High temperature resistant acid-resisting anticorrosive primer
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An anti-corrosion primer and high temperature resistant technology, applied in the field of paint, can solve the problems of not meeting consumers' requirements for paint use, not being environmentally friendly, easy to corrode, etc., and achieve the effect of fast drying, strong wear resistance and strong adhesion
Inactive Publication Date: 2014-06-25
ANHUI PUYUAN SEPARATION MACHINERY MFG CO LTD
View PDF3 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] Paint can be seen everywhere in daily life. It mainly plays the role of protection and decoration. According to different use environments, there are various types of paint. Traditional paints generally have heavy odor, easy to fall off, easy to corrode, and not environmentally friendly, etc. The problem is that it can no longer meet the requirements of consumers for the use of paint. Therefore, it is necessary to improve the formula of the original paint, increase the practicability and durability of the paint, reduce its harm to the environment and human body, and make it adaptable to various use environments. condition
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0012] The paint of this embodiment is made of the following raw materials in parts by weight: E-12 epoxy resin 14, silicone resin 24, amino resin 12, mica powder 5, polyhexamethylene guanidine hydrochloride 2, epoxy acrylate 30, hydroxyethyl Phosphate methacrylate 3, isobornyl acrylate 8, triethanolamine 2, p-tert-amylphenol 4, methyl acrylate 4, crosslinking agent TAIC2, isoamyl butyrate 10, nano diatomite powder 28 , linseed oil alkyd resin 9, antioxidant NBC2, isocyanate 3, zinc naphthenate 3, additives 6, xylene 12, butyl acetate 12.
[0013] The auxiliary agent is made of the following raw materials in parts by weight: loess 2, polytetrafluoroethylene powder 5, accelerator DM2, silane coupling agent KH5504, sodium laurate 2, jade 2, salicylic acid 3, phthalate Formate 40, propyl gallate 4, coix seed oil 3, vanadium diboride 2, epicatechin 3; the preparation method is to send loess and jade into a calciner for 3 hours at 720-740°C, and then Take it out, soak in 15% hydro...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to an oil paint, and particularly relates to a high temperature resistant acid-resisting anticorrosive primer. The primer is prepared from following raw materials in parts by weight: 12-14 parts of E-12 epoxy resin, 20-24 parts of organic silicon resin, 10-12 parts of amino resin, 3-5 parts of mica powder, 1-2 parts of poly hexamethylene guanidinium hydrochloride, 25-30 parts of epoxy acrylate, 2-3 parts of ethoxyl methacrylate phosphate, 5-8 parts of isobornyl acrylate, 1-2 parts of triethanolamine, 3-4 parts of 4-tert-amylphenol, 3-4 parts of acrylic acid methyl ester, 1-2 parts of cross-linking agent TAIC, 8-10 parts of isoamyl butyrate, 24-28 parts of nanometer diatomite powder, 7-9 parts of linseed oil alkyd resin, 1-2 parts of antiager NBC, 2-3 parts of isocyanate, 2-3 parts of zinc naphthenate, 5-6 parts of additive, 10-12 parts of xylene, and 10-12 parts of butyl acetate. The primer has strong adhesive force, can form bright film, is dried rapidly, can bear high temperature damage, resists acid and corrosion, has long service life, and has excellent comprehensive performance.
Description
technical field [0001] The invention relates to a paint, in particular to a high-temperature-resistant, acid-resistant and anti-corrosion primer and a preparation process thereof. Background technique [0002] Paint can be seen everywhere in daily life. It mainly plays the role of protection and decoration. According to different use environments, there are various types of paint. Traditional paints generally have heavy odor, easy to fall off, easy to corrode, and not environmentally friendly, etc. The problem is that it can no longer meet the requirements of consumers for the use of paint. Therefore, it is necessary to improve the formula of the original paint, increase the practicability and durability of the paint, reduce its harm to the environment and human body, and make it adaptable to various use environments. condition. Contents of the invention [0003] The object of the present invention is to provide a kind of high temperature and acid resistant anticorrosion ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.