Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of alkali slag tunnel fireproof coating and its application method

A technology of fire-resistant coatings and alkali slag, which is applied in fire-resistant coatings, cement coatings, coatings, etc., can solve the problems of multiple components of geopolymers, complex preparation methods, and cost reduction, and achieve a good low-temperature environment, simple formula, and reduce production cost effect

Active Publication Date: 2016-07-06
FUZHOU UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are many geopolymer components in the coating, and the preparation method is relatively complicated, which is not conducive to reducing the cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of alkali slag tunnel fireproof coating and its application method
  • A kind of alkali slag tunnel fireproof coating and its application method
  • A kind of alkali slag tunnel fireproof coating and its application method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] An alkali slag tunnel fireproof coating, which is prepared by mixing cementing materials, thermal insulation materials and additives as dry materials with water; each component in the dry materials contains cementing materials by weight percentage: alkali slag cement 46.5 %, redispersible latex powder 2.5%, polyvinyl alcohol 2.5%;

[0032] Thermal insulation materials: expanded vermiculite 15.5%, expanded perlite 12.5%, sepiolite 6.5%, hollow floating beads 2%;

[0033] Additives: 3.5% magnesium hydroxide, 8.5% aluminum hydroxide;

[0034] The alkali slag cement is made of 92% slag and 8% sodium hydroxide by weight.

[0035] The using method of the alkali slag tunnel fireproof coating specifically comprises the following steps:

[0036] 1) Basic level cleaning: clean up the floating dust, residue, oil stains, etc. on the surface of the inner wall of the tunnel;

[0037] 2) Spray water to wet: Spray water to wet the surface of the wall, and then dry it until there is ...

Embodiment 2

[0045] A kind of alkali slag tunnel fireproof coating, which is prepared by mixing cementing material, thermal insulation material and additives as dry material with water; each component in the dry material contains cementing material by weight percentage: alkali slag cement 40 %, redispersible latex powder 4%, polyvinyl alcohol 1%;

[0046] Thermal insulation materials: expanded vermiculite 16%, expanded perlite 13%, sepiolite 8%, hollow floating beads 3%;

[0047] Additives: magnesium hydroxide 5%, aluminum hydroxide 10%;

[0048]The alkali slag cement is formulated by blending 85% slag and 15% sodium hydroxide by weight.

[0049] The using method of the alkali slag tunnel fireproof coating specifically comprises the following steps:

[0050] 1) Basic level cleaning: clean up the floating dust, residue, oil stains, etc. on the surface of the inner wall of the tunnel;

[0051] 2) Spray water to wet: Spray water to wet the surface of the wall, and then dry it until there i...

Embodiment 3

[0059] An alkali slag tunnel fireproof coating, which is prepared by mixing bonding materials, thermal insulation materials and additives as dry materials with water; each component in the dry materials contains bonding materials by weight percentage: alkali slag cement 50 %, redispersible latex powder 1%, polyvinyl alcohol 6%;

[0060] Thermal insulation materials: expanded vermiculite 13%, expanded perlite 14%, sepiolite 5%, hollow floating beads 1%;

[0061] Additives: magnesium hydroxide 2%, aluminum hydroxide 8%;

[0062] The alkali slag cement is prepared by blending 95% slag and 5% sodium hydroxide by weight.

[0063] The using method of the alkali slag tunnel fireproof coating specifically comprises the following steps:

[0064] 1) Basic level cleaning: clean up the floating dust, residue, oil stains, etc. on the surface of the inner wall of the tunnel;

[0065] 2) Spray water to wet: Spray water to wet the surface of the wall, and then dry it until there is no clea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an alkali slag tunnel fireproof coating and a using method thereof. The alkali slag tunnel fireproof coating is obtained by mixing a bonding material, a thermal insulation material and an auxiliary agent with water as a dry material, that is, a redispersible latex Powder, polyvinyl alcohol, expanded vermiculite, expanded perlite, sepiolite, hollow floating beads, magnesium hydroxide, aluminum hydroxide and slag are mixed evenly, and sodium hydroxide solution is added to stir evenly; Moisture with water, construction and maintenance of fire-resistant coatings, form a fire-proof layer on the inner wall of the tunnel. The alkali slag tunnel fireproof coating of the present invention has good cohesiveness, fire resistance and freeze-thaw cycle resistance performance, no toxic or irritating gas is produced in the production process, has the advantages of green environmental protection, is suitable for large-scale popularization and application, and has Very good application prospects.

Description

technical field [0001] The invention belongs to the technical field of fireproofing materials for tunnels, and in particular relates to an alkali slag tunnel fireproofing coating and its application method. Background technique [0002] With the vigorous development of tunnel construction, the problem of tunnel fire has become increasingly prominent. The temperature of the tunnel can exceed 1000°C in case of fire, and the reinforced concrete structure will lose its basic performance in this high-temperature environment, resulting in huge loss of life and property. It has been widely used in the engineering field. [0003] Patent (CN103232197A) discloses a tunnel fireproof coating, which is composed of geopolymer, expanded perlite, expanded vermiculite, brucite fiber, sepiolite, hydroxymethyl cellulose, fatty alcohol sulfonate air-entraining agent The geopolymer is composed of silica fume, kaolin, calcium-based bentonite, calcium oxide, sodium carbonate, sodium chloride, so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/08C09D5/18C09D7/12B05D7/24
Inventor 季韬王文程吴怀中
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com