Corrosion and aging resistant rubber material for ships

A rubber material and corrosion-resistant technology, applied in the rubber field, can solve problems such as restricting the safe operation of ships and increasing operating costs, and achieve the effects of excellent anti-aging, improving anti-aging, and reducing molecular gaps.

Inactive Publication Date: 2014-09-10
天长市远洋船舶设备股份有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the rubber materials used in current ships can meet the general needs of ships, many shipowners want to prevent damage to the rubber materials used in ship equipment during ship operation for the sake of safe operation of ships. The installation of materials not only increases the operating cost, but also restricts the safe operation of some ships that need to perform special tasks for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A corrosion-resistant and aging-resistant rubber material for ships proposed by the present invention, its raw materials include by weight: 50 parts of chlorinated polyethylene 140B, 30 parts of natural rubber, 20 parts of chlorosulfonated polyethylene, 2 parts of metal oxide vulcanization system, 0.5 parts of sulfur, 5 parts of magnesium oxide, 20 parts of high wear-resistant carbon black, 20 parts of nano-calcium carbonate, 15 parts of superfine talc, 40 parts of calcined clay, 1.5 parts of trimellitate, dioctyl phthalate 2 parts, 10101 parts of anti-aging agent, 1.5 parts of anti-aging agent MB, 0.5 parts of anti-aging agent RD, 1.5 parts of 1,2-ethylenethiourea, 0.8 parts of NOBS; the following preparation process is adopted:

[0016] S1, first send chlorinated polyethylene, natural rubber and chlorosulfonated polyethylene into the internal mixer and mix for 2 minutes;

[0017] S2, then add high wear-resistant carbon black, magnesium oxide, nano-calcium carbonate, s...

Embodiment 2

[0021] A corrosion-resistant and aging-resistant rubber material for ships proposed by the present invention, its raw materials include by weight: 70 parts of chlorinated polyethylene 140B, 25 parts of natural rubber, 30 parts of chlorosulfonated polyethylene, 1.5 parts of metal oxide vulcanization system, 1.5 parts of sulfur, 2 parts of magnesium oxide, 30 parts of high wear-resistant carbon black, 15 parts of nano-calcium carbonate, 20 parts of superfine talcum powder, 30 parts of calcined clay, 2 parts of trimellitate, dioctyl phthalate 1 part, 10101.5 parts of anti-aging agent, 1 part of anti-aging agent MB, 1 part of anti-aging agent RD, 1 part of 1,2-ethylenethiourea, 1.3 parts of NOBS; the following preparation process is adopted:

[0022] S1, first send chlorinated polyethylene, natural rubber and chlorosulfonated polyethylene into the internal mixer and mix for 1min;

[0023] S2, then add high wear-resistant carbon black, magnesium oxide, nano-calcium carbonate, super...

Embodiment 3

[0027]A corrosion-resistant and aging-resistant rubber material for ships proposed by the present invention, its raw materials include by weight: 55 parts of chlorinated polyethylene 140B, 29 parts of natural rubber, 22 parts of chlorosulfonated polyethylene, 1.9 parts of metal oxide vulcanization system, 0.7 parts of sulfur, 4 parts of magnesium oxide, 23 parts of high wear-resistant carbon black, 18 parts of nano-calcium carbonate, 16 parts of superfine talc, 37 parts of calcined clay, 1.7 parts of trimellitate, dioctyl phthalate 1.9 parts, 10101.1 parts of anti-aging agent, 1.4 parts of anti-aging agent MB, 0.6 parts of anti-aging agent RD, 1.4 parts of 1,2-ethylenethiourea, 0.9 parts of NOBS, of which the chlorine content of chlorinated polyethylene 140B is 36.3 %, the Mooney viscosity ML(1+4) of chlorinated polyethylene 140B is 60 at 125°C, and the volatile matter of chlorinated polyethylene 140B is 0.25%; the following preparation process is adopted:

[0028] S1, first s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a corrosion and aging resistant rubber material for ships. Raw materials for preparing the corrosion and aging resistant rubber material comprise, by weight, 50-70 parts of chlorinated polyethylene 140B, 25-30 pars of natural rubber, 20-30 parts of chlorosulfonated polyethylene, 1.5-2 parts of a metal oxide vulcanization system, 0.5-1.5 parts of sulfur, 2-5 parts of magnesium oxide, 20-30 parts of high abrasion furnace black, 15-20 parts of nanometer calcium carbonate, 15-20 parts of superfine talcum powder, 30-40 parts of calcined potter's clay, 1.5-2 parts of trimellitate, 1-2 parts of dicapryl phthalate, 1-1.5 parts of an antioxidant 1010, 1-1.5 parts of an antioxidant MB, 0.5-1 part of an antioxidant RD, 1-1.5 parts of 1,2-ethylene thiourea, and 0.8-1.3 parts of NOBS. The corrosion and aging resistant rubber material has good mechanical properties, and excellent aging resistance, wear resistance, high temperature resistance, oil resistance and corrosion resistance, and can be used in the complex environment of ships.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to a corrosion-resistant and aging-resistant rubber material for ships. Background technique [0002] As we all know, regardless of mechanical properties, heat resistance, corrosion resistance and disaster protection, the rubber materials used in ships play a vital role in maintaining the normal operation of ships. In specific applications, rubber materials must be resistant to sunlight , aging and acid and alkali erosion, and can withstand severe weather conditions such as high temperature and severe cold, and can still temporarily guarantee its normal operation in the case of accidental disasters. [0003] The working environment of rubber materials in ships is very harsh. It is necessary to ensure good wear resistance, seawater corrosion resistance, and oil resistance and high temperature resistance. Although the rubber materials used in current ships can meet the general needs o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L7/00C08L23/34C08K13/02C08K3/04C08K3/34C08K3/26C08K3/22C08K5/12C08K3/06C08K5/405B29C35/02B29B7/00
CPCC08L23/286B29C35/02C08K2201/011C08K2201/014C08L2201/08C08L2205/03
Inventor 卢文龙
Owner 天长市远洋船舶设备股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com