Water-based composite passivation solution for galvanized steel plate and preparation method of water-based composite passivation solution

A technology of galvanized steel sheet and passivation solution, applied in the direction of metal material coating process, can solve the problems of complex drying and curing process, poor stability of passivation solution, no self-healing ability of film layer, etc., and achieve fast drying and curing. , Short curing time, improve the effect of fastness and corrosion resistance

Inactive Publication Date: 2015-03-25
北京蓝星清洗有限公司
View PDF7 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The toxicity of trivalent chromium is only 1/100 of that of hexavalent chromium. Trivalent chromium passivation is a transitional technology. The passivation film is beautiful and has excellent corrosion resistance, but the passivation solution has poor stability, low service life, narrow allowable pH, The film layer has the disadvantage of no self-healing ability; and because most of the trivalent chromium passivation solutions need to add oxidants, improper formulation will make

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based composite passivation solution for galvanized steel plate and preparation method of water-based composite passivation solution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Components and mass fraction of passivation solution: sodium molybdate 10g / L, sodium phosphate 6g / L, organic phosphoric acid 5g / L, fluotitanic acid 1g / L, silane coupling agent 5g / L, sodium metasilicate 10g / L L, wetting and dispersing agent 0.1%, and deionized water as the rest.

Embodiment 2

[0032] Components and mass fraction of passivation solution: sodium molybdate 15g / L, sodium phosphate 5g / L, organic phosphoric acid 5g / L, fluotitanic acid 3g / L, silane coupling agent 10g / L, sodium metasilicate 10g / L L, wetting and dispersing agent 0.1%, and deionized water as the balance.

Embodiment 3

[0034] Components and mass fraction of passivation solution: sodium molybdate 20g / L, sodium phosphate 10g / L, organic phosphoric acid 8g / L, fluotitanic acid 5g / L, silane coupling agent 15g / L, sodium metasilicate 15g / L L, wetting and dispersing agent 0.1%, and deionized water as the balance.

[0035] The performance indexes of the hexavalent chromium passivation solution and the molybdate passivation solution of each embodiment and reference are as follows:

[0036] Table 1 Properties of passivation solution

[0037]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a water-based composite chromium-free passivation solution for a galvanized steel plate. The passivation solution contains 10-30g/L of sodium molybdate, 0-10g/L of sodium phosphate, 5-10g/L of organic phosphoric acid, 1-10g/L of fluotitanic acid, 5-15g/L of a silane coupling agent, 5-20g/L of sodium metasilicate, 0.1-1% of a wetting dispersant and the balance of deionized water. The passivation solution provided by the invention consists of an organic phosphoric acid-molybdate system in match with the modified hydrolysis type silane coupling agent and a nano-inorganic filler, does not contain a chromate and is in line with ROHS requirements; the passivation and drying curing time is short, the degree of stability is high, the quality of a film layer is good, the white rust area in a 72h salt fog test does not exceed 5%, the cost is relatively low, a passivation process device does not need to be changed, and continuous passivation can be realized by using a hexavalent chromium passivation device in early period.

Description

technical field [0001] The invention belongs to the technical field of hot-dip plating, and in particular relates to a water-based composite passivation solution for galvanized steel sheets and a preparation method thereof. Background technique [0002] At present, from the viewpoint of ensuring corrosion resistance, the surface of a coated steel sheet is often galvanized. Steel is usually passivated after electro-galvanizing or hot-dip galvanizing to prevent white rust in a short period of time. Although the traditional chromate treatment film is a thin film, it has excellent corrosion resistance, but it contains a large amount of hexavalent chromium, which is seriously harmful to the human body and the environment; in order to make the passivation film meet the requirements of environmental protection and solve the pollution problem of hexavalent chromium, Abandoning the traditional chromic acid passivation process and developing and researching chromium-free passivation ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/44
CPCC23C22/44
Inventor 候悖王双田白剑利单素灵盛仲翰
Owner 北京蓝星清洗有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap