Method for treating pulping black liquor through alkali cooking method taking gramineous plants as materials
A technology for gramineous plants and pulping black liquor, which is applied in the regeneration of lye, can solve problems such as unreasonable processing technology, and achieve the effects of low cost, low price and reduction of carbon dioxide emissions.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0037] The pulp black liquor treatment method of pulping with bagasse as raw material by alkaline cooking method:
[0038]In this example, the research and development team of Guangxi Xingdao Science and Technology Development Co., Ltd. carried out the following treatment process on the black liquor of alkaline cooking pulping with bagasse as raw material in the paper mill of Guangxi Guitang (Group) Co., Ltd.:
[0039] After testing, the content of CODcr in pulp black liquor made from bagasse as raw material and sodium hydroxide as alkaline cooking agent is 350000mg / L; the content of BOD5 is about 135000mg / L, the content of lignin is 13.4%, and the content of inorganic substances is 22.1%. Polysaccharides are 17.1% and the pH is 13.
[0040] Add 15% concentrated sulfuric acid to the pulping black liquor without adding any coagulant, adjust the pH of the black liquor to 2-3, and after standing for 56 hours, filter to obtain a precipitate, and the filtrate enters the treatment t...
Embodiment 2
[0044] The high-purity lignin product of the present invention obtained in Example 1 with a purity of 82% was used as a raw material to conduct research on lignin phenolic resin.
[0045] First, 1000g of high-purity lignin of the present invention, 1500g of water, and 500g of phenol are added in a 10-liter flask with a condenser and agitator, and then 37% formaldehyde is Amount is added wherein, then, 20% sodium hydroxide is slowly added wherein by the amount that is 0.48 with respect to the molar ratio of phenol sodium hydroxide. After all the sodium hydroxide was added, the temperature was raised, and the reaction was carried out at 70° C. for 5 hours to obtain a lignin phenolic resin with a concentration of 38%.
[0046] The obtained lignin phenolic resin is used as an adhesive to manufacture particleboard.
[0047] The raw material of the particle board is obtained by crushing construction wood waste, and the moisture content is 4%. The lignin phenolic resin with a solid ...
Embodiment 3
[0050] Using the low-molecular-weight lignin product with a purity of 12% obtained in Example 1, an evaluation test of a binder for turning the powder into granules was carried out, using coal powder and bitter earth lime powder.
[0051] Coal powder is the water that has added 5% by weight and 60% by weight of the lignin product of the present invention, and bitter earth lime powder is the water that has added 5% by weight and 40% by weight of the lignin product of the present invention, using a bread-type granulator A granulation test was carried out, and both powders formed granules with a diameter of 3-8mm, so the effect of the lignin product of the present invention as a binder has been confirmed.
PUM
Property | Measurement | Unit |
---|---|---|
Static bending strength | aaaaa | aaaaa |
Static bending strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com