Preparation method of corrosion-resistant conveyor belt

A technology of anti-corrosion and conveyor belt, applied in the field of preparation of anti-corrosion conveyor belt, can solve problems such as poor scorch resistance, achieve good plasticity, improve vulcanization speed and fluidity, and have good corrosion resistance such as acid and alkali resistance.

Inactive Publication Date: 2015-06-10
QINGDAO ALLPOLY CONVEYOR BELT
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The lower the molecular weight of ordinary fluororubber, the worse the vulcanization performance, but the better the scorch resistance. The higher the molecular weight, the better the vulcanization performance, but the worse the scorch resistance. Good vulcanization speed and scorch resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A method for preparing a corrosion-resistant conveyor belt is characterized in that it mainly includes the following steps:

[0018] (1) Reactor pretreatment: evacuate the reactor to remove oxygen, add deionized water to the reactor, and reserve 45% of the space;

[0019] (2) Modified rubber: Add 60 parts of mixed rubber composed of isoprene rubber and ethylene-propylene rubber in a weight ratio of 1:1 to the reactor, and then add tetrafluoroethylene and perfluoropropylene in a molar ratio of 2:1. 15 parts of mixed monomers, the control pressure is 2MPa, carbon tetrachloride is added, and the polymerization reaction is carried out for 20 minutes;

[0020] (3) Rubber compounding: put the above rubber into the internal mixer, add 4 parts of polyethylene resin, vinyltrimethoxysilane and methyltriethoxysilane according to the weight ratio of 1:1 composition of silane crosslinking 3 parts of additives, 1 part of zinc oxide and 1 part of stearic acid, fully mixed in a high-s...

Embodiment 2

[0023] A method for preparing a corrosion-resistant conveyor belt is characterized in that it mainly includes the following steps:

[0024] (1) Reactor pretreatment: evacuate the reactor to remove oxygen, add deionized water to the reactor, and reserve 45% of the space;

[0025] (2) Modified rubber: Add 70 parts of mixed rubber composed of isoprene rubber and ethylene-propylene rubber in a weight ratio of 1:1 to the reactor, and then add tetrafluoroethylene and perfluoropropylene in a molar ratio of 2:1. 18 parts of mixed monomers, the pressure is controlled at 3MPa, acetone or ethyl acetate is added, and the polymerization reaction is carried out for 18 minutes;

[0026] (3) Rubber compounding: put the above rubber into the internal mixer, add 5 parts of polyethylene resin, vinyltrimethoxysilane and methyltriethoxysilane according to the weight ratio of 1:1 composition of silane crosslinking 3 parts of additives, 1.5 parts of zinc oxide and 2 parts of stearic acid are fully ...

Embodiment 3

[0029] A method for preparing a corrosion-resistant conveyor belt is characterized in that it mainly includes the following steps:

[0030] (1) Reactor pretreatment: evacuate the reactor to remove oxygen, add deionized water to the reactor, and reserve 50% of the space;

[0031] (2) Modified rubber: Add 80 parts of mixed rubber composed of isoprene rubber and ethylene-propylene rubber in a weight ratio of 1:1 to the reactor, and then add tetrafluoroethylene and perfluoropropylene in a molar ratio of 2:1. 20 parts of mixed monomers, the control pressure is 3MPa, carbon tetrachloride, acetone or ethyl acetate are added, and the polymerization reaction is carried out for 20 minutes;

[0032] (3) Rubber compounding: put the above rubber into the internal mixer, add 6 parts of polyethylene resin, vinyltrimethoxysilane and methyltriethoxysilane according to the weight ratio of 1:1 composition of silane crosslinking 4 parts of additives, 2 parts of zinc oxide and 3 parts of stearic ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a corrosion-resistant conveyor belt. The preparation method is characterized in comprising following steps: (1) reaction kettle pretreatment; (2) preparation of modified rubber; (3) rubber material mixing; and (4) milling and sulfuration. A fluorine-containing rubber used for preparing the conveyor belt is prepared via the preparation method; molecular weight distribution is ideal; plasticity is excellent; acid and alkali resistance is excellent; sulfuration speed and fluidity are increased effectively; the obtained conveyor belt possesses excellent heat resistance, wear resistance, and acid and alkali resistance, and is especially suitable for industrial production.

Description

technical field [0001] The invention belongs to the technical field of conveyor belt production, and in particular relates to a preparation method of a corrosion-resistant conveyor belt. Background technique [0002] Isoprene rubber has good elasticity and wear resistance, excellent heat resistance and good chemical stability. The strength of raw isoprene rubber (before processing) is significantly lower than that of natural rubber, but its quality uniformity and processing performance are superior to natural rubber. Ethylene-propylene rubber is synthesized with ethylene and propylene as the main raw materials, and has outstanding aging resistance, electrical insulation properties and ozone resistance. Ethylene-propylene rubber can be filled with a large amount of oil and carbon black, and the product price is low. Ethylene-propylene rubber has good chemical stability, and its abrasion resistance, elasticity, oil resistance and styrene-butadiene rubber are close. [0003] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/04C08L51/06C08L23/06C08K13/02C08K3/22C08K5/09C08K3/06C08K5/18C08K5/5425C08K5/5419C08F291/02C08F214/26C08F214/28
Inventor 向华
Owner QINGDAO ALLPOLY CONVEYOR BELT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap