Environment-friendly high-elasticity rubber material

A high-elasticity rubber and environmentally friendly technology, applied in the field of rubber materials, can solve the problems of low elasticity, elasticity, and cold resistance, and achieve the effects of improving wear resistance, perfect performance and reducing costs.

Active Publication Date: 2014-10-08
宁国日格美橡塑股份有限公司
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The performance of nitrile rubber is affected by the content of acrylonitrile. As the content of acrylonitrile increases, the tensile strength, heat resistance, oil resistance, water resistance, air tightness and hardness increase, but the elasticity and cold resistance decrease.
Existing nitrile rubber is widely used due to its oil resistance, but its elasticity is low and it is difficult to meet certain use environments. Now there is a need for a rubber material with excellent elastic properties, good impact resistance, and less rubber Toxic and harmful substances in materials, reducing the harm to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A kind of environment-friendly high elastic rubber material that the present invention proposes, its raw material comprises by weight:

[0015] 30 parts of powdered nitrile rubber, 18 parts of polyvinyl chloride thermoplastic elastomer, 10 parts of ABS resin, 5 parts of p-tert-butylphenol formaldehyde resin, 1.5 parts of sulfur, 1.8 parts of accelerator TMTD, 2 parts of magnesium oxide, 3 parts of zinc oxide 5 parts of epoxy soybean oil, 1 part of paraffin wax, 1 part of zinc barium stabilizer, 3 parts of organic phosphate, 20 parts of modified kaolin, 20 parts of white carbon black, 1.5 parts of black smoke rubber, new rubber reinforcing agent XRE1 .5 copies;

[0016] First masticate the powdered nitrile rubber and polyvinyl chloride thermoplastic elastomer on the internal mixer for 3 minutes at a speed of 45r / min, then knead for 3 minutes at a speed of 50r / min, and add ABS resin and p-tert-butylphenol formaldehyde resin in proportion , magnesium oxide, zinc oxide, ep...

Embodiment 2

[0018] A kind of environment-friendly high elastic rubber material that the present invention proposes, its raw material comprises by weight:

[0019] 40 parts of powdered nitrile rubber, 10 parts of polyvinyl chloride thermoplastic elastomer, 20 parts of ABS resin, 3 parts of p-tert-butylphenol formaldehyde resin, 2 parts of sulfur, 1.2 parts of accelerator TMTD, 4 parts of magnesium oxide, 1 part of zinc oxide 8 parts of epoxy soybean oil, 0.5 parts of paraffin, 3 parts of zinc barium stabilizer, 2 parts of organic phosphate, 30 parts of modified kaolin, 15 parts of white carbon black, 3 parts of black smoke rubber, new rubber reinforcing agent XRE0 .5 copies;

[0020] First, the powdered nitrile rubber and polyvinyl chloride thermoplastic elastomer are masticated on the internal mixer for 2 minutes at a speed of 50r / min, then mixed for 1 minute at a speed of 55r / min, and ABS resin and p-tert-butylphenol formaldehyde resin are added in proportion , magnesium oxide, zinc oxi...

Embodiment 3

[0022] A kind of environment-friendly high elastic rubber material that the present invention proposes, its raw material comprises by weight:

[0023] 35 parts of powdered nitrile rubber, 16 parts of polyvinyl chloride thermoplastic elastomer, 14 parts of ABS resin, 5 parts of p-tert-butylphenol formaldehyde resin, 1.5 parts of sulfur, 1.5 parts of accelerator TMTD, 3 parts of magnesium oxide, 2 parts of zinc oxide 6 parts of epoxy soybean oil, 0.8 parts of paraffin, 2 parts of zinc barium stabilizer, 2.4 parts of organic phosphate, 23 parts of modified kaolin, 19 parts of white carbon black, 1.9 parts of black smoke rubber, new rubber reinforcing agent XRE1 parts, wherein the content of acrylonitrile in powdered nitrile rubber is 35%;

[0024] First masticate the powdered nitrile rubber and polyvinyl chloride thermoplastic elastomer on the internal mixer for 2.6 minutes at a speed of 49r / min, then knead for 2 minutes at a speed of 52r / min, and add ABS resin and p-tert-butylph...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly high-elasticity rubber material which is prepared from the following raw materials in parts by weight: 30-40 parts of powder nitrile-butadiene rubber, 10-18 parts of polyvinyl chloride thermoplastic elastomer, 10-20 parts of ABS (acrylonitrile-butadiene-styrene) resin, 3-5 parts of p-tert-butyl phenol-formaldehyde resin, 1.5-2 parts of sulfur, 1.2-1.8 parts of accelerator TMTD (tetramethyl thiuram disulfide), 2-4 parts of magnesium oxide, 1-3 parts of zinc oxide, 5-8 parts of epoxy soybean oil, 0.5-1 part of paraffin, 1-3 parts of zinc-barium stabilizer, 2-3 parts of organophosphate, 20-30 parts of modified kaolin, 15-20 parts of silica white, 1.5-3 parts of carbon master batch and 0.5-1.5 parts of novel rubber reinforcing agent XRE. The rubber material has the advantages of excellent elasticity, wear resistance, favorable tear resistance and low cost, and reduces the hazard to the environment.

Description

technical field [0001] The invention relates to the technical field of rubber materials, in particular to an environment-friendly high-elastic rubber material. Background technique [0002] Nitrile rubber has excellent oil resistance, second only to polysulfide rubber and fluorine rubber, and has excellent wear resistance and air tightness. The heat resistance is better than that of styrene-butadiene rubber and neoprene, and it can work at 120°C for a long time. Air tightness is second only to butyl rubber. The performance of nitrile rubber is affected by the content of acrylonitrile. As the content of acrylonitrile increases, the tensile strength, heat resistance, oil resistance, water resistance, air tightness and hardness increase, but the elasticity and cold resistance decrease. Existing nitrile rubber is widely used due to its oil resistance, but its elasticity is low and it is difficult to meet certain use environments. Now there is a need for a rubber material with ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L27/06C08L55/02C08L61/08C08K13/06C08K9/00C08K3/34C08K3/06C08K3/22C08K5/1515C08K5/521C08K3/36
Inventor 李元焕
Owner 宁国日格美橡塑股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com