Clay sculpture Buddha repair material and preparation method thereof

A technology for repairing materials and Buddha statues. It is applied in the field of mud materials. It can solve the problems of easy cracking on the surface, slow drying and curing speed, and difficulty in coating various pigments. It achieves good surface coating performance, scientific and reasonable formula, and shortens the hardening time. Effect

Active Publication Date: 2015-01-07
江西桐青金属工艺品股份有限公司
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to natural disasters and man-made disasters, or due to long-term disrepair, or due to environmental factors, many clay Buddha statues have their body surface damaged, so that the mud on the surface corrodes and peels off. In order to maintain the original artistic style of clay Buddha statues, clay sculptures must Repair the parts where the mud on the upper surface of the Buddha statue has been eroded and peeled off
[0003] At present, the materials used for the restoration of clay sculpture Buddha statues are mostly clay or concrete materials. Among them, clay materials are easy to obtain, low in cost, and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A clay sculpture Buddha statue repair material is made from the following raw materials by weight: 60 parts of yellow mud, 20 parts of slaked lime, 20 parts of river sand, 10 parts of brown sugar, 10 parts of glutinous rice flour, 2 parts of cotton wool, and 1 part of hydroxyethyl fiber element, 1 part of sodium humate, 2 parts of borax, 1 part of ammonium dihydrogen phosphate, 4 parts of magnesium oxide, and 30 parts of water, wherein the particle size of river sand is 36 meshes, and the particle size of magnesium oxide is 10 μm.

[0021] The preparation method of the clay Buddha statue repair material comprises the following steps:

[0022] (1) after the river sand is crossed with a 36 mesh sieve, take by weighing yellow mud, slaked lime, river sand, brown sugar, glutinous rice flour, cotton wool, hydroxyethyl cellulose, sodium humate, borax, phosphoric acid diphosphate by the above-mentioned weight portion ratio After ammonium hydrogen, magnesium oxide and water, mix...

Embodiment 2

[0027] A clay sculpture Buddha statue repair material is made from the following raw materials by weight: 50 parts of yellow mud, 10 parts of slaked lime, 10 parts of river sand, 5 parts of brown sugar, 5 parts of glutinous rice flour, 1 part of cotton wool, and 0.5 parts of hydroxyethyl fiber element, 0.5 part of sodium humate, 1 part of borax, 0.5 part of ammonium dihydrogen phosphate, 2 parts of magnesium oxide, 20 parts of water, wherein the particle size of river sand is 25 mesh, and the particle size of magnesium oxide is 5 μm.

[0028] The preparation method of the clay Buddha statue repair material comprises the following steps:

[0029] (1) after the river sand is crossed with a 25 mesh sieve, take by weighing yellow mud, slaked lime, river sand, brown sugar, glutinous rice flour, cotton wool, hydroxyethyl cellulose, sodium humate, borax, phosphoric acid diphosphate by the above-mentioned weight portion ratio After ammonium hydrogen, magnesium oxide and water, mix the...

Embodiment 3

[0034] A clay sculpture Buddha statue repair material, which is made from the following raw materials by weight: 55 parts of yellow mud, 12 parts of slaked lime, 12 parts of river sand, 7 parts of brown sugar, 6 parts of glutinous rice flour, 1.5 parts of cotton wool, and 0.6 parts of hydroxyethyl fiber element, 0.8 parts of sodium humate, 1.5 parts of borax, 0.8 parts of ammonium dihydrogen phosphate, 2.8 parts of magnesium oxide, 25 parts of water, wherein the particle size of river sand is 30 mesh, and the particle size of magnesium oxide is 8 μm.

[0035] The preparation method of the clay Buddha statue repair material comprises the following steps:

[0036] (1) after the river sand is crossed through a 30 mesh sieve, take by weighing yellow mud, slaked lime, river sand, brown sugar, glutinous rice flour, cotton wool, hydroxyethyl cellulose, sodium humate, borax, diphosphoric acid by the above-mentioned proportion by weight After ammonium hydrogen, magnesium oxide and wate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a clay sculpture Buddha repair material which is prepared from the following raw materials in parts by weight: 50-60 parts of yellow mud, 10-20 parts of white lime, 10-20 parts of river sand, 5-10 parts of brown sugar, 5-10 parts of glutinous rice flour, 1-2 parts of cotton wool, 0.5-1 part of hydroxyethyl cellulose, 0.5-1 part of sodium humate, 1-2 parts of borax, 0.5-1 part of ammonium dihydrogen phosphate, 2-4 parts of magnesium oxide and 20-30 parts of water. The repair material has the advantages of accessible raw materials, low cost, scientific and reasonable formula, high plasticity, high binding force between the clay sculpture Buddha and lithopedion layer, low cracking tendency after drying and favorable surface application performance, and is especially suitable for repairing the surface layer of the clay sculpture Buddha. The invention also discloses a preparation method of the clay sculpture Buddha repair material, which has the advantages of simple steps and high operability.

Description

technical field [0001] The invention relates to a clay material, in particular to a clay sculpture Buddha statue repair material and a preparation method thereof. Background technique [0002] my country's traditional religious clay sculptures have a long history and a large number of them. They are scattered in famous mountains, rivers, temples and temples all over the motherland. They not only have high artistic value, but also can be called rare treasures. However, due to natural disasters and man-made disasters, or due to long-term disrepair, or due to environmental factors, the surface of many clay Buddha statues has been damaged, so that the surface mud is eroded and peeled off. Repair the parts where the mud on the upper surface of the Buddha statue has eroded and peeled off. [0003] At present, the materials used for the restoration of clay Buddha statues are mostly clay or concrete materials. Among them, clay materials are easy to obtain and low in cost. After dry...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/10C04B41/50
Inventor 吴持跃
Owner 江西桐青金属工艺品股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap