Formula of wood-plastic bathroom plate and production method

A bathroom and wood-plastic technology, which is applied to the formulation and preparation of wood-plastic materials, can solve the problems of cumbersome processes of additives, and achieve the effects of wide source of raw materials, good antibacterial properties and simple production process.

Active Publication Date: 2014-08-20
山东宜居新材料科技有限公司
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation of this additive also requires a more cumbersome process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Formula of wood-plastic bathroom plate and production method
  • Formula of wood-plastic bathroom plate and production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] The preparation of nano silver ion modified carbon black antibacterial agent adopts the following method:

[0071] 1) A 2M aqueous solution of soluble silver salt is reacted with ammonia to form an alkaline aqueous solution of silver ammonia complex; wherein the molar ratio of the aqueous solution of soluble silver salt to ammonia is 1:10;

[0072] 2) Add carbon black to hydrogen peroxide solution, mix well and let it stand for 60 minutes, add it to the alkaline aqueous solution of silver ammonia complex prepared in step 1), carry out the reduction reaction, separate the precipitate and wash after the end, the brown-black solid is the nanometer Silver particles modified carbon nanotubes; the mass of carbon black is 0.5 times the mass of the silver ions; the molar amount of hydrogen peroxide is 2 times the molar mass of the silver ions.

Embodiment 2

[0074] Weigh each raw material according to the following parts by weight, wherein the silver ion modified carbon black antibacterial agent adopts the antibacterial agent prepared in Example 1:

[0075] PVC resin powder: 30 parts;

[0076] Calcium filler: 5 parts;

[0077] Silver ion antibacterial agent: 1 part;

[0078] The bottom layer is made of the following raw materials in parts by weight:

[0079] PVC resin powder: 70 parts;

[0080] Wood fiber powder: 30 parts;

[0081] Calcium filler: 35 parts;

[0082] Plasticizing regulator: 10 parts;

[0083] Stabilizer: 6 parts;

[0084] Internal and external lubricants: 2.0 parts;

[0085] ACR processing aid: 7 parts;

[0086] Foaming agent: 2 parts.

[0087] The present invention also provides a preparation method of the above-mentioned wood-plastic bathroom board, which includes the following steps:

[0088] 1) Bottom material: mix the calcium filler, wood fiber powder, plasticizing regulator, stabilizer, internal and external lubricant, ACR proc...

Embodiment 3

[0094] Weigh the raw materials according to the following parts by weight:

[0095] PVC resin powder: 20 parts;

[0096] Calcium filler: 25 parts;

[0097] Silver ion antibacterial agent: 1 part;

[0098] The bottom layer is made of the following raw materials in parts by weight:

[0099] PVC resin powder: 80 parts;

[0100] Wood fiber powder: 30 parts;

[0101] Calcium filler: 25 parts;

[0102] Plasticizing regulator: 8 parts;

[0103] Stabilizer: 8 parts;

[0104] Internal and external lubricants: 1.0 parts;

[0105] ACR processing aid: 6 parts;

[0106] Foaming agent: 1.2 parts.

[0107] The present invention also provides a preparation method of the above-mentioned wood-plastic bathroom board, which includes the following steps:

[0108] 1) Bottom material: mix calcium filler, wood fiber powder, plasticizing regulator, stabilizer, internal and external lubricant, ACR processing aid and foaming agent, add it to the mixing mixer, mix for 10 minutes, then add PVC resin powder, stir for 30 min...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a wood-plastic bathroom plate. The wood-plastic bathroom plate comprises a surface layer and a bottom layer, and the surface layer comprises 1-2 parts by weight of a nanometer silver-ion modified carbon black antibacterial agent. Compared with conventional wood-plastic materials, the wood-plastic bathroom plate has the following advantages: 1) the wood-plastic bathroom plate is capable of well resisting bacteria and preventing mildew because the surface of the plate posses the antibacterial layer, and the wood-plastic bathroom plate has relatively good waterproofness because the antibacterial layer on the surface is relatively low in porosity; and the wood-plastic bathroom plat is wide in raw material resource, low in cost, energy-saving and environment-friendly, and is an ideal bathroom decoration plate replacing common density plates and multi-layer plates; 2) the wood-plastic bathroom plate is easy to process without being limited by processing length, has hard and flat surface crust which does not need manually polishing, helps to save labor resource, and is 100% recyclable after being used for years; and 3) the production technology is simple and easy to operate, and the wood-plastic bathroom plate is good in stability and easy to process.

Description

Technical field [0001] The invention relates to the field of wood-plastic materials, in particular, to a formula of wood-plastic materials used as bathroom panels and a preparation method thereof. Background technique [0002] Wood-plastic composite material is a material made of wood powder, wood fiber or plant fiber filled with thermoplastic polymer and processed by high temperature and high pressure. It has the advantages of wood and plastic. Its main raw material is agricultural and forestry waste (such as waste wood, Crops, rice straw, etc.) and thermoplastics. As a by-product of agricultural production, crop straw has a large output and a wide distribution. According to statistics, the current crop straw production in my country is about 800 to 1 billion tons per year. For a long time, extensive research has been carried out on the comprehensive utilization of crop stalks at home and abroad, and some available ways have been obtained. One of the important ones is to blend ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04C2/24C08L27/06C08L97/02C08J9/10B29C47/00
Inventor 杨明赵悦英顾元喆
Owner 山东宜居新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More