High-heat-resistant transparent reinforcing material as well as preparation method and application thereof

A reinforced material, high heat-resistant technology, applied in the field of high heat-resistant transparent reinforced material and its preparation, can solve the problems of high cost, poor practicability, low transparency, etc., achieve high heat distortion temperature, strong versatility, and expand application field effect

Active Publication Date: 2014-10-01
JIANGSU KINGFA ENVIRONMENTAL PROTECTION SCI &TECH CO LTD
View PDF14 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These two methods are to add special materials, such as PCCD or transparent agent,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-heat-resistant transparent reinforcing material as well as preparation method and application thereof
  • High-heat-resistant transparent reinforcing material as well as preparation method and application thereof
  • High-heat-resistant transparent reinforcing material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0045] Example 1: Preparation of high heat-resistant transparent reinforced material of the present invention

[0046] (1) Mix the polymethyl methacrylate, styrene-maleic anhydride copolymer, toughening agent, antioxidant and processing aids in proportion to a high-speed mixing mixer or mix them evenly through a metering feeder. In the screw extruder, the glass fiber is added in the sixth zone of the screw through the side feeding system;

[0047] (2) Feed the above mixture into a twin-screw extruder. The temperature of each section of the twin-screw extruder from the feeding port to the die head is preferably 80°C in the first zone, 140°C in the second zone, and three Zone temperature 200℃, four zone temperature 210℃, five zone temperature 220℃, six zone temperature 230℃, seven zone temperature 220℃, eight zone temperature 230℃, nine zone temperature 230℃, head temperature 230℃, screw speed is preferred It is 350rpm, the length to diameter ratio of the twin-screw extruder is 40. ...

Example Embodiment

[0049] Example 2: Preparation of high heat-resistant transparent reinforced material of the present invention

[0050] (1) Mix the polymethyl methacrylate, styrene-maleic anhydride copolymer, toughening agent, antioxidant and processing aids in proportion to a high-speed mixing mixer or mix them evenly through a metering feeder. In the screw extruder, the glass fiber is added in the sixth zone of the screw through the side feeding system;

[0051] (2) Feed the above mixture into a twin-screw extruder. The temperature of each section of the twin-screw extruder from the feeding port to the die head is preferably 80°C in the first zone, 140°C in the second zone, and three Zone temperature 200℃, four zone temperature 210℃, five zone temperature 220℃, six zone temperature 230℃, seven zone temperature 220℃, eight zone temperature 230℃, nine zone temperature 230℃, head temperature 230℃, screw speed is preferred It is 350rpm, the length to diameter ratio of the twin-screw extruder is 40. ...

Example Embodiment

[0053] Example 3: Preparation of high heat-resistant transparent reinforced material of the present invention

[0054] (1) Mix the polymethyl methacrylate, styrene-maleic anhydride copolymer, toughening agent, antioxidant and processing aids in proportion to a high-speed mixing mixer or mix them evenly through a metering feeder. In the screw extruder, the glass fiber is added in the sixth zone of the screw through the side feeding system;

[0055] (2) Feed the above mixture into a twin-screw extruder. The temperature of each section of the twin-screw extruder from the feeding port to the die head is preferably 80°C in the first zone, 140°C in the second zone, and three Zone temperature 200℃, four zone temperature 210℃, five zone temperature 220℃, six zone temperature 230℃, seven zone temperature 220℃, eight zone temperature 230℃, nine zone temperature 230℃, head temperature 230℃, screw speed is preferred It is 350rpm, the length to diameter ratio of the twin-screw extruder is 40. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Heat distortion temperatureaaaaaaaaaa
Heat distortion temperatureaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of high molecular materials, and discloses a high-heat-resistant transparent reinforcing material with strong universality, good heat resistance and high transparency as well as a preparation method and an application thereof. The reinforcing material contains the following components by mass percent: 59% to 93% of mixture of polymethyl methacrylate and styrene-maleic anhydride copolymers, 5% to 30% of glass fibers, 1% to 30% of flexibilizer, 0.1% to 1% of antioxidant and 0.5% to 5% of processing aid. The refractive index of an obtained resin composition is matched with glass fiber phases by applying and regulating the adding proportion of two different resins, so that the reinforcing material is transparent, wherein the transparency of the reinforcing material can reach 87%; and the high heat deformation temperature of the obtained reinforcing material is realized, so that the reinforcing material has the advantages of good heat resistance, high transparency, high strength, good dimensional stability, good comprehensive performance and the like. Thus, the reinforcing material can be applied to various electrical appliances and decorative products, and is particularly suitable for front frames of televisions, air conditioner panels, outer frames of sound equipment and the like.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a highly heat-resistant transparent reinforcing material with strong versatility, good heat resistance and high transparency, and a preparation method and application thereof. Background technique [0002] Glass fiber reinforced thermoplastics (referred to as glass fiber reinforced plastics, GRTP) first appeared in the 1950s. After years of development, CRTP has accounted for more than 1 / 4 of the total composite materials in the world today, and has grown steadily. GRTP is a light-weight and high-strength composite material, and the content of glass fiber is generally 10-50wt%. The base plastics used are polyamide, polypropylene, polyethylene, AS, ABS, PET, PBT, polycarbonate, polyoxymethylene, polyphenylene ether, polyphenylene sulfide, polysulfone, polyethersulfone, polyamide-imide , polyetherimide, polyether ether ketone, chlorinated polyether, polyvinyl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L35/06C08L33/12C08K9/06C08K7/14B29C47/92B29C48/92
CPCB29B7/46B29C47/889B29B9/06B29B9/14B29B7/90B29C47/92B29B7/72B29C48/92B29C2948/9259B29C2948/92704
Inventor 王亮程庆郭涛王林叶南飚刘奇祥
Owner JIANGSU KINGFA ENVIRONMENTAL PROTECTION SCI &TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products