Heat-preservation and thermal-insulating water-based paint for glass sliding door and preparation method of water-based paint

A thermal insulation performance, glass sliding door technology, applied in polyurea/polyurethane coatings, coatings, paints containing biocide, etc., can solve the problems of poor thermal insulation effect, expensive construction equipment, complicated process, etc., to achieve Suitable for popularization, improving hardness and improving anti-fouling effect

Inactive Publication Date: 2015-02-11
凤阳徽亨商贸有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the heat insulation products used in the market have defects such as poor heat insulation effect, low light transmittance, expensive construction equipment, complicated process, etc., which are not conducive to large-scale promotion to the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] specific implementation plan

[0015] The present invention will be described in detail below through specific examples.

[0016] A water-based coating for glass sliding doors with thermal insulation performance, prepared from the following raw materials in parts by weight (kg): water-based polyurethane resin 52, water-based hydroxyacrylic acid 18, polyoxypropylene glyceryl ether 0.3, tripropylene glycol monobutyl ether 3 , alcohol amine titanate 0.4, modified pure acrylic emulsion 8, polyether modified polyorganosiloxane 0.3, dimethyl silicone oil 0.3, accelerator TMTM 0.2, butyl glycidyl ether 0.4, guar gum 0.4, Diacetone acrylamide 0.4, zeolite powder 0.6, pigment 2, hollow glass microspheres 2, silica sol 3, deionized water 14;

[0017] The modified pure acrylic emulsion is made of the following raw materials in parts by weight (kg): nano titanium dioxide 5, nano silicon dioxide 2, nano calcium carbonate 1, methyl methacrylate 54, butyl acrylate 44, methacrylic ac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses heat-preservation and thermal-insulating water-based paint for a glass sliding door. The water-based paint is prepared from the following raw materials in parts by weight: 48-53 parts of waterborne polyurethane resin, 16-19 parts of waterborne hydroxyl acrylic acid, 0.2-0.4 part of polypropylene oxide glyceryl ether, 1-3 parts of tripropylene glycol monobutyl ether, 0.3-0.6 part of alkylol amine titanate, 7-10 parts of modified pure acrylic emulsion, 0.2-0.5 part of polyether modified organo-polysiloxane, 0.2-0.4 part of dimethicone, 0.2-0.4 part of an accelerant TMTM, 0.3-0.6 part of butyl glycidyl ether, 0.3-0.6 part of guar gum, 0.3-0.5 part of diacetone-acryloamide, 0.4-0.9 part of zeolite powder, 1-2 parts of pigment, 1-3 parts of hollow glass microspheres, 2-3 parts of silica sol and 12-16 parts of deionized water. Due to adoption of the silica sol in the water-based glass paint disclosed by the invention, the hardness of a paint film is improved, and the paint film is not easy to peel off and is smooth and flat; due to adoption of the hollow glass microspheres, the heat preservation and thermal insulation effects are achieved, and the cost is lowered; due to adoption of the modified pure acrylic emulsion, properties such as the flouring resistance, the bactericidal activity, the scrubbing resistance and the weather resistance of the water-based paint are improved; the water-based paint is high in practicability and applicable to popularization.

Description

Technical field [0001] The present invention involves a coating and preparation method, especially a glass -migraphic coatings and preparation methods with insulation and insulation performance. Background technique [0002] Glass coatings are a kind of coating.It can stably adhere to the surface of the glass appliance, and use different colors to make the glass appliances aesthetically and decorate.Conventional glass coatings are divided into oily coatings and water -based coatings according to the type of solvents. Oilness is based on benzene and ester as solvents, and water properties are used as solvents.Glass coatings are developed from solvent type to water. It is an inevitable trend of glass jewelry, crafts, glass containers and wine bottles to adapt to the development of green environmental protection requirements. It has gradually replaced traditional solvent -based coatings and occupies the mainstream market areas.And with the continuous expansion of the application fie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D133/00C09D133/12C09D7/12C08F220/14C08F220/18C08F220/06C08F2/44
CPCC08F220/14C08K2201/011C08L2201/10C08L2205/035C09D5/14C09D7/61C09D7/62C09D7/63C09D7/65C09D7/70C09D175/04C08L33/00C08L71/02C08L33/12C08L83/04C08L83/12C08L5/08C08K13/06C08K9/06C08K2003/2241C08K3/36C08K2003/265C08K5/1515C08K7/28C08F220/1804C08F220/06
Inventor 张波
Owner 凤阳徽亨商贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products