Environment-friendly lightweight calcium carbide slag aerated brick and manufacturing method thereof

A technology of slag aerated bricks and calcium carbide slag, which is applied in the field of aerated bricks, can solve the problems of being unable to meet diversified markets and slow development of aerated bricks, and achieve the effect of turning waste into treasure, circular economy, good sound absorption effect, and reduced pollution effect

Inactive Publication Date: 2014-06-04
ANHUI SHENGREN NEW BUILDING MATERIAL
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the production technology of aerated bricks in my country is not mature enough, which makes the development of aerated bricks technology slow and cannot meet the needs of diversified markets.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The environmentally friendly lightweight carbide slag aerated brick is characterized in that it is made of the following raw materials in parts by weight: carbide slag 25, cement 4, catechol 1, ferrosilicon alloy 0.35, p-aminobenzenesulfonic acid 0.3, Paclitaxel waste residue 0.5, diatomaceous earth 15, fly ash 9, glass fiber 2, sodium chloride 1, coconut oil 3, construction waste recycled powder (including construction waste recycled concrete powder and / or construction waste recycled brick powder) 14, Polyacrylamide 0.49, calcium bicarbonate 0.02, sweet-scented osmanthus 0.02, centipede 0.08, auxiliary agent 4, appropriate amount of water; the auxiliary agent is made of the following raw materials in parts by weight: polyvinylidene fluoride 3.1, silicon carbide powder 2, titanium White powder 5, silica sol 0.36, redispersible latex powder 0.6, citronella oil 3, borneol 1, superfine wax powder 0.9, grapevine 4, the preparation method is to pulverize and mix the materials...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly lightweight calcium carbide slag aerated brick which is characterized by being prepared by the following raw materials by weight: 24-26 parts of calcium carbide slag, 4-7 parts of cement, 1-3 parts of catechol, 0.3-0.5 part of ferrosilicon alloy, 0.3-0.6 part of sulfanilic acid, 0.5-1 part of paclitaxel waste residues, 15-19 parts of diatomite, 9-11 parts of fly ash, 2-4 parts of glass fibers, 1-4 parts of sodium chloride, 3-6 parts of coconut oil, 11-14 parts of building waste regenerated powder (including building waste regenerated concrete powder and / or building waste regenerated brick powder), 0.4-0.9 part of polyacrylamide, 0.02-0.05 part of calcium bicarbonate, 0.02-0.05 part of sweet osmanthus, 0.04-0.08 part of radix stemonae, 4-6 parts of auxiliary agents, and a proper amount of water. The aerated brick processed in the invention has the characteristics of high finished product qualified rate, high compressive strength, low unit weight, high thermal insulation performance, and good sound-absorbing effect, and can be used as non-bearing walls or bearing walls.

Description

technical field [0001] The invention relates to the technical field of aerated bricks, in particular to an environment-friendly lightweight calcium carbide slag aerated brick and a manufacturing method thereof. Background technique [0002] In recent years, with the acceleration of the industrialization process and the improvement of the level of urbanization, various environmental pressures and problems have also been brought about. Various solid wastes generated in the industrial production process and solid wastes caused by urban construction demolition and reconstruction have been troubled. In order to meet the living environment of residents, the present invention adds solid waste as a raw material to the aerated bricks, realizes waste recycling, reduces environmental pollution, and meets the strategic requirements of sustainable development. [0003] Aerated bricks are aerated concrete blocks produced by high-temperature autoclaved equipment. The aerated concrete blo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00
Inventor 任劲松
Owner ANHUI SHENGREN NEW BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com