A kind of method that prepares hydrated rhodium trichloride by silica gel polymeric amine resin

A technology of hydrated rhodium trichloride and silica gel polymerized amine, which is applied in chemical instruments and methods, inorganic chemistry, ruthenium/rhodium/palladium/osmium/iridium/platinum compounds, etc., which can solve the difficulty of rhodium elution and cannot be directly produced Hydrated rhodium trichloride and other problems, to achieve high rhodium adsorption rate, reduce rhodium loss, and simple treatment process

Active Publication Date: 2016-06-15
CNOOC TIANJIN CHEM RES & DESIGN INST +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When anion exchange resin is used to purify rhodium acid solution, it is difficult to elute the rhodium adsorbed on the resin, and it needs to be eluted with lye, so what is obtained is an alkaline solution containing rhodium, and rhodium trichloride hydrate cannot be directly obtained

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Get the rhodium acid solution that 1000 grams of concentrated sulfuric acid and nitric acid digestion rhodium slag obtain, wherein the mass content of rhodium is 7.2% (0.70mol), the mass content of nitric acid is 3%, the mass content of sulfuric acid is 55%, the rhodium acid solution is diluted with water When the molar concentration of the acid is 5.2 mol / L, add 368 grams (6.29 mol) of sodium chloride solid, and then heat and reflux the solution for 1 hour. After cooling, the rhodium solution was passed through a layer of silica gel polyamine resin equipped with 2L model WP-1 at a linear speed of 3m / h. After the rhodium in the solution is completely absorbed by the resin, use deionized water and 3mol / L hydrochloric acid solution to elute a small amount of sodium, iron, nickel, calcium and other metals remaining between the columns and adsorbed on the resin, and then use a concentration of 10mol / L of 90°C hydrochloric acid elutes the rhodium adsorbed on the resin to ob...

Embodiment 2

[0033] Get the rhodium acid solution that 1000 grams of concentrated sulfuric acid and nitric acid digestion rhodium slag obtain, wherein the mass content of rhodium is 1.6% (0.16mol), the mass content of nitric acid is 5%, the mass content of sulfuric acid is 32%, the rhodium acid solution is diluted with water When the molar concentration of the acid is 6.1 mol / L, 140 grams (2.40 mol) of sodium chloride solid is added, and the solution is then heated to reflux for 1 hour. After cooling, the rhodium solution was passed through a layer of silica gel polyamine resin equipped with 2L model WP-1 at a linear speed of 3m / h. After the rhodium in the solution is completely absorbed by the resin, use deionized water and 3mol / L hydrochloric acid solution to elute a small amount of sodium, iron, nickel, calcium and other metals remaining between the columns and adsorbed on the resin, and then use a concentration of 6mol / L of 90°C hydrochloric acid elutes the rhodium adsorbed on the res...

Embodiment 3

[0035] Get the rhodium acid solution that 1000 grams of concentrated sulfuric acid and nitric acid digestion rhodium slag obtain, wherein the mass content of rhodium is 10.5% (1.02mol), the mass content of nitric acid is 4%, the mass content of sulfuric acid is 84%, the rhodium acid solution is diluted with water When the molar concentration of the acid is 1.2 mol / L, 358 grams (6.12 mol) of sodium chloride solid are added, and the solution is then heated to reflux for 1 hour. After cooling, the rhodium solution was passed through a layer of silica gel polyamine resin equipped with 2L model WP-1 at a linear speed of 3m / h. After the rhodium in the solution is completely absorbed by the resin, use deionized water and 3mol / L hydrochloric acid solution to elute a small amount of sodium, iron, nickel, calcium and other metals remaining between the columns and adsorbed on the resin, and then use a concentration of 12mol / L of 60°C hydrochloric acid elutes the rhodium adsorbed on the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing rhodium trichloride hydrate by using silica gel-polyamine resin. The method comprises the following steps: adding water to dilute a rhodium acid digestion solution obtained after digestion of rhodium residues by concentrated sulfuric acid and nitric acid, adding a sodium chloride solid, and heating to reflux the obtained solution; allowing the solution to go through an exchange column filled with silica gel-polyamine resin; and sequentially eluting a small amount of sodium, iron, calcium, nickel and other metals residual in the column and adsorbed to the resin by using deionized water and 1-6mol / L of a hydrochloric acid solution, eluting rhodium adsorbed to the resin by using 6-12mol / L of 50-90DEG C hydrochloric acid, and evaporating the eluted chlororhodic acid solution to obtain the rhodium trichloride hydrate. In the rhodium acid digestion solution, the rhodium content is 1-10wt%, the nitrate content is 1-5wt%, and the sulfuric acid content is 30-85wt%; a molar ratio of sodium chloride to rhodium in the digestion solution is 3-15; and the silica gel-polyamine resin is water soluble polyurethane, and is combined to resin formed on the surface of a silica gel carrier in a covalent bond mode. The method for preparing rhodium trichloride hydrate from the rhodium acid digestion solution has the characteristics of high recovery efficiency, simple process, mild process conditions and the like.

Description

Technical field: [0001] The invention relates to the field of precious metal recovery and utilization, and aims to provide a more efficient method for absorbing and separating rhodium contained in rhodium acid digestion solution and then preparing hydrated rhodium trichloride. Background technique: [0002] Rhodium homogeneous organic complex catalysts have the advantages of high catalytic activity and good selectivity, and have important applications in catalytic hydrogenation, olefin hydroformylation, and oxo synthesis catalysis, and many of them have been used in industrial production. For example: three (triphenylphosphine) rhodium chloride is used in industry as an efficient olefin hydrogenation catalyst, rhodium acetylacetonate dicarbonyl, triphenylphosphine acetylacetonate carbonyl rhodium, three (triphenylphosphine) carbonyl rhodium hydrogen, three [Tris(m-sulfonate phenyl)phosphine] rhodium carbonyl hydride, etc. are used as efficient olefin hydroformylation catalys...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G55/00
Inventor 李晨于海斌蒋凌云李继霞郝婷婷王鹏飞姜雪丹张雪梅
Owner CNOOC TIANJIN CHEM RES & DESIGN INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com