A kind of temperature and ph dual response xylan-based hydrogel and its preparation method and application

A double-response, xylan-based technology, applied in the direction of aerosol delivery, liquid delivery, ointment delivery, etc., to achieve the effect of easy operation, environmental friendliness and easy process

Active Publication Date: 2016-10-05
SOUTH CHINA UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, there have been no reports on temperature and pH sensitive hydrogels prepared from xylan-type hemicelluloses and their application in sustained release of drugs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of temperature and ph dual response xylan-based hydrogel and its preparation method and application
  • A kind of temperature and ph dual response xylan-based hydrogel and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A temperature and pH dual response xylan-based hydrogel, the preparation steps are as follows:

[0041] Weigh 2.5g of xylan (xylan) into a three-necked flask, add 50mL of deionized water, heat at 80°C for 30min and stir to dissolve; cool down to 50°C, and then add 0.25g of N-isopropylacrylamide (NIPA), 25g acrylamide (AM) and 0.25g N,N'-methylenebisacrylamide (MBA), bubbled with nitrogen for 15min to remove dissolved oxygen in the solution and air in the bottle; then add photoinitiated 0.125g of benzoin dimethyl ether (dissolve 0.125g of benzoin dimethyl ether in N-methylpyrrolidone first, and the mass concentration is 2.5%); after the mixed solution is uniform, it is cooled to room temperature, poured into a quartz dish and placed in ultraviolet radiation In the reactor, set the irradiation conditions as follows: the wavelength is 365nm, the power is 400W, and the irradiation is at room temperature for 6h; The gel is taken out and washed with excess deionized water to...

Embodiment 2

[0051] A temperature and pH dual response xylan-based hydrogel, the preparation steps are as follows:

[0052] Weigh 3.0g xylan into a three-necked flask, add 50mL deionized water, heat at 60°C for 40min and stir to dissolve; cool down to 50°C, then add 0.45g of N-isopropylacrylamide (NIPA), 24g of acrylamide (AM) and 0.18g of N,N'-methylenebisacrylamide (MBA), bubbled with nitrogen for 30min to remove dissolved oxygen in the solution and air in the bottle; then add photoinitiated 0.15g of benzoin dimethyl ether (dissolve 0.15g of benzoin dimethyl ether in N-methylpyrrolidone first, and the mass concentration is 2.5%); after the mixed solution is uniform, it is cooled to room temperature, poured into a quartz dish and placed in ultraviolet radiation In the reactor, set the irradiation conditions as follows: the wavelength is 365nm, the power is 400W, and the irradiation is at room temperature for 8h; The gel is taken out and washed with excess deionized water to remove residu...

Embodiment 3

[0057] A temperature and pH dual response xylan-based hydrogel, the preparation steps are as follows:

[0058] Weigh 3.0g of xylan (xylan) into a three-necked flask, add 75mL of deionized water, heat at 70°C for 15min and stir to dissolve; cool down to 50°C, then add 0.24g of N-isopropylacrylamide (NIPA), 45g of acrylamide (AM) and 0.24g of N,N'-methylenebisacrylamide (MBA), bubbled with nitrogen for 10min to remove dissolved oxygen in the solution and air in the bottle; then add photoinitiated 0.15g of benzoin dimethyl ether (dissolve 0.15g of benzoin dimethyl ether in N-methylpyrrolidone first, and the mass concentration is 2.5%); after the mixed solution is uniform, it is cooled to room temperature, poured into a quartz dish and placed in ultraviolet radiation In the reactor, set the irradiation conditions as follows: the wavelength is 365nm, the power is 400W, and it is irradiated at room temperature for 4h; The gel is taken out and washed with excess deionized water to r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of preparation of natural polymer functional materials, and discloses a xylan-based hydrogel with dual response to temperature and pH, a preparation method and application thereof. The preparation steps of the temperature and pH dual-response xylan-based hydrogel are: dissolving xylan in hot water to obtain a xylan solution; adding N-isopropylacrylamide and propylene to the xylan solution Amide, then add cross-linking agent, blow nitrogen gas, add photoinitiator, mix evenly, cool to room temperature, place in ultraviolet radiation reactor, irradiate with ultraviolet light at room temperature, then seal and place reaction at room temperature, after the reaction After washing with deionized water, the obtained solid is the xylan-based hydrogel with dual response to temperature and pH. The preparation method of the present invention is easy to operate and has environmental friendliness; the obtained xylan-based hydrogel with dual response to temperature and pH has biocompatibility, good slow-release behavior for drugs, and releases drugs in simulated intestinal physiological fluid The amount reaches 80%.

Description

technical field [0001] The invention belongs to the technical field of preparation of natural polymer functional materials, and in particular relates to a xylan-based hydrogel with dual response to temperature and pH, a preparation method and application thereof. Background technique [0002] Plants around the world produce 3.5×10 hemicellulose per year 10 There are so many t. Hemicellulose is one of the most abundant and cheapest renewable resources on earth, and it is an inexhaustible renewable resource in nature. Hemicellulose is a rational raw material for the preparation of materials due to its wide range of sources, biodegradability, biocompatibility, and special physiological activities. As the main component of hemicellulose, xylan mainly exists in hardwoods and grasses. Xylan itself has special physical and chemical properties that other natural polymers such as cellulose and starch do not have, and has potential application value in the pharmaceutical industry. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F251/00C08F220/56C08F220/54C08F222/38C08J3/075A61K47/36A61K9/06
Inventor 任俊莉高存殿孙润仓孔维庆
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com