Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Air-drying protective paint for plastics and preparation method thereof

A self-drying, plastic technology, used in anti-corrosion coatings, coatings, etc., can solve the problems of long self-drying time, anti-corrosion, wear-resistant can not meet the requirements, can not apply plastic coating, etc., to achieve the effect of excellent performance

Inactive Publication Date: 2015-01-14
SUZHOU POLYMER NEW MATERIALS TECH
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it cannot be used in plastic coating, and the self-drying time is longer, and the performance of corrosion resistance and wear resistance cannot meet the requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Air-drying protective paint for plastics and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A self-drying plastic protective coating, comprising in terms of weight components: 10 parts of butyl acrylate, 5 parts of light calcium carbonate, 1 part of talc, 2 parts of bentonite, 0.2 parts of silicone defoamer, ethylene carbonate 2 parts, 5 parts of ethyl 2-cyanoacrylate, 0.2 part of ethylene glycol monoethyl ether, 1 part of disodium succinate, 0.6 part of N-oleoyl sarcosine octadecylamine, and 20 parts of ethyl acetate.

[0021] The preparation method of the above-mentioned self-drying plastic protective coating is characterized in that the steps are as follows:

[0022] Step 1, add butyl acrylate, light calcium carbonate, bentonite, ethylene carbonate and ethyl acetate in the reactor with condenser, stirrer and thermostat, stir and heat to reflux, continue stirring for 60 minutes, above The stirring speed is 120 rev / min to obtain mixture 1;

[0023] Step 2, add ethyl 2-cyanoacrylate, ethylene glycol monoethyl ether and N-oleoyl sarcosine octadecylamine to mix...

Embodiment 2

[0026] A self-drying plastic protective coating, comprising in terms of weight components: 14 parts of butyl acrylate, 6 parts of light calcium carbonate, 3 parts of talcum powder, 3 parts of bentonite, 0.3 parts of silicone defoamer, ethylene carbonate 3 parts, 6 parts of ethyl 2-cyanoacrylate, 0.4 parts of ethylene glycol monoethyl ether, 2 parts of disodium succinate, 0.8 parts of N-oleoyl sarcosine octadecylamine, and 25 parts of ethyl acetate.

[0027] The preparation method of the above-mentioned self-drying plastic protective coating is characterized in that the steps are as follows:

[0028] Step 1, add butyl acrylate, light calcium carbonate, bentonite, ethylene carbonate and ethyl acetate in the reactor with condenser, stirrer and thermostat, stir and heat to reflux, continue stirring for 70 minutes, above The stirring speed is 130 rev / min to obtain mixture 1;

[0029] Step 2, add ethyl 2-cyanoacrylate, ethylene glycol monoethyl ether and N-oleoyl sarcosine octadecy...

Embodiment 3

[0032] A self-drying plastic protective coating, comprising in terms of weight components: 15 parts of butyl acrylate, 7 parts of light calcium carbonate, 4 parts of talcum powder, 4 parts of bentonite, 0.4 parts of silicone defoamer, ethylene carbonate 4 parts, 7 parts of ethyl 2-cyanoacrylate, 0.5 parts of ethylene glycol monoethyl ether, 3 parts of disodium succinate, 1.5 parts of N-oleoyl sarcosine octadecylamine, and 27 parts of ethyl acetate.

[0033] The preparation method of the above-mentioned self-drying plastic protective coating is characterized in that the steps are as follows:

[0034] Step 1, add butyl acrylate, light calcium carbonate, bentonite, ethylene carbonate and ethyl acetate in the reactor with condenser, stirrer and thermostat, stir and heat to reflux, continue stirring for 80 minutes, above The stirring speed is 130 rev / min to obtain mixture 1;

[0035] Step 2, add ethyl 2-cyanoacrylate, ethylene glycol monoethyl ether and N-oleoyl sarcosine octadecy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an air-drying protective paint for plastics and a preparation method thereof. The paint comprises butyl acrylate, light calcium carbonate, talcum powder, bentonite, a defoaming agent, ethylene carbonate, ethyl 2-cyanoacrylate, ethylene glycol monoethyl ether, disodium succinate, N-oleoylsarcosine octadecylamine and ethyl acetate. The preparation method comprises the following steps: adding the butyl acrylate, light calcium carbonate, bentonite, ethylene carbonate and ethyl acetate into a reaction kettle which is provided with a condenser, a stirrer and a thermometer, stirring, heating to reflux, continuing stirring to obtain a mixture 1, adding the ethyl 2-cyanoacrylate, ethylene glycol monoethyl ether and N-oleoylsarcosine octadecylamine, continuing stirring under reflux, cooling to room temperature, finally adding the talcum powder, defoaming agent and disodium succinate, and uniformly mixing. The air-drying protective paint for plastics has the advantages of quick air-drying capacity and weather resistance, and can be widely popularized and applied.

Description

technical field [0001] The invention belongs to the technical field of chemical paint preparation, in particular to a self-drying plastic protective paint and a preparation method thereof. Background technique [0002] At present, coatings are used in many fields, and are widely used in various fields such as machinery, automobiles, electronics, and communications. Since coatings are often exposed to the atmosphere during use and are eroded by oxygen, moisture, etc., it is easy to cause metal corrosion, wood decay, cement weathering and other phenomena. The requirements in all aspects have been improved, especially for the hardness, wear resistance, fullness, impact resistance, aging resistance, corrosion resistance, water resistance, oil resistance, chemical resistance, light resistance, temperature resistance and other properties of coatings. The requirements are getting higher and higher, so it is necessary to study more advanced coatings to meet people's needs. At pres...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/08C09D7/12C09D5/08C08F220/18
CPCC08F220/18C08F220/1804C08F220/34C08K3/26C08K3/34C08K3/346C08K5/06C08K2003/265C09D5/08C09D7/40C09D133/08
Inventor 翟红波杨振枢韦洪屹
Owner SUZHOU POLYMER NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com