Heavy metal-containing wastewater treatment chemical

A technology for sewage treatment and heavy metals, applied in water/sewage treatment, water/sludge/sewage treatment, flocculation/sedimentation water/sewage treatment, etc. Slow settling speed and other problems, to achieve the effect of easy clarification of stratification, reduction of equipment maintenance costs, and rapid settling

Inactive Publication Date: 2015-03-11
WUXI EPIC TECH
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0019] The existing water treatment technology has treated harmful substances such as heavy metals in industrial wastewater, but it cannot achieve a good removal effect on harmful substances other than heavy metals in wastewater, especially when dealing with industrial circulating water. matter of matter
The chemicals used in the existing wastewater treatment still have problems such as poor treatment effect, slow settling speed, high cost, and serious corrosion of equipment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A heavy metal sewage treatment agent, characterized in that: the sewage treatment agent is prepared by mixing barium sulfide, ferric sulfate, polysilicic aluminum sulfate, and a small amount of calcium hydroxide and lithopone, and its weight ratio is: barium sulfide 35 parts, iron sulfate 25 parts, polysilicon aluminum sulfate 30 parts, calcium hydroxide 5 parts, lithopone 5 parts.

[0040] (1) Prepare raw materials by weight: 35 parts of barium sulfide, 25 parts of iron sulfate, 30 parts of polysilicoaluminum sulfate, 5 parts of calcium hydroxide, and 5 parts of lithopone. ;

[0041] (2) Add 35 parts of barium sulfide, 25 parts of ferric sulfate, 30 parts of polysilicon aluminum sulfate in reactor;

[0042](3) Stir and heat to 120°C, keep the reaction temperature at 125°C, and reflux for 6 hours;

[0043] (4) Dilute 5 parts of calcium hydroxide with water, and fully stir with the dried jelly;

[0044] (5) Boiling and reacting at a temperature of 100°C for 6 hours t...

Embodiment 2

[0049] A heavy metal sewage treatment agent, characterized in that: the sewage treatment agent is prepared by mixing barium sulfide, ferric sulfate, polysilicic aluminum sulfate, and a small amount of calcium hydroxide and lithopone, and its weight ratio is: barium sulfide 33 parts, iron sulfate 22 parts, polysilicon aluminum sulfate 35 parts, calcium hydroxide 5 parts, lithopone 5 parts.

[0050] (1) Prepare raw materials by weight: 33 parts of barium sulfide, 22 parts of iron sulfate, 35 parts of polysilicoaluminum sulfate, 5 parts of calcium hydroxide, and 5 parts of lithopone. ;

[0051] (2) Add 33 parts of barium sulfide, 22 parts of iron sulfate, 35 parts of polysilicon aluminum sulfate in reactor;

[0052] (3) Stir and heat to 120°C, keep the reaction temperature at 130°C, and reflux for 8 hours;

[0053] (4) Dilute 5 parts of calcium hydroxide with water, and fully stir with the dried jelly;

[0054] (5) Boiling and reacting at a temperature of 100°C for 8 hours to...

Embodiment 3

[0059] A heavy metal sewage treatment agent, characterized in that: the sewage treatment agent is prepared by mixing barium sulfide, ferric sulfate, polysilicic aluminum sulfate, and a small amount of calcium hydroxide and lithopone, and its weight ratio is: barium sulfide 37 parts, ferric sulfate 20 parts, polysilicoaluminum sulfate 33 parts, calcium hydroxide 5 parts, lithopone 5 parts.

[0060] (1) Prepare raw materials by weight: 37 parts of barium sulfide, 20 parts of iron sulfate, 33 parts of polysilicoaluminum sulfate, 5 parts of calcium hydroxide, and 5 parts of lithopone. ;

[0061] (2) Add 37 parts of barium sulfide, 20 parts of iron sulfate, 33 parts of polysilicon aluminum sulfate in reactor;

[0062] (3) Stir and heat to 120°C, keep the reaction temperature at 115°C, and reflux for 9 hours;

[0063] (4) Dilute 5 parts of calcium hydroxide with water, and fully stir with the dried jelly;

[0064] (5) Boiling and reacting at a temperature of 100°C for 10 hours t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a heavy metal-containing wastewater treatment chemical. The wastewater treatment chemical is prepared by mixing barium sulfide, ferric sulfate, poly-silicon aluminum sulfate and a few calcium hydroxide and lithopone, wherein barium sulfide accounts for 30-40 parts by weight, ferric sulfate accounts for 20-30 parts by weight, poly-silicon aluminum sulfate accounts for 20-40 parts by weight, calcium hydroxide accounts for 5 parts by weight and lithopone accounts for 5 parts by weight. The chemical has a wide range of application and has high universality. The wastewater treatment chemical has a good effect of treating industrial wastewater of metallurgy, heavy metal, mine, printing and dyeing, spinning, building, casting, chemical, electric power, leather and papermaking, etc. as well as municipal composite wastewater. The chemical has a wide range of pH for water and has purifying effects at pH 4-10. The chemical has good sedimentation efficiency and good water purification quality and is non-corrosive. The pH value of a solution treated by the use of the chemical is 6.5-8.5 and is close to neutral. The solution contains no chloride ion. A steel structure in a water system can effectively be protected during recycling so as to protect the steel structure from being corroded. Thus, a large amount of equipment maintenance cost can be minimized annually.

Description

technical field [0001] The invention belongs to the technical field of water treatment, and in particular relates to a water treatment agent for treating heavy metal sewage. Background technique [0002] Sewage treatment technology plays a very important role in water saving, energy saving and other issues, but at the same time, the use of sewage treatment chemicals also has a certain impact on the environment. In the cooling water system, in various occasions where the water temperature is higher than the ambient temperature, the scaling of calcium carbonate and other inorganic salts will bring serious consequences. In recent years, in the field of water treatment, the application of alkaline water treatment technology that does not adjust the pH value is increasing. Among them, the addition of corrosion and scale inhibitors, low-phosphorus and phosphorus-free formulas are more and more widely used. Phosphorus-free green Water treatment agents have become a hot topic in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/00C02F1/52C02F101/20
CPCC02F1/00C02F1/52C02F1/62C02F2101/20
Inventor 尤为
Owner WUXI EPIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap