oleamide, 1% diethanolamine, 1% triethanolamine, 0.5% benzoate, 2.1% polyglycolic acid salt, 1.5% carbonate, 0.5% borax, 0.3% sodium hydroxide, 2% alcohol, the rest is deionized Water was added to 100%.

[0024] In this embodiment, the polycarboxylate is tetrasodium edetate. In this embodiment, the tetrasodium edetate is replaced by disodium edetate, lemon One of sodium oxyacetate and sodium glycolate; or a mixture of tetrasodium edetate and disodium edetate, sodium citrate, and sodium hydroxyacetate in the same weight percentage, all of which are qualified cleaning agents , there was no significant difference in the properties of the obtained products.

[0025] In this embodiment, the alcohol ether surfactant is alkylphenol polyoxyethylene ether; in ...

Embodiment 3

[0031] The water-based cleaning agent for aluminum alloy parts of the present embodiment comprises the following components by weight percentage: 10% alcohol ether carboxylate, 10% polycarboxylate, 20% alcohol ether surfactant, 10% oleamide, 2.5% diethanolamine, 2.5% triethanolamine, 2% benzoate, 2.5% polyglycolic acid salt, 0.8% carbonate, 0.5% borax, 0.2% sodium hydroxide, 10% alcohol, the rest is deionized Water was added to 100%.

[0032] In this embodiment, the polycarboxylate is sodium citrate. In this embodiment, the sodium citrate is replaced by tetrasodium edetate, disodium edetate, hydroxyl One of sodium acetate; or replace it with a mixture of sodium citrate, tetrasodium edetate, disodium ethylenediaminetetraacetate, and sodium glycolate according to the same weight percentage to obtain a qualified cleaning agent. No significant difference.

[0033] In this embodiment, the alcohol ether surfactant is sorbitol monooleate; in this embodiment, sorbitol monooleate is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based cleaning agent for an aluminum alloy part. The cleaning agent comprises components in percentage by weight as follows: 2%-10% of AEC (alcohol ether carboxylate), 2%-10% of poly-carboxylate, 5%-20% of an alcohol ether surfactant, 5%-10% of oleamide, 1%-2.5% of diethanol amine, 1%-2.5% of triethanolamine, 0.5%-2% of benzoate, 0.5%-4% of hydroxyacetic acid salt, 1.5%-4% of carbonate, 0.5%-3% of borax, 0.1%-0.6% of sodium hydroxide, 2%-10% of alcohol and the balance of deionized water. The water-based cleaning agent can guarantee the machining precision of an aluminum alloy and is environment-friendly, fast, safe, non-ignitable, non-explosive, simple to operate, low in cost, non-toxic, free from harm to a human body, convenient and safe to use and energy-saving, the cleaning speed is high, the surface quality is good, and a cleaned aluminum alloy can be electroplated later.

Description

technical field [0001] The invention relates to a cleaning agent, in particular to a water-based cleaning agent for aluminum alloy parts. Background technique [0002] At present, cleaning agents for aluminum alloys at home and abroad generally use solvent cleaning, strong acid and strong alkali cleaning, etc. Solvent cleaning mainly utilizes solvent-based cleaning agents for steam cleaning or immersion cleaning with appropriate equipment. Since solvent-based cleaning agents are not only expensive and have the disadvantages of being flammable and damaging to the skin, but also environmental pollutants, high-cost methods and special devices are required to prevent steam leakage and to recover and dispose of used solvents. Strong acid and strong alkali cleaning is to use the strong chemical action of strong acid (such as concentrated acetic acid, concentrated nitric acid, concentrated phosphoric acid) or strong alkali (such as potassium hydroxide, sodium hydroxide, etc.) to r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23G1/22
Inventor 袁清和汪小龙
Owner 苏州安美润滑科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com